Polymer Property : Tensile Strength at Break = 60.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	50.0 - 60.0 MPa	7250 - 8700 psi	ASTM D638-03
Proto3000 Objet Digital Materials™ DM_8210 Rigid Opaque Prototyping Polymer Primary material: VeroBlueSecondary material: VeroBlackDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to provide the ..
Tensile Strength at Break	40.0 - 60.0 MPa	5800 - 8700 psi	ASTM D638-03
Proto3000 Objet Digital Materials™ DM_8505Gray20 Rigid Opaque Prototyping Polymer Primary material: VeroWhitePlusSecondary material: TangoBlackPlusDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to pr..
Tensile Strength at Break	40.0 - 60.0 MPa	5800 - 8700 psi	ASTM D638-03
Proto3000 Objet Digital Materials™ DM_8505Gray25 Rigid Opaque Prototyping Polymer Primary material: VeroWhitePlusSecondary material: TangoBlackPlusDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to pr..
Tensile Strength at Break	40.0 - 60.0 MPa	5800 - 8700 psi	ASTM D638-03
Proto3000 Objet Digital Materials™ DM_8505Gray35 Rigid Opaque Prototyping Polymer Primary material: VeroWhitePlusSecondary material: TangoBlackPlusDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to pr..
Tensile Strength at Break	40.0 - 60.0 MPa	5800 - 8700 psi	ASTM D638-03
Proto3000 Objet Digital Materials™ DM_8505Gray40 Rigid Opaque Prototyping Polymer Primary material: VeroWhitePlusSecondary material: TangoBlackPlusDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to pr..
Tensile Strength at Break	50.0 - 60.0 MPa	7250 - 8700 psi	ASTM D638-03
Proto3000 Objet Digital Materials™ DM_Dots_7513 Transparent Prototyping Polymer Primary material: FullCure720Secondary material: VeroBlackDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to provide t..
Tensile Strength at Break	50.0 - 60.0 MPa	7250 - 8700 psi	ASTM D638-03
Proto3000 Objet Digital Materials™ DM_Grid_7523 Transparent Prototyping Polymer Primary material: FullCure720Secondary material: VeroBlackDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to provide t..
Tensile Strength at Break	55.0 - 60.0 MPa	7980 - 8700 psi	ASTM D638-03
Proto3000 Objet Digital Materials™ RGD5160-DM ABS-like Prototyping Polymer Objet ABS-like Digital Material made of Object RGD515 & Objet RGD535Digital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to..
Tensile Strength at Break	50.0 - 60.0 MPa	7250 - 8700 psi	ASTM D638-03
Proto3000 Objet VeroBlue FullCure840 Rigid Opaque Prototyping Polymer Objet’s FullCure® Materials family of proprietary acrylic-based photopolymer materials enables Objet users to create highly accurate, finely detailed 3D models and parts for a wide range of Rapid ..
Tensile Strength at Break	55.0 - 60.0 MPa	7980 - 8700 psi	ASTM D683
Loxim 600 00HB Polycarbonate/Polybutylene Terephthalate Information provided by Loxim Industries
Tensile Strength at Break	50.0 - 60.0 MPa	7250 - 8700 psi	ISO 527
Vyncolit 4221 XB Novolac Phenolic Mineral and organic filled phenolic molding compound with good mechanical properties.Information provided by Vyncolit, a Sumitomo Bak Group
Tensile Strength at Break	50.0 - 60.0 MPa	7250 - 8700 psi	ISO 527
Vyncolit 4451 XB Novolac Phenolic Organic and mineral filled phenolic molding compound with excellent mechanical properties (highest notched impact strength).USES: Fuse holders, brush holders, circuit breakers, automotive ignition a..
Tensile Strength at Break	40.0 - 60.0 MPa	5800 - 8700 psi	ISO 527
Vyncolit X658 Novolac Phenolic Glass fiber and mineral filled phenolic molding compound with excellent mechanical and thermal properties and a very good dimensional stability.USES: Complex precision parts.Information provided by ..
Tensile Strength at Break	50.0 - 60.0 MPa	7250 - 8700 psi	ISO 527
Vyncolit X681 Novolac Phenolic Glass fiber filled phenolic molding compound with excellent mechanical properties and a low coefficient of friction. Tribological compound with PTFE additive.USES: Water pump seals and self-lubrica..
Tensile Strength at Break	46.0 - 60.0 MPa	6670 - 8700 psi	5 mm/min.; IS 867-1963
Amity Thermosets ATM 122 Phenolic Molding Organic Filler, Compression Molded Characteristics:Good mouldability Good mechanical strengthGood electrical insulationGood surface finishMedium thermal stabilityColor- black, brownSoft/medium flow Applications: Electric control pane..
Tensile Strength at Break	46.0 - 60.0 MPa	6670 - 8700 psi	5 mm/min.; IS 867-1963
Amity Thermosets ATM 144 Phenolic Molding Organic Filler, Compression Molded Characteristics:Good mouldability Good mechanical strengthGood electrical insulationGood surface finishMedium thermal stabilityColor- black, brownSoft/medium flow Applications: Electric control pane..
Tensile Strength at Break	50.0 - 60.0 MPa	7250 - 8700 psi	5 mm/min.; IS 867-1963
Amity Thermosets ATO 142 Phenolic Molding Organic Filler, Compression Molded Characteristics:Electrical low loss Good mechanical strengthHigh electrical insulationGood mechanical strengthGlossy surfaceLow water absorptionColor-black, brownMedium/hard flow Applications: Elec..
Tensile Strength at Break	53.0 - 60.0 MPa	7690 - 8700 psi	5 mm/min.; IS 867-1963
Amity Thermosets ATO 156 Phenolic Molding Glass Filler, Compression Molded Characteristics:High electrical insulationHigh mechanical strengthDimensional stabilityLow water absorptionColor-black Medium flow Applications: High electric insulation componentsHigh voltage swit..
Tensile Strength at Break	50.0 - 60.0 MPa	7250 - 8700 psi	5 mm/min.; IS 867-1963
Amity Thermosets ATS 135 Phenolic Molding Inorganic and glass fiber Filler, Compression Molded Characteristics: Self lubricating Good mechanical strength Low co-efficient of friction Good thermal conductivity Heat stable (200°C) Good mouldability Not suitable for electrical application Color..