Polymer Property : Tensile Strength at Break = 3340 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	23.0 MPa	3340 psi	50 mm/min; ASTM D638
Ovation Polymers Nemcon™ E HDPE 11000 HDPE HDPE-ESD Range Conductivity with improved processability and UV resistance.Information provided by Ovation Polymers
Tensile Strength at Break	<= 23.0 MPa	<= 3340 psi	ISO/R527
Polykemi AB POLYfill PPC 05ENH Polypropylene Copolymer, Flame Retardant, Halogen Free Information provided by Polykemi AB
Tensile Strength at Break	23.0 MPa	3340 psi	50 mm/min; ISO 527
Polimeri Europa Edistir RK Polystyrene  (discontinued **) UL94 V-0, flame retarded, high impact polystyrene. This grade is suitable for injection moulding. It combines high mechanical strength, heat resistance and good processability. Designation: Thermopl..
Tensile Strength at Break	23.0 MPa	3340 psi	50 mm/min; ISO 527
Polimeri Europa Edistir RKL Polystyrene  (discontinued **) UL94 V-0, flame retarded, high impact polystyrene. This grade is designed for the extrusion of flame retardant sheets, foils and profiles. Designation: Thermoplastics ISO 2897-PS-I,E,093-06-04-18App..
Tensile Strength at Break	23.0 MPa	3340 psi	ISO 527
FKuR Kunststoff Bio-FlexÂ® F 6510 Compostable PLA Blend The BIO-FLEXÂ® trade name indicates blends of co-polyester and PLA* with, depending on the particular grade, a very high content of natural resource material. BIO-FLEXÂ® does not contain any sta..
Tensile Strength at Break	23.0 MPa	3340 psi	50mm/min; ASTM D638
Kingfa FRHIPS-117 Flame Retardant Polystyrene Features:UL 94 V-0 @ 1.6 & 3.2mmExcellent balance properties, high strengthExcellent heat stabilityExcellent electrical propertiesApplications:Injection moldingGas moldingTV & Audio housingElectrica..
Tensile Strength at Break	23.0 MPa	3340 psi	ASTM D638
ITW Devcon Metal Repair Stainless Steel Putty (ST), Grey Information provided by ITW Devcon
Tensile Strength at Break	23.0 MPa	3340 psi
JPJ Technologies 5000S HDPE Extrusion Information provided by JPJ Technologies
Tensile Strength at Break	23.0 MPa	3340 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics NORYL WCA105 PPE-TPE (Europe-Africa-Middle East) Flexible, non-halogenated FR mPPE extrusion grade ideal for evaluation in applications such as wire insulation. Flame retardant performance capable of meeting VW1 and 105C temperature rating requir..
Tensile Strength at Break	23.0 MPa	3340 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics NORYL WCA901 PPE-TPE (Europe-Africa-Middle East) Non-Halogenated flame retardant, flexible Noryl resin intended for evaluation in wire and cable applications, capable of meeting VW-1 and 105°C end use temperature requirements as defined by UL..
Tensile Strength at Break	23.0 MPa	3340 psi	UL 1581
SABIC Innovative Plastics NORYL WCD855 PPE-TPE (Asia Pacific) Flexible and non-halogenated flame retardant extrusion grade intended for evaluation in applications such as cable jacket of UL 62 SPE and NISPE confiations. Flame retardant performance capable of m..
Tensile Strength at Break	23.0 MPa	3340 psi	ASTM D638
SABIC Innovative Plastics LNP STAT-LOY A3000T ABS (Asia Pacific) LNP* Stat-loy* A3000T is a compound based on Acrylonitrile Butadiene Styrene resin containing Anti-Static. Added features of this material include: Antistat.
Tensile Strength at Break	23.0 MPa	3340 psi	ISO 527
SABIC Innovative Plastics LNP Thermocomp KB005 Acetal Copolymer LNP THERMOCOMP* KB005 is a compound based on Acetal Copolymer resin containing Glass Bead.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break	23.0 MPa	3340 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP MFB71L PP LNP* THERMOCOMP* MFB71L is a compound based on Polypropylene resin containing 35% Glass Bead, 5% Glass Fiber. Added features of this material include: Low Extractible.
Tensile Strength at Break	23.0 MPa	3340 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP MFB71L PP (Asia Pacific) LNP* Thermocomp* MFB71L is a compound based on Polypropylene resin. Added features of this material include: Low Extractible.
Tensile Strength at Break	23.0 MPa	3340 psi	50mm/min; ISO 527
Borealis Borcell™ HE1346 High Density Polyethylene Borcell™ HE1346 is a fully formulated compound for chemical foamed telesingles. Borcell™ HE1346 is a high-density polyethylene compound containing chemical blowing agent. Applications Borcell™ HE..
Tensile Strength at Break	23.0 MPa	3340 psi	ISO 527-2
Tisan TISOPLEN® 10% Calcite Filled Heat Stabilized Copolymer Polypropylene TISOPLEN has a wide area of application in furniture, durable goods, household appliances, electrics/electronics, and telecommunication industries. General specifications include Low densityLow mois..
Tensile Strength at Break	23.0 MPa	3340 psi	ASTM D638
Toyobo PELPRENE™ P40U Polyester TPE, Weather-resistant Features: Polyester TPE, Weather-resistantInformation provided by Toyobo.
Tensile Strength at Break	23.0 MPa	3340 psi	ASTM D638
Eastman Eastman AP007 Copolyester Applications:Automotive componentsBreathable filmsElectronic componentsFilm ModificationFlexible hingesHose mandrelIndustrial componentsOffice furniturePackagingPolymer modificationProfilesRubber an..
Tensile Strength at Break	23.0 MPa	3340 psi	ASTM D638
Eastman Neostar FN007 Elastomer Neostar FN007 elastomer is the third in Eastman’s series of tough, clear, durable copolyester ethers. Though originally designed for use in the profile and automotive markets, this innovative copol..
Tensile Strength at Break	23.0 MPa	3340 psi	ASTM D 638
Cossa Polimeri ESTADIENE 2506 Acrylonitrile Butadiene Styrene ABS for sheet and profile extrusionHigh impact resistance, excellent heat resistance, excellent dimensional stability and processabilityInformation provided by Cossa Polimeri S.r.l.
Tensile Strength at Break	23.0 MPa	3340 psi	ASTM D 638
Cossa Polimeri ESTAPROP H 2550 CBS/E Polypropylene, 25% Mineral Filled PP homopolymer 25% mineral fillerHigh gloss, very high melt flow rate, excellent processabilityInformation provided by Cossa Polimeri S.r.l.
Tensile Strength at Break	23.0 MPa	3340 psi	ASTM D 638
Cossa Polimeri ESTASTIR HI 0508 V0 Flame Retardant Polystyrene Flame retardant class V0, PBDE free, good impact resistance, good thermal resistance, good processabilityInformation provided by Cossa Polimeri S.r.l.
Tensile Strength at Break	23.0 MPa	3340 psi	ISO 527-1/-2
DuPont Performance Polymers Hytrel® 3078FG Polyester Elastomer TPC-ET  (Unverified Data**) 30 Shore D High Performance Polyester Elastomer Developed for Food Contact ApplicationsInformation provided by DuPont Performance Polymers
Tensile Strength at Break	23.0 MPa	3340 psi	Compounded, 35 mins.; ISO 37
Dynasol Calprene® 1204B Solution Random SBR Calprene 1204B is a 75/25 Butadiene/Styrene Copolymer, polymerized in solution. It has a random structure with a typical vinyl content of 30%. It is presented in bales wrapped in low melting point p..
Tensile Strength at Break	23.0 MPa	3340 psi	ASTM D638
Azdel SuperLite® SL550700-100 PP Resin Matrix / 55% Glass Fiber (2 mm Molded Thickness) AZDEL SuperLite® SL550700-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic..
Tensile Strength at Break	23.0 MPa	3340 psi	ASTM D638
Aclo Accutech Polypropylene Homopolymer HP0334W30L1 Wollastonite Reinforced
Tensile Strength at Break	23.0 MPa	3340 psi	ISO 527-2
Total Lacqrene® 740 High Impact Polystyrene  (discontinued **) LACQRENE® alpha 740 is a high gloss, high impact grade of polystyrene.ApplicationWhite goods (washing machines, driers), Toys and games, Garden equipment, All applications needing high gloss with g..
Tensile Strength at Break	23.0 - 24.0 MPa	3340 - 3480 psi	ASTM D4745-97
Adamas Adalon® 600 PTFE, Boro Nitruro Information provided by Adamas, HPM
Tensile Strength at Break	23.0 MPa	3340 psi	ISO 527
SABIC Innovative Plastics LNP STAT-KON MFD02 PP (Asia Pacific) LNP* Stat-kon* MFD02 is a compound based on Polypropylene resin containing Glass Fiber, Carbon Powder. Added features of this material include: Electrically Conductive.