Polymer Property : Tensile Strength at Break = 21500 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	148 MPa	21500 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP DFL28 PC LNP* Lubricomp* DFL28 is a compound based on Polycarbonate resin containing 40% Glass Fiber and 10% PTFE. Added features include: Internally Lubricated.
Tensile Strength at Break	148 MPa	21500 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP DFL28 PC (Asia Pacific) LNP* Lubricomp* DFL28 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Tensile Strength at Break	148 MPa	21500 psi	ASTM D638
Ravago Manufacturing Americas Enviramid™ N2335HL BK Nylon 6 Available in North America Filler: Glass Fiber Reinforcement, 35% Filler by WeightAdditive: Heat Stabilizer and Lubricant Features: Lubricated and Heat StabilizedContains Recycled ContentRoHS Compl..
Tensile Strength at Break	148 MPa	21500 psi	ASTM D638
Ravago Manufacturing Americas Enviramid™ N2335HL BK Post Consumer Recycle Nylon 6, 35% Glass Filled Heat Stabilized, Lubricated, Black and made from EnViramid™ Post Consumer Recycled NylonInformation provided by Ravago.
Tensile Strength at Break	148 MPa	21500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP RFP36 PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RFP36 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE, Silicone.
Tensile Strength at Break	148 MPa	21500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM SF2260 PEI Blend (Asia Pacific) High flow Ultem for thin wall application
Tensile Strength at Break	148 MPa	21500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM SF2360 PEI Blend (Asia Pacific) High flow Ultem for thin wall application
Tensile Strength at Break	148 MPa	21500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON DX13320C PC COPOLYMER (Asia Pacific) LNP* Statkon DX13320C is ultra clean polycarbonate/carbon fiber compound with high modulus, good flow ability, easy mold release, and high level of cleanliness for the most demanding application. A ..
Tensile Strength at Break	148 MPa	21500 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DC006ER PC LNP THERMOCOMP* DC006ER is a compound based on Polycarbonate resin containing 30% Carbon Fiber. Added features of this material include: Easy Molding, Mold Release, Electrically Conductive.
Tensile Strength at Break	148 MPa	21500 psi	ISO 527
SABIC Innovative Plastics LNP Thermocomp DF008P PC LNP THERMOCOMP* DF008P is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Exceptional Processing.This data was supplied by SABIC-IP for the ..
Tensile Strength at Break	148 MPa	21500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP RF004XXH PA 66 LNP THERMOCOMP* RF004XXH is a compound based on Nylon 66 resin containing 20% Glass Fiber. Added feature of this grade is: Healthcare.
Tensile Strength at Break	148 MPa	21500 psi	ISO 527
SABIC Innovative Plastics LNP STAT-KON DE006ER PC LNP STAT-KON* DE006ER is a compound based on Polycarbonate resin containing 30% Carbon Fiber. Added features of this material include: Easy Molding. Mold Release, Electrically Conductive.
Tensile Strength at Break	148 MPa	21500 psi	ISO 527
SABIC Innovative Plastics LNP STAT-KON DE006ER PC (Asia Pacific) LNP STAT-KON* DE006ER is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Easy Molding.
Tensile Strength at Break	148 MPa	21500 psi	ISO 527
SABIC Innovative Plastics LNP Thermocomp DF008P PC (Asia Pacific) LNP* THERMOCOMP* DF008P is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Exceptional Processing.This data was supplied by SABIC-IP for the..
Tensile Strength at Break	148 MPa	21500 psi	ASTM D638
Chase Plastics CP Pryme® NN130M2 (Dry) Nylon 66, 30% Glass Fiber Reinforced, Lubricated Features: Good chemical resistanceGood compressive strengthGood creep resistanceFast cycleLubricatedHigh rigiditySolvent resistanceHigh strengthForm: PelletsInformation provided by Chase Plastics.
Tensile Strength at Break	148 MPa	21500 psi	ASTM D638
Chase Plastics CP Pryme® NN333L (Dry) Nylon 66, 33% Glass Fiber Reinforced, Lubricated, Recycled Content Features: LubricatedRecycled ContentForm: PelletsInformation provided by Chase Plastics.
Tensile Strength at Break	148 MPa	21500 psi	ISO 527-1/-2
Unitika A1025GO PA6, Flame Retardant, Dry Information provided by Unitika Ltd.
Tensile Strength at Break	148 MPa	21500 psi	DAM; ISO 527-1/-2
DuPont Performance Polymers Zytel® 80G33HS1L BK104 Nylon 66  (Unverified Data**) 33% Glass Reinforced Toughened Heat Stabilized Polyamide 66 Zytel 80G33HS1L BK104 is a 33% glass fiber reinforced heat stabilized black polyamide 66 resin with outstanding impact resistance develope..
Tensile Strength at Break	148 MPa	21500 psi	Type I, 5.1 mm/min; ASTM D638
PolyOne Nymax™ GF 1800 33 BLACK 13 Nylon 612 with 33% Glass Fiber  (discontinued **) Molded Test Bars: Dry as Molded
Tensile Strength at Break	148 MPa	21500 psi	ISO 527-1
Vyncolit Neopreg Kinel® SK4504 S12 Carbon Reinforced Molding Compound Epoxy based molding compound long carbon fiber reinforced suited for demanding tribologic applications under dry running conditions, exposed to a wide range of temperatures (-100°C up to 150°C)...
Tensile Strength at Break	148 MPa	21500 psi	ASTM D638
Polymer Resources PPX/NY G30 Modified PPO, 30% Glass Reinforced PPX/Nylon 6,6 Alloy  (Unverified Data**)&l Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.