Polymer Property : Tensile Strength at Break = 85.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	85.0 MPa	12300 psi	STN EN ISO 527-2
Plastcom PLASTAMID® 66 BT B 27 TS PA66 heat stabilized Basic type PA66 for injection molding, heat stabilized, modified for general use, with excellent manufacturing properties. Use: automotive, engineering, electrical and consumer-goods industry - elec..
Tensile Strength at Break	85.0 MPa	12300 psi
Plastcom SLOVAMID 6 FRC 1 PA6 with flame retardant Features: Determined for electrotechnical use. Delivered in natural mode. PA 6 for injection moulding with reduced flammability, with nonhalogen flame retardant. Excellent fluidity of the material p..
Tensile Strength at Break	85.0 MPa	12300 psi	ISO 527
Nilit FRIANYL B63 K Nylon 6 for injection molding Nylon 6 for injection molding, specially formulated for knobs.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Tensile Strength at Break	85.0 MPa	12300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP COLORCOMP EX12304C PEI (Asia Pacific) LNP* Colorcomp* EX12304C is an unfilled polyetherimide clean compound with extremely high level of cleanliness for the most demanding application. This compound is manufactured using LNP CCS technol..
Tensile Strength at Break	85.0 MPa	12300 psi
Plastcom SLOVAMID 6 GF 5 PA6, 5% glass fibre FeaturesPA 6 for injection moulding, chemically strengthened with 5% glass fibre. Application: impacted mouldings and mouldings with high strength applied in automotive, electrical, engineering and ..
Tensile Strength at Break	85.0 MPa	12300 psi	5 mm/min; ISO 527 - 1/2
Hexion Bakelite™ PF 6507 Phenolic Formaldehyde Resin, Elasticized, Low Shrinkage, Resistant to High Temperatures, High Mechanical Strength Phenolic molding compound, inorganically filled, glass fiber reinforced, elastomer modified, galvanizable, heat resistant, good media resistance, high dimensional stability at raised temperature, hi..
Tensile Strength at Break	85.0 MPa	12300 psi	ISO 527-1,-2
Lanxess DurethanÂ® BKV 215 H3.0 000000 Nylon 6-Copolymer, 15% Glass Fibers PA 6-Copolymer, 15% glass fibers, injection molding, impact modified
Tensile Strength at Break	85.0 MPa	12300 psi	ISO 527-1/-2
Lanxess DurethanÂ® DP 2802/30 000000 Nylon 66, 30% Glass Fiber PA 66 injection molding grade, 30% glass fibers, UL 94V-2 at 0.75 mm , GWFI:960Â°C at 0.75 mm, GWIT: 775Â°C at 0,75 mm, halogen-freeApplication Examples: mixer insert for blenders, washing machi..
Tensile Strength at Break	85.0 MPa	12300 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP EL003 PEI (Europe-Africa-Middle East) LNP LUBRICOMP* EL003 is a compound based on Polyetherimide resin containing PTFE. Added features of this material include: Internally Lubricated.
Tensile Strength at Break	85.0 MPa	12300 psi	ISO 527 Type 1A
Solvay TECHNYLÂ® C 216 PA6, DRY Description: Unreinforced polyamide PA6, standard nucleation for fast cycling, for injection molding.Available in: Asia PacificProduct Applications: This grade has a high fluidity and good mould rel..
Tensile Strength at Break	85.0 MPa	12300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics Ultem 1000FV PEI Transparent, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing; color dependant, see UL Yellow Card. US FDA and EU Food Contact Compliant, NSF 51 Listing.This data wa..
Tensile Strength at Break	85.0 MPa	12300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics Ultem 1010KM PEI (Asia Pacific) Enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Strength at Break	85.0 MPa	12300 psi	50 mm/min; ISO 527
SABIC Innovative Plastics ULTEM 1010M PEI (Europe-Africa-Middle East) Enhanced flow Polyetherimide (Tg 217C) with internal mold release. Resin is RoHS compliant.
Tensile Strength at Break	85.0 MPa	12300 psi	50 mm/min; ISO 527
SABIC Innovative Plastics Ultem 1100R PEI (Europe-Africa-Middle East) Standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Tensile Strength at Break	85.0 MPa	12300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics ULTEM 1100V PEI Transparent, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 VO and 5VA listing; color dependant, see UL Yellow Card.
Tensile Strength at Break	85.0 MPa	12300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics ULTEM CRS5011R PEI Enhanced flow Polyetherimide copolymer (Tg 225C) with internal mold release and enhanced chemical resistance to strong acids, bases, aromatics and ketones. ECO Conforming.
Tensile Strength at Break	85.0 MPa	12300 psi	ISO 527
SABIC Innovative Plastics LNP Thermocomp RFZ349 PA 66 (Asia Pacific) LNP* Thermocomp* RFZ349 is a compound based on Nylon 66 resin containing Glass Fiber, Milled Glass. Added features of this material include: Flame Retardant.This data was supplied by SABIC-IP for t..
Tensile Strength at Break	85.0 MPa	12300 psi	ISO 527
Sumitomo Bakelite North America RXÂ® 613 Fiberglass Reinforced Phenolic RXÂ 613 is a fiberglass reinforced phenolic molding compound with good dimensional stability and good strength at elevated temperatures.Information provided by Sumitomo Bak North America, Inc.
Tensile Strength at Break	85.0 MPa	12300 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP QFL32 PA 6/10 LNP* LUBRICOMP* QFL32 is a compound based on Nylon 6/10 containing 10% Glass Fiber, 15% PTFE. Added features of this grade include: Wear Resistant.
Tensile Strength at Break	85.0 MPa	12300 psi	5 mm/min; ISO 527
SABIC Innovative Plastics ULTEM UF5011S PEI (Europe-Africa-Middle East) Enhanced flow, Specialty filtered Polyetherimide (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics and ketones. ECO Conforming.
Tensile Strength at Break	85.0 MPa	12300 psi	ASTM D638
Sumitomo Bakelite North America XB-22 Fiberglass Reinforced Phenolic Novolac XB-22 is a fiberglass reinforced phenolic novolac molding compound, with excellent dimensional stability and good strength at elevated temperatures. This material is formulated for low thermal condu..
Tensile Strength at Break	85.0 MPa	12300 psi	ISO 527-93
Wellman Wellamid® GFT13-66 XE-NBK1 13% Glass Fiber Reinforced, Impact Modified Nylon 66 Description: Glass Fiber Reinforced, Impact Modified Nylon 66Information provided by Wellman.
Tensile Strength at Break	85.0 MPa	12300 psi	ISO 527-93
Wellman Wellamid® MR409 22H-GY1 Nylon 66, 40% Mineral Reinforced All information provided by Wellman Engineered Resins.
Tensile Strength at Break	85.0 MPa	12300 psi	ISO 527-1/-2
Covestro Makrolon® GF8001* Polycarbonate, 20% Glass Filled ISO 7391-PC,MR,(,,)-18-3,GF20Developmental productFormerly Makrolon DP1-1951MVR (300 °C/1.2 kg) 16 cm3/10 min20 % Glass fiber reinforcedLow viscosityEasy releaseInjection molding - Melt temperature..
Tensile Strength at Break	85.0 MPa	12300 psi	5 mm/min; ISO 527
CP-Polymer-Technik Wellamid® 6600 GV 5 HWCP 5% Glass Fiber Nylon 66, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG
Tensile Strength at Break	85.0 MPa	12300 psi	50%RH; ISO 527-1/-2
DuPont Performance Polymers Zytel® 70K20HSL NC010 Nylon 66  (Unverified Data**) Kevlar® Fiber Reinforced Heat Stabilized Polyamide 66 Zytel 70K20HSL NC010 is a heat stabilized PA66 resin modified with Kevlar aramid fiber for excellent wear resistance.Information provided by Du..
Tensile Strength at Break	85.0 MPa	12300 psi	ISO 527
Eurotec® Tecotek® PC40 GR10 NL PC, 10% glass fiber reinforced, natural Information provided by Eurotec®
Tensile Strength at Break	85.0 MPa <br>@Temperature 80.0 °C	12300 psi <br>@Temperature 176 °F	ASTM Test
BASF Ultramid® 8233G HS BK-106 33% Glass Filled PA6 (Dry) Ultramid 8233G HS BK-106 is a heat stabilized, weather resistant, 33% glass fiber reinforced PA6 injection molding compound offering excellent strength, stiffness, high temperature performance and ..
Tensile Strength at Break	85.0 MPa	12300 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP 2X04505 ETFE LNP* THERMOCOMP* 2X04505 is a compound based on ETFE resin containing Proprietary Filler(s).