Polymer Property : Tensile Strength at Break = 58.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	58.0 MPa	8410 psi	50 mm/min; ISO 527
PolyOne Nymax™ 1308 A HS Natural Polyamide 66 (Nylon 66) The Nymax® Series of nylon 6/6 compounds have been specifically developed to deliver outstanding performance in a wide range of application areas. These materials are available with a broad range o..
Tensile Strength at Break	58.0 MPa	8410 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Cycoloy® CX7240U PC+ABS (Asia Pacific) Cycoloy* CX7240U resin is an injection moldable PC/ABS blend with a UV stabilization package. It contains non-brominated and non-chlorinated flame retardant systems to meet thin wall flame resistanc..
Tensile Strength at Break	58.0 MPa	8410 psi	Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Cycoloy® CX7240U PC+ABS (Europe-Africa-Middle East) Cycoloy* CX7240U resin is an injection moldable PC/ABS blend with a UV stabilization package. It contains non-brominated and non-chlorinated flame retardant systems to meet thin wall flame resistanc..
Tensile Strength at Break	58.0 MPa	8410 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® EXL1890T PC Copolymer (Europe-Africa-Middle East) Lexan* EXL1890T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade for food contact applications. This resin offers cold temperature (0 °C) ductility in combin..
Tensile Strength at Break	58.0 MPa	8410 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® EXL9112 PC Copolymer Opaque PC-Siloxane copolymer with excellent processability. Improved flow, low temp. ductility. Non-chlorinated, non-brominated flame retardant product. UL rated V-0/5VA.
Tensile Strength at Break	58.0 MPa	8410 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® FST9436 PC Copolymer Medium viscosity opaque, low smoke, and OSU 65/65 compliant PC Copolymer
Tensile Strength at Break	58.0 MPa	8410 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® FXD1433T PC Copolymer Clear PC-siloxane copolymer with excellent processability in special light diffusion colors. Medium flow, UV stabilized. Improved toughness compared to standard PC in same color. Color package may ..
Tensile Strength at Break	58.0 MPa	8410 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® HPX8REU PC Copolymer (Europe-Africa-Middle East) Very high flow specialty polycarbonate with outstanding processability and ductility. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 o..
Tensile Strength at Break	58.0 MPa	8410 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® ML3729 PC Excellent flow, UV stabilized, grade which contains a release agent to ensure easy processing.
Tensile Strength at Break	58.0 MPa	8410 psi	Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Lexan® EXL1860T PC Copolymer Lexan* EXL1860T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers improved release performance, cold temperature (0 °C) ductility in combi..
Tensile Strength at Break	58.0 MPa	8410 psi	Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Lexan® EXL1860T PC Copolymer (Asia Pacific) Lexan* EXL1860T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers improved release performance, cold temperature (0 °C) ductility in combi..
Tensile Strength at Break	58.0 MPa	8410 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® FXD1413T PC Copolymer (Europe-Africa-Middle East) Clear PC-siloxane copolymer with excellent processability, in special light diffusion colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may af..
Tensile Strength at Break	58.0 MPa	8410 psi	Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Lexan® FXE1810T PC Copolymer (Europe-Africa-Middle East) Lexan* FXE1810T polycarbonate (PC) siloxane copolymer resin is a transparent injection moldable grade. This specialty PC offers excellent processability, very high flow and improved ductility charac..
Tensile Strength at Break	58.0 MPa	8410 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® HP1HF PC (Asia Pacific) Very high flow, biocompatible polycarbonate for healthcare applications. EtO sterilizable.
Tensile Strength at Break	58.0 MPa	8410 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® LUX9616G PC (Europe-Africa-Middle East) Lexan LUX9616G (EXRL0945) is a UV stabilized high viscosity, flame retardant polycarbonate featuring non brominated and non chlorinated FR system with diffusion effect and thin wall FR performance p..
Tensile Strength at Break	58.0 MPa	8410 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP COLORCOMP DX06407H PC LNP* COLORCOMP* DX06407H is an unfilled Polycarbonate. Added features of this material include: Easy Molding, Mold Release, Healthcare
Tensile Strength at Break	58.0 MPa	8410 psi	ISO 527
SABIC Innovative Plastics LNP STAT-LOY 9X03508 PPO+PA66 (Asia Pacific) LNP* Stat-loy* 9X03508 is a compound based on PPO+PA66 resin containing Flame Retardant, Anti-Static. Added features of this material include: Antistat, Flame Retardant, High Impact.
Tensile Strength at Break	58.0 MPa	8410 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP Thermocomp OX92080 PPS - LINEAR LNP* Thermocomp* OX92080 is a compound based on Linear PPS containing Proprietary Fillers.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break	58.0 MPa <br>@Thickness 4.00 mm	8410 psi <br>@Thickness 0.157 in	50mm/min, injection molded, unannealed; ISO 527-2
Styron EMERGEâ„¢ 8600-20 Polycarbonate EMERGEâ„¢ PC 8600-20 is a translucent, ignition-resistant and easy flow polycarbonate resin. The resin contains no bromine, chlorine or phosphate additives and is intended to comply with global ..
Tensile Strength at Break	58.0 MPa	8410 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP YF002 POLYESTER ELASTOMER LNP* THERMOCOMP* YF002 is a compound based on Poyester Elastomer containing 10% Glass Fiber. Added feature of this grade is: High Modulus.
Tensile Strength at Break	58.0 MPa	8410 psi	50 mm/min; ISO 527
SABIC Innovative Plastics NORYL NH6010B PPE+HIPS (Asia Pacific) Noryl* NH6010B resin is a high performance, modified PPE-PS blend that exhibits an excellent balance of lower smoke production upon burning, nonhalogenated flame retardance and low specific gravity...
Tensile Strength at Break	58.0 MPa	8410 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Noryl PPX PPX615 PPE+PP Good chemical resistance. Designed for a balance of stiffness and practical impact strength.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break	58.0 MPa	8410 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP KFI12 Acetal Copolymer LNP LUBRICOMP* KFI12 is a compound based on Acetal Copolymer resin containing 10% Glass Fiber, 2% Silicone. Added feature of this grade is: Wear Resistant.
Tensile Strength at Break	58.0 MPa	8410 psi	50 mm/min; ISO 527
SABIC Innovative Plastics ValoxÂ® FXV310SK PBT VALOX FXV310SK is an unreinforced PBT injection moulding Visualfx* resin with high flow characteristics and containing a metal sparkle. Applications: automotive bezels and appliances.
Tensile Strength at Break	58.0 MPa	8410 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP 9X11428J PPS LNP* THERMOCOMP* 9X11428J is a compound based on Polyphenylsulfone containing Proprietary Fillers. Added features of this material include: Healthcare, Low Extractable.
Tensile Strength at Break	58.0 MPa	8410 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP MF742XXH PP LNP* THERMOCOMP* MF742XXH is a compound based on Polypropylene resin containing Glass Fiber and proprietary antimicrobial additives. This product is best suited for touch surfaces in healthcare app..
Tensile Strength at Break	58.0 MPa	8410 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP RB006 PA 66 LNP* THERMOCOMP* RB006 is a compound based on Nylon 66 resin containing 30% Glass Bead.
Tensile Strength at Break	58.0 MPa	8410 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Noryl FXN2090H PPE+HIPS (Europe-Africa-Middle East) Noryl* FXN2090H resin is an unfilled, injection moldable grade. Designed for exceptionally high gloss and improved pencil hardness vs. standard Noryl grades, FXN2090H resin uses non-halogenated FR a..
Tensile Strength at Break	58.0 MPa	8410 psi	50%RH; ISO 527-1/-2
DuPont Performance Polymers Minlon® 12TA BKB124 Nylon 66  (Unverified Data**) 32% Mineral Reinforced Toughened Polyamide 66 Minlon 12TA BKB124 is a 32% mineral reinforced toughened heat stabilized black polyamide 66 resin for injection molding.Information provided by DuPont P..
Tensile Strength at Break	58.0 MPa <br>@Temperature 80.0 °C	8410 psi <br>@Temperature 176 °F	ISO Data
BASF Ultramid® SEGM35 H1 BK-126 15/25% Glass/Mineral Filled PA6 (Dry) Ultramid SEGM35 H1 BK-126 is a 40% glass/mineral reinforced injection molding grade. It offers enhanced surface appearance, it also exhibits similar UV weathering characteristics compared to 8267G ..