Mechanical PropertiesTips: 30 items are displayed at most.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 51.0 MPa | 7400 psi | Type I, 50 mm/min; ASTM D638 |
|
SABIC Innovative Plastics Cycoloy® C3650 PC+ABS
Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering high impact and excellent extrusion and thermoforming characteristics. Halogen free according ..
|
|||
| Tensile Strength at Break | 51.0 MPa | 7400 psi | 5 mm/min; ISO 527 |
|
SABIC Innovative Plastics Cycoloy® C7240P PC+ABS (Asia Pacific)
Cycoloy* C7240P resin is a mineral filled, flame retardant PC/ABS. High stiffness combined with balanced flow and impact performance, makes it a good condidate for various applications.
|
|||
| Tensile Strength at Break | 51.0 MPa | 7400 psi | 50 mm/min; ISO 527 |
|
SABIC Innovative Plastics Cycoloy® CY9640 PC+ABS (Asia Pacific)
PC+ ABS, High Impact and High Flow, ductility at low temperature, excellent properties retention after Hydrolytic and Heat Aging
|
|||
| Tensile Strength at Break | 51.0 MPa | 7400 psi | 50 mm/min; ISO 527 |
|
SABIC Innovative Plastics Cycoloy® XCY620 PC+ABS (Asia Pacific)
PC+ ABS Automotive applications, High Impact and High Flow, ductility at low temperature, excellent properties retention after Hydrolytic and Heat Aging
|
|||
| Tensile Strength at Break | 51.0 MPa | 7400 psi | 5 mm/min; ISO 527 |
|
SABIC Innovative Plastics GELOY HRA222F ASA+PC
Geloy HRA222F is a multi-purpose, chlorine and bromine free flame retardant PC+ASA alloy for injection molding processes. F1 rating according UL746C. Use for exterior/interior electrical application..
|
|||
| Tensile Strength at Break | 51.0 MPa | 7400 psi | Type I, 50 mm/min; ASTM D638 |
|
SABIC Innovative Plastics Lexan® 905 PC Copolymer (Asia Pacific)
Lexan 905 resin is a high flow, opaque, flame retardant polycarbonate resin blend. It is designed with non-chlorinated, non-brominated FR systems with UL-94 listing of both V0 and 5V ratings. Its ex..
|
|||
| Tensile Strength at Break | 51.0 MPa | 7400 psi | Type I, 50 mm/min; ASTM D638 |
|
SABIC Innovative Plastics Lexan® CFR9712 PC COPOLYMER (Europe-Africa-Middle East)
Lexan* CFR9712 Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 2.0 mm and high flow capability. ..
|
|||
| Tensile Strength at Break | 51.0 MPa | 7400 psi | Type I, 50 mm/min; ASTM D638 |
|
SABIC Innovative Plastics Lexan® FXD1414T PC Copolymer (Asia Pacific)
PC-siloxane copolymer in special light diffusion colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may affect performance.
|
|||
| Tensile Strength at Break | 51.0 MPa | 7400 psi | 50 mm/min; ISO 527 |
|
SABIC Innovative Plastics Lexan® ML7681 PC Copolymer (Asia Pacific)
Polycarbonate with high flow, good processability, good impact and thermal properties, non-Chlorine and non-Bromine flame retardant, UL rated V-0 and V-1. Available in limited translucent colors onl..
|
|||
| Tensile Strength at Break | 51.0 MPa | 7400 psi | ASTM D638 |
|
Albis Plastics Cellulose Acetate Butyrate B930 (Base Grade), 4% Plasticizer
(discontinued **)
Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T..
|
|||
| Tensile Strength at Break | 51.0 MPa | 7400 psi | ASTM D638 |
|
Albis Plastics Cellulose Acetate Butyrate B9304 (Odor Mask Added), 4% Plasticizer
(discontinued **)
Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T..
|
|||
| Tensile Strength at Break | 51.0 MPa | 7400 psi | ASTM D638 |
|
Albis Plastics Cellulose Acetate Butyrate B9324 (UVI, Odor Mask Added), 4% Plasticizer
(discontinued **)
Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and T..
|
|||
| Tensile Strength at Break | 51.0 MPa | 7400 psi | Type I, 5 mm/min; ASTM D638 |
|
SABIC Innovative Plastics LNP LUBRICOMP DX09410H PC
LNP* LUBRICOMP* DX09410H is a compound based on Polycarbonate resin containing Proprietary FIllers. Added features of this grade include: Healthcare, Wear Resistant.
|
|||
| Tensile Strength at Break | 51.0 MPa | 7400 psi | Type I, 5 mm/min; ASTM D 638 |
|
SABIC Innovative Plastics LNP Lubricomp PL004 PA 6
LNP* Lubricomp* PL004 is a compound based on Nylon 6 containing PTFE Lubricant. Characteristics of this grade are Internally Lubricated.This data was supplied by SABIC-IP for the Americas region.
|
|||
| Tensile Strength at Break | 51.0 MPa | 7400 psi | ASTM D638 |
|
SABIC Innovative Plastics LNP LUBRILOY D20009P PC
LNP* LUBRILOY* D20009P is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Wear Resistant, Flame Retardant, Exceptional Processing...
|
|||
| Tensile Strength at Break | 51.0 MPa | 7400 psi | ASTM D638 |
|
SABIC Innovative Plastics LNP LUBRILOY K2000 Acetal
LNP LUBRILOY* K2000 is a compound based on Acetal resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant.
|
|||
| Tensile Strength at Break | 51.0 MPa | 7400 psi | ASTM D638 |
|
SABIC Innovative Plastics LNP LUBRILOY K2000XXH Acetal
LNP LUBRILOY* K2000XXH is a compound based on Acetal resin containing Proprietary Lubricant. Added features of this material are: Wear Resistant, Healthcare.
|
|||
| Tensile Strength at Break | 51.0 MPa | 7400 psi | ISO 527 |
|
SABIC Innovative Plastics LNP STAT-KON DD000P PC (Asia Pacific)
LNP* Stat-kon* DD000P is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Electrically Conductive, Exceptional Processing.
|
|||
| Tensile Strength at Break | 51.0 MPa | 7400 psi | Type I, 5 mm/min; ASTM D638 |
|
SABIC Innovative Plastics LNP THERMOCOMP AFB42 ABS
LNP* THERMOCOMP* AFB42 is a compound based on ABS containing 10% Glass Fiber, 20% Glass Bead.
|
|||
| Tensile Strength at Break | 51.0 MPa | 7400 psi | 50 mm/min; ISO 527 |
|
SABIC Innovative Plastics Noryl GTX GTX9200 PPE+PS+PA66 (Asia Pacific)
High Flow GTX for Automotive applicationsThis data was supplied by SABIC-IP for the Asia Pacific region.
|
|||
| Tensile Strength at Break | 51.0 MPa | 7400 psi | 50 mm/min; ISO 527 |
|
SABIC Innovative Plastics Noryl GTX GTX9200 PPE+PS+PA66 (Europe-Africa-Middle East)
High Flow GTX for Automotive applicationsThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
|
|||
| Tensile Strength at Break | 51.0 MPa | 7400 psi | Type I, 5 mm/min; ASTM D 638 |
|
SABIC Innovative Plastics Noryl HS1000X PPE+PS
PPE+PS blend. 13% Mineral reinforced. Non-brominated, non-chlorinated FR system. UL94 V0 and 5VA listing. UL 746C f1. Radiant Panel listing. Dielectric strength. Dimensional stability. Suitable for ..
|
|||
| Tensile Strength at Break | 51.0 MPa | 7400 psi | ISO 527 |
|
SABIC Innovative Plastics LNP STAT-KON DD0009PC PC
LNP STAT-KON* DD0009PC is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Electrically Conductive, Flame Retardant.
|
|||
| Tensile Strength at Break | 51.0 MPa | 7400 psi | Type I, 50 mm/min; ASTM D638 |
|
SABIC Innovative Plastics Valox® IQ3001 PBT
Valox IQ3001 is an unfilled environmentally responsible iQ-PBT resin modified with elastomer. Targeted for flexible hinge applications.
|
|||
| Tensile Strength at Break | 51.0 MPa | 7400 psi | ASTM D638 |
|
SABIC Innovative Plastics LNP THERMOCOMP MF002S PP
LNP* Thermocomp* MF002S is a compound based on Polypropylene resin containing 10% Glass Fiber. Added features of this material include: Heat Stabilized.
|
|||
| Tensile Strength at Break | 51.0 MPa | 7400 psi | 5 mm/min; ISO 527 |
|
SABIC Innovative Plastics LNP THERMOCOMP MF002S PP (Europe-Africa-Middle East)
LNP* THERMOCOMP* MF002S is a compound based on Polypropylene resin containing Glass Fiber. Added features include: Heat Stabilized.
|
|||
| Tensile Strength at Break | 51.0 MPa | 7400 psi | ASTM D638 |
|
Eastman DuraStar MN611 Polymer, Natural
Durastar Polymer MN611 contains a mold release. It has excellent appearance and is nearly water-clear. Its most outstanding features are toughness, chemical resistance, and excellent processing char..
|
|||
| Tensile Strength at Break | 51.0 MPa | 7400 psi | ASTM D412 |
|
Alliance Polymers Zythane™ 3045D Thermoplastic Polyurethane Elastomer
Zythane™ 3045D is a polycaprolactone-based TPU specifically formulated for injection molding applications .It exhibits excellent low compression set, abrasion resistance and toughness and has good ..
|
|||
| Tensile Strength at Break | 51.0 MPa | 7400 psi | ASTM D412 |
|
Alliance Polymers Zythane™ 7065D Thermoplastic Polyurethane Elastomer
Zythane™ 7065D is a polycaprolactone-based TPU specifically formulated for injection molding applications .It exhibits excellent low compression set, abrasion resistance and toughness and has good ..
|
|||
| Tensile Strength at Break |
51.0
MPa <br>@Temperature 120 °C
|
7400
psi <br>@Temperature 248 °F
|
ASTM Test |
|
BASF Ultramid® 8267G HS BK-106 15/25% Glass/Mineral Filled PA6 (Dry)
Ultramid 8267G HS BK-106 is a heat stabilized, weather resistant, 40% mineral and glass fiber reinforced PA6 injection molding compound with improved UV resistance and sink mark resistance. The com..
|
|||