Polymer Property : Tensile Strength at Break = 21000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	145 MPa	21000 psi	Type I, 5.1 mm/min; ASTM D638
PolyOne Nymax™ ND633 GF Black Polyamide 6 (Nylon 6) The Nymax® GF 600 Series of glass fiber-reinforced nylon 6 compounds have been specifically engineered for applications requiring high stiffness, tensile strength, and toughness, while providing en..
Tensile Strength at Break	145 MPa	21000 psi	ASTM D638
Polymer Resources NY66-G20-MD Nylon 66, 20% Glass Reinforced with MoS2 Nylon 66, 20% Glass Reinforced with Molybdenum Disulfide for Lubrication and WearProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigment..
Tensile Strength at Break	145 MPa	21000 psi	ASTM D638
LNP Lubricomp® OFL-4036 Polyphenylene Sulfide, Glass Fiber Reinforced, PTFE Lubricant  (discontinued **) Features: LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still ac..
Tensile Strength at Break	145 MPa <br>@Temperature 23.0 °C	21000 psi <br>@Temperature 73.4 °F	ISO 527
DuPont Performance Polymers Crastin® SK609 BK851 PBT  (Unverified Data**) Crastin® SK609 BK851 is a 50% glass fiber reinforced, lubricated, black polybutylene terephthalate resin for injection molding.Information provided by DuPont Performance Polymers
Tensile Strength at Break	<= 145 MPa	<= 21000 psi	ISO/R527
Polykemi AB POLYshine PBT D203 GF30 FR PBT, Glass Fiber Reinforced, Flame Retardant Information provided by Polykemi AB
Tensile Strength at Break	145 MPa	21000 psi	ISO 527-1, -2; 5 mm/min
Lanxess PocanÂ® ECO T 3230 000000 PBT + PET, 30% Glass Fiber PBT + PET, 30% glass fibers, injection molding, improved surface finish, contains 30% post-consumer recycled material, increased temperature peak loadInformation provided by LANXESS.
Tensile Strength at Break	145 MPa	21000 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP OFL36 PPS - Branched (Asia Pacific) LNP LUBRICOMP* OFL36 is a compound based on PPS - Branched resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Tensile Strength at Break	145 MPa	21000 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP OFL36A PPS - Branched (Europe-Africa-Middle East) LNP LUBRICOMP* OFL36 is a compound based on PPS - Branched resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Tensile Strength at Break	145 MPa	21000 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DX06094 PC (Europe-Africa-Middle East) LNP* THERMOCOMP* DX06094 is a compound based on Polycarbonate resin containing Glass Fiber . Added features include: High Impact, Non- Brominated & Non-Chlorinated Flame Retardant and Mold Release...
Tensile Strength at Break	145 MPa	21000 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP JF006E PES LNP* THERMOCOMP* JF006E is a compound based on Polyethersulfone resin containing 30% Glass Fiber. Added features of this material include: Easy Molding.
Tensile Strength at Break	145 MPa	21000 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP PF004 PA 6 (Europe-Africa-Middle East) 20% glass fibre reinforced Polyamide 6 injection moulding resin.
Tensile Strength at Break	145 MPa	21000 psi	ISO 527-93
Wellman Wellamid® GF1685-WBK1 Nylon 6, 20% Glass Fiber Reinforced All information provided by Wellman Engineered Resins.
Tensile Strength at Break	145 MPa	21000 psi	ISO 527-93
Wellman Wellamid® GFX1624-BK(PTFE) 30% Glass Fiber Reinforced, Lubricated Nylon 66 Description: Glass Fiber Reinforced, Lubricated Nylon 66Information provided by Wellman.
Tensile Strength at Break	145 MPa	21000 psi	ASTM D638
A. Schulman SCHULADUR® B GF30 30% Glass Fiber Reinforced PET Information provided by A. Schulman.
Tensile Strength at Break	145 MPa	21000 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® GV-2 FWA nat PA*-GF20 Product description: Grivory GV-2 FWA natural is a 20% glass fiber reinforced engineering thermoplastic material based on a combination of semicrystalline polyamide with partially aromatic copolyami..
Tensile Strength at Break	145 MPa	21000 psi	5 mm/min; ISO 527
CP-Polymer-Technik Wellamid® 6600 CF30 HWCP 30% Carbon Fiber Nylon 66, Heat Stabilized, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG
Tensile Strength at Break	145 MPa	21000 psi	DAM; ISO 527-1/-2
DuPont Performance Polymers Zytel® FE270038 BK267 Nylon 66  (Unverified Data**) 40% Glass/Mineral Reinforced Polyamide 66 Zytel FE270038 is a 40% glass fiber/mineral reinforced heat stabilized polyamid 66 for injection molding. It is well suited for water injection technology.I..
Tensile Strength at Break	145 MPa	21000 psi	5 mm/min; ISO 527
Eurostar Staramide PF005 PA6, 25% Glass Fiber Filled, Injection Molded Staramide PF005 is an 25% Glass Fiber Reinforced, Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
Tensile Strength at Break	145 MPa	21000 psi	ISO 527
Eurotec® Tecodur® PB70 GR30 NL XA 21 PBT/PET 30% glass fiber reinforced, UL94 V0 Excellent stiffness and hardnessGood mechanical strengthGood creep and fatigue behaviorVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance..
Tensile Strength at Break	145 MPa	21000 psi	ISO R 527
Addiplast Addinyl B2 V20 Nylon 6. 20% Glass Filled Glass fiber reinforced, high strengthInformation provided by Addiplast.
Tensile Strength at Break	145 MPa	21000 psi	0.2 in/min; ASTM Test
BASF Ultramid® 8232G HS FR BK-102 25% Glass Filled PA6 (Dry) Ultramid 8232G HS FR BK-102 is a 25% glass fiber reinforced, heat stabilized, flame retardant pigmented black PA6 injection molding compound exhibiting excellent melt stability characteristics. It ..
Tensile Strength at Break	145 MPa	21000 psi	0.2 in/min; ASTM Test
BASF Ultramid® 8234G HS 44% Glass Filled PA6 (Conditioned) Ultramid 8234G HS is a heat stabilized, 44% glass fiber reinforced polyamide 6 injection molding compound offering the highest level of strength, stiffness, high temperature performance and dimensio..
Tensile Strength at Break	145 MPa	21000 psi	ISO 527-2
Ascend Performance Materials Vydyne® R533H BK0201 Nylon 66, 33% Glass Reinforced, Conditioned Vydyne® R533H BK0201 is 33% glass-fiber reinforced, hydrolysis-resistant, heat-stabilized PA66 resin. Available in black, it is specifically designed to maximize the retention of physical propertie..
Tensile Strength at Break	145 MPa	21000 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP JF006EXZ PES LNP* THERMOCOMP* JF006EXZ is a compound based on Polyethersulfone resin containing 30% Glass Fiber. Added features of this material include: Easy Molding.