- Polymer Property : Tensile Strength at Break = 8410 psi
Polymer Property : Tensile Strength at Break = 8410 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 58.0 MPa | 8410 psi | ISO.527 DIN.53455 |
|
Omnia Plastica Akulon® PA 66.6 - Akulon GX - at 50% RH
Copolymer of nylon with excellent mechanical features, it combines the good impact resistances of PA6 as well as the higher stiffness of PA66. For this reason it machines very well on automatic tool..
|
|||
| Tensile Strength at Break | 58.0 MPa | 8410 psi | Type I, 50 mm/min; ASTM D638 |
|
SABIC Innovative Plastics Lexan® EXL1132 PC Copolymer
Lexan* EXL1132 polycarbonate (PC) siloxane copolymer resin is a high flow, UV stabilized injection molding grade. This resin offers good low temperature (-20 C) ductility in combination with high fl..
|
|||
| Tensile Strength at Break | 58.0 MPa | 8410 psi | Type I, 50 mm/min; ASTM D638 |
|
SABIC Innovative Plastics Lexan® EXL1810T PC Copolymer
Lexan* EXL1810T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers cold temperature (0 °C) ductility in combination with very high flow char..
|
|||
| Tensile Strength at Break | 58.0 MPa | 8410 psi | Type I, 50 mm/min; ASTM D 638 |
|
SABIC Innovative Plastics Lexan® HPX8R PC Copolymer (Europe-Africa-Middle East)
Very high flow specialty polycarbonate with outstanding processability and ductility. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 o..
|
|||
| Tensile Strength at Break | 58.0 MPa | 8410 psi | 50 mm/min; ISO 527 |
|
SABIC Innovative Plastics Lexan® LUX9610 PC (Asia Pacific)
Lexan LUX9610 is a flame retardant transparent polycarbonate featuring non brominated and non chlorinated FR system with good flow and thin wall FR performance. It intended to meet WEEE/RoHS require..
|
|||
| Tensile Strength at Break | 58.0 MPa | 8410 psi | 50 mm/min; ISO 527 |
|
SABIC Innovative Plastics Lexan® ML6413 PC (Asia Pacific)
Lexan* ML6413 resin is an impact modified, flame retardant polycarbonate grade with Br- & Cl-free FR systems. It features improved light shielding capability with good flow, impact and thermal prope..
|
|||
| Tensile Strength at Break | 58.0 MPa | 8410 psi | STN EN ISO 527-2 |
|
Plastcom SLOVAMID 6 HI Polyamide 6, Impacted
FeaturesPA 6 with the content of thermoplastic elastomer. Impacted, for mouldings with high toughness either at low temperatures, suitable for external use, eg. ski shoes, sports and safety helmets..
|
|||
| Tensile Strength at Break | 58.0 MPa | 8410 psi | Type I, 50 mm/min; ASTM D638 |
|
SABIC Innovative Plastics Cycoloy® CX2244ME PC+ABS (Asia Pacific)
Cycoloy* CX2244ME resin is a flame retardant PC/ABS blend featuring excellent balance of flow and impact together with UL-94 V0 rating at < 1mm. Cycoloy CX2244ME resin also demonstrates improved che..
|
|||
| Tensile Strength at Break | 58.0 MPa | 8410 psi | Type I, 50 mm/min; ASTM D 638 |
|
SABIC Innovative Plastics Lexan® EXL1860T PC Copolymer
Lexan* EXL1860T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers improved release performance, cold temperature (0 °C) ductility in combi..
|
|||
| Tensile Strength at Break | 58.0 MPa | 8410 psi | 50 mm/min; ISO 527 |
|
SABIC Innovative Plastics Lexan® EXL8414 PC Copolymer (Asia Pacific)
Lexan* EXL8414 is a PC/siloxane copolymer resin with medium flow, excellent low temperature impact and 25% post consumer recycle content. Limited availability and restricted color only. Higher color..
|
|||
| Tensile Strength at Break | 58.0 MPa | 8410 psi | Type I, 50 mm/min; ASTM D638 |
|
SABIC Innovative Plastics Lexan® EXL9330S PC Copolymer (Asia Pacific)
Opaque PC-Siloxane copolymer with excellent processability. UV stabilized. UL rated V-0/5VA/CTI-PLC-2. Available in limited colors.
|
|||
| Tensile Strength at Break | 58.0 MPa | 8410 psi | 50 mm/min; ISO 527 |
|
SABIC Innovative Plastics Lexan® FXD1413T PC Copolymer
Clear PC-siloxane copolymer with excellent processability, in special light diffusion colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may af..
|
|||
| Tensile Strength at Break | 58.0 MPa | 8410 psi | 5 mm/min; ISO 527 |
|
SABIC Innovative Plastics LNP Colorcomp DX98735 PC
LNP COLORCOMP* DX98735 is a compound based on Polycarbonate resin containing Proprietary Fillers.This data was supplied by SABIC-IP for the Americas region.
|
|||
| Tensile Strength at Break | 58.0 MPa | 8410 psi | 5 mm/min; ISO 527 |
|
SABIC Innovative Plastics LNP COLORCOMP DX98735H PC
LNP* COLORCOMP* DX98735H is an unfilled Polycarbonate resin. Added feature of this grade is: Healthcare.
|
|||
| Tensile Strength at Break | 58.0 MPa | 8410 psi | 50mm/min; ASTM D638 |
|
Kingfa PC-S609 Toughened PC
Features:Good mechanical propertiesSuper high impact strengthGood weather resistanceHigh glossGood processing propertiesStress cracking propertiesApplications:OA and IT partsAutomobile accessoriesEl..
|
|||
| Tensile Strength at Break | 58.0 MPa | 8410 psi | 50 mm/min; ISO 527 |
|
SABIC Innovative Plastics Valox® FXV310SK PBT (Europe-Africa-Middle East)
LIMITED USE, No New Customers / Applications as of Jan. 2010: VALOX FXV310SK is an unreinforced PBT injection moulding resin with high flow characteristics and containing a metal sparkle Visual FX. ..
|
|||
| Tensile Strength at Break | 58.0 MPa | 8410 psi | Type I, 50 mm/min; ASTM D 638 |
|
SABIC Innovative Plastics Xenoy® 1101 PBT+PC (Asia Pacific)
Unreinforced, opaque polycarbonate/polyester alloy. Excellent low temperature impact plus chemical resistance to automotive fluid.This data was supplied by SABIC-IP for the Asia Pacific region.
|
|||
| Tensile Strength at Break | 58.0 MPa | 8410 psi | 50 mm/min; ISO 527 |
|
SABIC Innovative Plastics Xenoy® 1731 PBT+PC
Impact/chemical resistant. UV-Stabilized. Excellent physical property retention in automotive exteriors and OVAD.
|
|||
| Tensile Strength at Break | 58.0 MPa | 8410 psi | Type I, 50 mm/min; ASTM D 638 |
|
SABIC Innovative Plastics Xenoy® 5220 PBT+PC (Asia Pacific)
Unreinforced, polycarbonate-based polymer blend, excellent chemical resistance and impact.This data was supplied by SABIC-IP for the Asia Pacific region.
|
|||
| Tensile Strength at Break | 58.0 MPa | 8410 psi | Type I, 50 mm/min; ASTM D638 |
|
SABIC Innovative Plastics Xenoy® X4820 PBT+PC (Asia Pacific)
Xenoy X4820 is a high modulus PC/PBT Blend. This resin provides high chemical resistance, excellent impact, very low creep, low CTE, excellent fatigue and dimensional stability.
|
|||
| Tensile Strength at Break | 58.0 MPa | 8410 psi | 50mm/min; ISO 527 |
|
Teijin Multilon DN-3520F Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy
Halogen-free flame retardant PC/ABS polymer alloy, and is also antimony-free. It has improved stiffness through the addition of 20 % filler. Improved stiffness and high flowability realizes a thin w..
|
|||
| Tensile Strength at Break | 58.0 MPa | 8410 psi | 5 mm/min; ISO 527 |
|
SABIC Innovative Plastics LNP THERMOCOMP Lexan_JK2000 PC+ABS
LNP* Thermocomp* Lexan_JK2000 compound is a 22% GR, ECO-compliant FR, PC+ABS for thinwall molding applications.
|
|||
| Tensile Strength at Break | 58.0 MPa | 8410 psi | ASTM D 638 |
|
SABIC Innovative Plastics LNP Thermocomp WFB51 PBT
LNP THERMOCOMP* WFB51 is a compound based on Polybutylene Terephalate resin containing Glass Bead, Glass Fiber. Added features of this material include: Low Warpage.This data was supplied by SABIC-..
|
|||
| Tensile Strength at Break | 58.0 MPa | 8410 psi | Type I, 5 mm/min; ASTM D 638 |
|
SABIC Innovative Plastics Noryl PPX PPX615 PPE+PP (Asia Pacific)
Good chemical resistance. Designed for a balance of stiffness and practical impact strength.This data was supplied by SABIC-IP for the Asia Pacific region.
|
|||
| Tensile Strength at Break | 58.0 MPa | 8410 psi | Type I, 5 mm/min; ASTM D 638 |
|
SABIC Innovative Plastics Noryl PPX PPX615 PPE+PP (Europe-Africa-Middle East)
Good chemical resistance. Designed for a balance of stiffness and practical impact strength.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
|
|||
| Tensile Strength at Break | 58.0 MPa | 8410 psi | 50 mm/min; ISO 527 |
|
SABIC Innovative Plastics Noryl FXN2090H PPE+HIPS
Noryl* FXN2090H resin is an unfilled, injection moldable grade. Designed for exceptionally high gloss and improved pencil hardness vs. standard Noryl grades, FXN2090H resin uses non-halogenated FR a..
|
|||
| Tensile Strength at Break | 58.0 MPa | 8410 psi | ASTM D638 |
|
A. Schulman POLYFORT™ FXP 6630 Nylon 6.6 Polypropylene Alloy
DescriptionPolyfort® FXP 6630 is a nylon 6.6 / polypropylene alloy with 30% wollastonite.Information provided by A. Schulman.
|
|||
| Tensile Strength at Break | 58.0 MPa | 8410 psi | ASTM D638 |
|
A. Schulman POLYFORT™ FXP 6630 Nylon 6.6 Polypropylene Alloy
DescriptionPolyfort® FXP 6630 is a nylon 6.6 / polypropylene alloy with 30% wollastonite.Information provided by A. Schulman.
|
|||
| Tensile Strength at Break | 58.0 MPa | 8410 psi | 5 mm/min; ISO 527 |
|
CP-Polymer-Technik Wellamid® 6600 GS 30 HWCP 30% Glass Sphere Filled Nylon 66, Heat Stabilized, Conditioned
Information provided by CP-Polymer-Technik GmbH & Co. KG
|
|||
Copyright © lookpolymers.com All Rights Reserved