Polymer Property : Tensile Strength at Break = 4060 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	28.0 MPa	4060 psi	STN EN ISO 527-2
Plastcom SLOVALEN PC 78 FRD 1 Polypropylene Copolymer, Halogen Flame Retardant, UV Stabilized FeaturesModified copolymer PP with the possibility of changing the MFI within the interval 5 - 20 g/10min. Stabilized against the UV-radiation by the UV stabilizer on the HALS basis. Retarded with..
Tensile Strength at Break	28.0 MPa	4060 psi
Plastcom SLOVALEN PC 82 T 30 PP, 30% mineral filling FeaturesModified copolymer PP for injection moulding with the content of 30% micronized, floated, chemically modified talc. General application - packing material, garden flower-pots, toys, furnitur..
Tensile Strength at Break	28.0 MPa	4060 psi	ISO.527 DIN.53455
Omnia Plastica PE 300 - Polyethylene 300 Molecular weight 300,000 polyethylene similar to the type 500 with higher rigidity and lower resistance to continuous shocks. The applications are similar to those of PE 500, being more commonly spe..
Tensile Strength at Break	<= 28.0 MPa	<= 4060 psi	ISO/R527
Polykemi AB POLYfill PPH TS4020D Polypropylene Homopolymer, Mineral Reinforced, Detergent Resistant Information provided by Polykemi AB
Tensile Strength at Break	28.0 MPa	4060 psi	ISO 527
Eastman Eastar GN002 Copolyester, Natural  (discontinued **) Eastar GN002 Copolyester is a glycol modified polyethylene terephthalate (PET) with an added mold release. Eastar GN002 copolyester will not crystallize and thus offers wider processing latitude tha..
Tensile Strength at Break	28.0 - 35.0 MPa	4060 - 5080 psi	ASTM D638
Manifattura Cattaneo PTFE Polytetrafluoroethylene Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a.
Tensile Strength at Break	28.0 MPa	4060 psi	ASTM D638
IRPC Polimaxx Polene G2865 High Density Polyethylene CHARACTERISTICS: HIGH STIFFNESS, GOOD IMPACT STRENGTH, GOOD PROCESSABILITYAPPLICATIONS: BLOW MOLDING FOR CONTAINERS FROM A FEW ml TO ABOUT 20 LITRES, DIARY PRODUCT BOTTLES, FRUIT JUICE BOTTLES, ONE-..
Tensile Strength at Break	28.0 MPa	4060 psi	ISO 37
Huntsman AVALONÂ® 85 AE Thermoplastic Polyurethane Introduction: AVALON 85 AE is a general purpose polyester based thermoplastic polyurethane for injection molding. AVALON 85 AE is part of the AVALON Perform Range and offers a premium soiling materi..
Tensile Strength at Break	28.0 MPa	4060 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics NORYL WCV063 PPE+SEBS+Polyolefin (Europe-Africa-Middle East) Flexible, non-halogenated FR, mPPE extrusion grade material for evaluation in automotive wire coating applications requiring ISO6722.
Tensile Strength at Break	>= 28.0 MPa	>= 4060 psi	50 mm/min; ASTM D638
Solvay Specialty Polymers HyflonÂ® MFAÂ® F1530 Perfluoropolymer HyflonÂ® MFA is a family of perfluoro polymers which combine excellent mechanical characteristics to unique properties such as chemical inertness, high flexural endurance, inherent flame resistanc..
Tensile Strength at Break	28.0 MPa	4060 psi	50 mm/min; ISO 527
SABIC Innovative Plastics NORYL PPX PPX7200 PPE+PP+PS (Asia Pacific) PP+PPE+PS. Improved chemical resistance and surface aesthetics in injection molded applications. NSF61-capable. UL-94 HB listed.
Tensile Strength at Break	28.0 MPa	4060 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP MB006HS PP LNP* THERMOCOMP* MB006HS is a compound based on Polypropylene resin containing 30% Glass Bead. Added features of this material include: Heat Stabilized, Healthcare.
Tensile Strength at Break	28.0 MPa	4060 psi	50mm/min; ISO 527
Borealis Borstar® LE8706 Natural Bimodal LLDPE Jacketing Compound for Energy and Communication Cables Borstar® LE8706 is a natural colorable linear low density (LLD) jacketing compound, which is produced with the Borealis proprietary Borstar® bimodal process technology. Borstar technology allows ..
Tensile Strength at Break	28.0 MPa	4060 psi	ASTM D638
Total PSI 3341 High Impact Polystyrene Total Petrochemicals Polystyrene 3341 is a high impact polystyrene for the extrusion industry. Its good mechanical and thermal properties leads to the production of thermoformed articles of good ri..
Tensile Strength at Break	28.0 MPa	4060 psi	ASTM D638
Eastman Eastar MN210 Copolyester, Natural Eastar copolyesters are brilliantly clear polymers that have excellent impact strength, chemical resistance, dimensional stability, and low shrinkage rates.Applications/UsesMedical
Tensile Strength at Break	28.0 MPa	4060 psi	ASTM D 638
Cossa Polimeri ESTAPROP 1000 V2 K Flame Retardant Polypropylene PP copolymerFlame retardant class V2, PBDE free, good processability, good impact strengthInformation provided by Cossa Polimeri S.r.l.
Tensile Strength at Break	28.0 MPa	4060 psi	50 mm/min; ISO 527
Chi Mei Polylac® PA-709S ABS - Extrusion Super Impact Extrusion
Tensile Strength at Break	28.0 MPa	4060 psi	50 mm/min; ISO 527
Chi Mei Polylac® PA-765A ABS - Flame Retardant F.R. High Flow
Tensile Strength at Break	28.0 MPa	4060 psi	50mm/min; ISO 527-2
Denka TE-30 Transparent Resin Polymer (MABS resin) ABS "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a..
Tensile Strength at Break	28.0 MPa	4060 psi	ISO 527-1/-2
DuPont Performance Polymers Hytrel® HTR8341C BK320 Polyester Elastomer TPC-ET  (Unverified Data**) 40 Shore D Lubricated High Viscosity Polyester Elastomer with Superior Fatigue Resistance Developed for Blow Molding Information provided by DuPont Performance Polymers
Tensile Strength at Break	28.0 MPa	4060 psi	ASTM-D638
Braskem GM5240PR HDPE High Density Extrusion Polyethylene GM5240PR is a high-density polyethylene compound specially developed for the manufacturing of pipes, underground conduits, and steel pipe coating. This resin is produced with bimodal technology and ..
Tensile Strength at Break	28.0 MPa	4060 psi	ISO R 527
Addiplast Addilene J 310 Polypropylene Copolymer UnreinforcedInformation provided by Addiplast.
Tensile Strength at Break	28.0 - 35.0 MPa	4060 - 5080 psi	5 mm/min.; IS 867-1963
Amity Thermosets ATS 132 Phenolic Molding Organic, inorganic, and graphite Filler, Compression Molded Characteristics:Self lubricating ( graphite modified )Good glide propertiesGood sealing propertiesMedium or low mechanical strengthUnsuitable for electrical applicationGlossy surfaceThermal conducti..
Tensile Strength at Break	28.0 MPa	4060 psi
AorTech Biomaterials Elast-Eon™ E2-945 Biomedical Polyurethane Pellets Elast-Eon™ polymers are used in biomedical applications. They have high biostability so they can be used for long term implantation.
Tensile Strength at Break	28.0 MPa	4060 psi	ASTM D638
Aclo Accucomp ABS ABS804L High Impact Grade
Tensile Strength at Break	28.0 MPa	4060 psi	ASTM D638
Aclo Accutech Polypropylene Copolymer HP0335W40L Wollastonite Reinforced
Tensile Strength at Break	28.0 MPa	4060 psi	ASTM D638
Aclo Accutech Polypropylene Homopolymer HP0339W30L Wollastonite Reinforced
Tensile Strength at Break	28.0 MPa	4060 psi	ISO 527-2
Pasargad Polymer Peyvand Pasalen 3P-H3240B Polypropylene, 40% Mineral Filled Reinforced Form: PelletsProcessing Method: Injection MoldingUses: Automotive Application Furniture Appliance Components Automotive Exterior PartsAutomotive Interior PartsInformation provided by Pasargad Poly..
Tensile Strength at Break	<= 28.0 MPa	<= 4060 psi	ISO/R527
Polykemi AB POLYfill PPH TS5040DS Polypropylene Homopolymer, Mineral Reinforced, Detergent Resistant Information provided by Polykemi AB
Tensile Strength at Break	<= 28.0 MPa	<= 4060 psi	ISO/R527
Polykemi AB POLYfill PPH TS8038 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB