Polymer Property : Tensile Strength at Break = 6530 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	45.0 MPa	6530 psi	5 mm/min; ISO 527
SABIC Innovative Plastics Cycoloy® C1204HF PC+ABS (Asia Pacific) High heat PC/ABS blend offering good flow and excellent impact. Food compliant according to FDA and European directive 2002/72/EC. Available in limited colors. Effective January 15th, 2008 this gra..
Tensile Strength at Break	45.0 MPa	6530 psi	5 mm/min; ISO 527
SABIC Innovative Plastics Cycoloy® C2100 PC+ABS (Europe-Africa-Middle East) CYCOLOY C2100 is a flame retardant blend, specifically developed to meet the stringent requirements of mains current carrying applications. CYCOLOY C2100 combinesThis data was supplied by SABIC-IP f..
Tensile Strength at Break	45.0 MPa	6530 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Cycoloy® CE8510 PC+ABS (Europe-Africa-Middle East) Extrusion grade PC/ABS. Low viscosity, high impact and ductility.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Tensile Strength at Break	45.0 MPa	6530 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Cycoloy® CU6800 PC+ABS (Europe-Africa-Middle East) Non-chlorinated and non-brominated flame retardant PC/ABS featuring excellent flow properties for a wide variety of applications including business equipment, TVs, monitors, enclosures, among others..
Tensile Strength at Break	45.0 MPa	6530 psi	5 mm/min; ISO 527
SABIC Innovative Plastics Cycoloy® XCM850 PC+ABS (Europe-Africa-Middle East) Reinforced PC/ABS with high stiffness and low CTE.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Tensile Strength at Break	45.0 MPa	6530 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Geloy XTPMFR15 ASA+PC (Europe-Africa-Middle East) Geloy XTPMFR15 is a chlorine and bromine free flame retardant ASA/PC blend with improved impact performance/ductility and an UL94 rating of V0 at 1.5mm. This grade has a f1 rating according UL746C.T..
Tensile Strength at Break	<= 45.0 MPa	<= 6530 psi	ISO/R527
Polykemi AB SCANBLEND FS7 FR UV PC/ASA Blend, Flame-Retardant, UV Stabilized Information provided by Polykemi AB
Tensile Strength at Break	45.0 MPa	6530 psi	5 mm/min; ISO 527
SABIC Innovative Plastics Lexan® 3441R PC (Europe-Africa-Middle East) Lexan 3441R is a medium viscosity, 10% glass reinforced polycarbonate grade, compliant with European food contact regulation EC Directive 2002/72/EC. The grade is especially designed for application..
Tensile Strength at Break	45.0 MPa	6530 psi	5 mm/min; ISO 527
SABIC Innovative Plastics Lexan® 500ECR PC (Asia Pacific) Lexan* 500ECR Polycarbonate (PC) resin is a 10% glass fiber filled, injection moldable grade. It is of non-chlorinated & non-brominated flame retardant systems with UL-94 V0 rating at 2.3mm. It is a..
Tensile Strength at Break	>= 45.0 MPa	>= 6530 psi	ISO 178
Perstorp Compounds AMITEC 751 Melamine Perstorp dinnerware compression and injection grade. Porcelain like properties suitable for household applications.Information provided by Perstorp Compounds Inc.
Tensile Strength at Break	45.0 MPa	6530 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP KONDUIT OX11314 PPS (Asia Pacific) Thermally conductive mineral filled PPS FR compound
Tensile Strength at Break	45.0 MPa	6530 psi	5 mm/min; ISO 527
SABIC Innovative Plastics Lexan® HF500R PC (Europe-Africa-Middle East) LEXAN HF500R is an easy flow, 9% glass reinforced, flame retardant grade, especially designed for applications requiring high rigidity together with high heat resistance and impact performance.
Tensile Strength at Break	45.0 MPa	6530 psi	5 mm/min; ISO 527
SABIC Innovative Plastics Lexan® ML3019 PC (Europe-Africa-Middle East) LEXAN ML3019 is a medium viscosity, 10% glass reinforced, flame retardant grade, especially designed for applications like industrial enclosures and fuse boxes requiring a low knock-out strength for..
Tensile Strength at Break	45.0 MPa	6530 psi
Huntsman IROGRANÂ® A 85 P 4394 FCM Ether-Based TPU-For Food Contact Extrusion grade; High microbial resistance, high transparencyInformation provided by Huntsman
Tensile Strength at Break	45.0 MPa	6530 psi	DIN 53504
Huntsman IROGRANÂ® A 87 H 4615 Polyester-Based TPU-Injection Molding Grade Introduction: IROGRAN A 87 H 4615 is a thermoplastic polyester- polyurethane for injection molding applications. Additional characteristics of the product are very short cycle times and high dimensi..
Tensile Strength at Break	45.0 MPa	6530 psi	50 mm/min; ISO 527
SABIC Innovative Plastics NORYL SE100 PPE+HIPS (Europe-Africa-Middle East) NORYL® SE100 is an unfilled, flame retardant material with a Vicat B/120 of 120Â°C. It has a UL-94 flammability rating V1 @ 1.47 mm, and is halogen free according to VDE/DIN 472 part 815.
Tensile Strength at Break	45.0 MPa	6530 psi
Shandong Guangyin Special Resin for Badminton Features and Applications: Wear resistance, higher strength, better tenacity, strong adhesion and better low temperature resistance. It is applicable to surface coating of wires, cables, optical cab..
Tensile Strength at Break	45.0 MPa	6530 psi	50 mm/min; ISO 527
SABIC Innovative Plastics XenoyÂ® X4870HH PC+PET (Asia Pacific) Xenoy X4870HH is a high heat, very high modulus and ductile PC/PET blend. Furthermore this resin provides chemical resistance, very low creep, low CTE, excellent fatique and high heat dimensional st..
Tensile Strength at Break	45.0 MPa	6530 psi	Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics NORYL GTX GTX944 PPE+PA (Europe-Africa-Middle East) NORYL GTX944 is an unfilled GTX grade with improved processability and increased impact performance.
Tensile Strength at Break	45.0 MPa	6530 psi	ISO 527-2
Tisan TISAKRIL® UNR ABS TISAKRIL has a wide area of application in automotive, electronics, computer, construction, and furniture industries. General Specifications include: High surface luminosityEasy processabilityDimens..
Tensile Strength at Break	45.0 MPa	6530 psi	ISO 527-93
Wellman Wellamid® XT1482-WT1 High Impact Nylon 66 Description: High Impact Nylon 66Information provided by Wellman.
Tensile Strength at Break	45.0 MPa	6530 psi	conditioned; ISO 527-1/-2
EMS-Grivory Grivory® XE 3997 nat PAMACM12 Product description: Grilamid XE 3997 natural is a transparent thermoplastic polyamide based on aliphatic and cycloaliphatic blocks. Grilamid XE 3997 natural is particularly suitable for blow molded..
Tensile Strength at Break	45.0 MPa	6530 psi	conditioned; ISO 527-1/-2
EMS-Grivory Grivory® XE 4073 nat PA610 Product description: Grilamid XE 4073 natural is a unreinforced, heat and UV stabilized polyamide 610 (PA610) injection molding grade. This product is to a large extent based on renewable raw materi..
Tensile Strength at Break	45.0 MPa	6530 psi	ISO 527
Eurotec® Tecodur® PB70 NL TD20 PBT, unfilled, flame retardant - halogen (RoHS compliant), impact modified, natural Information provided by Eurotec®
Tensile Strength at Break	45.0 MPa	6530 psi	conditioned; ISO 527-1/-2
EMS-Grivory Grivory® BRZ 340 H PA6 Product description: Grilon BRZ 340 H is a heat stabilized, high viscosity, impact modified PA6 extrusion grade. Grilon BRZ 340 H has the following important properties:High impact strength at low t..
Tensile Strength at Break	45.0 MPa @Temperature 120 °C	6530 psi @Temperature 248 °F	ISO Data
BASF Ultramid® 8272G HS BK-102 12% Glass Filled PA6 (Dry) Ultramid 8272G HS BK-102 is a 12% glass fiber reinforced, black pigmented, thermally modified, nylon 6 blow molding compound offering an excellent balance of engineering properties combined with the..
Tensile Strength at Break	45.0 MPa	6530 psi	ASTM D638
Aclo Accutech Polypropylene Copolymer CP0436G25M5CL Glass/Mineral Reinforced Coupled
Tensile Strength at Break	45.0 MPa	6530 psi	5 mm/min; ISO 527
CP-Polymer-Technik Wellamid® 6000 GS 25 HWCP 25% Glass Sphere Filled Nylon 6, Heat Stabilized, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG
Tensile Strength at Break	45.0 MPa	6530 psi	ISO 527-2
Ascend Performance Materials Vydyne® 21SPF1 Nylon 66, Conditioned Vydyne® 21SPF1 is a general-purpose PA66 resin available in natural color. It is designed principally for injection-molding applications with the added benefits of improved flow during the molding ..