Polymer Property : Tensile Strength at Break = 90.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	90.0 MPa	13100 psi	STN EN ISO 527-2
Plastcom SLOVAMID 6 GF 15 T 25 Polyamide 6, 15% Glass Fiber, 25% Micronized Talc FeaturesGood anisotropy of the manufacturing shrinkage. The talc is added to get the material shrinkage identical in both directions. Application for flat products in disc form / no screw after co..
Tensile Strength at Break	90.0 MPa	13100 psi	ISO 527
Nilit FRIANYL B63 W-KF30 Nylon 6 for injection molding, 30% short glass fiber reinforced Nylon 6 for injection molding, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Tensile Strength at Break	<= 90.0 MPa	<= 13100 psi	ISO/R527
Polykemi AB SCANAMID 66 A12^ Q40 Nylon 66, Mineral Reinforced Information provided by Polykemi AB
Tensile Strength at Break	>= 90.0 MPa	>= 13100 psi	50 mm/min; ISO 527-1,2
Qualchem Danamid AFGFLPX0-35 Polyamide 66, 35% Glass Fiber Reinforced with glass fiber, red phosphorous flame retardant, V-0Information provided by Qualchem Zrt.
Tensile Strength at Break	<= 90.0 MPa	<= 13100 psi	ISO/R527
Polykemi AB SCANMID 6 B12^ Q40 Nylon 6, Mineral Reinforced Information provided by Polykemi AB
Tensile Strength at Break	90.0 MPa	13100 psi	ISO 527
Nilit FRIANYL A63 HH Nylon 6.6 for injection molding Nylon 6.6 for injection molding, heat and hydrolysis stabilizedInformation provided by Frisetta Polymer, which merged into Nilit Plastics
Tensile Strength at Break	90.0 MPa	13100 psi	5 mm/min; ISO 527
SABIC Innovative Plastics Lexan® 3412R PC (Europe-Africa-Middle East) LEXAN 3412R is a high viscosity, 20% glass reinforced grade. It offers excellent flame retardancy and is especially designed for applications requiring high rigidity together with high heat.
Tensile Strength at Break	90.0 MPa	13100 psi	ISO 527-1/-2
DSM Akulon® S223-PG2U (Dry) 13% Glass Reinforced, Impact Modified Nylon 66 (North America)  (discontinued **)& Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis..
Tensile Strength at Break	90.0 - 95.0 MPa	13100 - 13800 psi	ASTM D683
Loxim 120 01V0 Polycarbonate, 20% Glass Filled, Flame Retardant Information provided by Loxim Industries
Tensile Strength at Break	90.0 MPa	13100 psi	ASTM D638
Mitsui Arlenâ„¢ C215 15% Glass Fiber-Reinforced Modified Nylon 6T (COND) ARLENâ„¢ is a heat resistant, modified polyamide 6T developed by Mitsui Chemicals, Inc. With a high melting point (320Â°C) and a rigidity level comparable to super engineering plastics, it poss..
Tensile Strength at Break	90.0 MPa	13100 psi	Conditioned; ISO 527-1/-2
Lanxess DurethanÂ® BKV 30 FN00 000000 Nylon 6, 30% Glass Fiber PA6, injection molding grade, 30% glass fibers, UL94 V-0 at 0,75 mm , free of halogen and red phosphorus, glow wire flammability test max. 960Â°C
Tensile Strength at Break	90.0 MPa	13100 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem 1000FV PEI Transparent, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing; color dependant, see UL Yellow Card. US FDA and EU Food Contact Compliant, NSF 51 Listing.This data wa..
Tensile Strength at Break	90.0 MPa	13100 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM 1000RV PEI (Asia Pacific) Standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing; color dependant, see UL Yellow Card.
Tensile Strength at Break	90.0 MPa	13100 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem 1000RV PEI (Europe-Africa-Middle East) Standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing; color dependant, see UL Yellow Card.This data was supplied by SABIC-IP for the Europe-Afr..
Tensile Strength at Break	90.0 MPa	13100 psi	Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Ultem 1000V PEI Transparent, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing; color dependant, see UL Yellow Card. US FDA and EU Food Contact compliant, NSF 51 listing, compliant in ..
Tensile Strength at Break	90.0 MPa	13100 psi	5 mm/min; ISO 527
SABIC Innovative Plastics Ultem 2412EPR PEI (Europe-Africa-Middle East) 40% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing.This data was supplied by SABIC-IP for the Eu..
Tensile Strength at Break	90.0 MPa	13100 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM HU1004 PEI (Asia Pacific) High Temperature, Transparent, Polyetherimide Blend with Improved Ductility and Enhanced Hydrostability. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI) and FDA and EUFC f..
Tensile Strength at Break	90.0 MPa	13100 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP EX06430H PEI LNP* THERMOCOMP* EX06430H is a compound based on Polyetherimide resin containing Proprietary Filler(s). Added feature of this grade is: Healthcare.
Tensile Strength at Break	90.0 MPa	13100 psi	ASTM D638
Sumitomo Bakelite North America EpiallÂ® 1904B-1 Short Glass Fiber Reinforced Epoxy Epiall 1904B-1 is a short fiberglass reinforced epoxy molding compound, with excellent dimensional stability, good strength properties and good electrical insulation properties.Information provided ..
Tensile Strength at Break	90.0 MPa	13100 psi	ISO 527
Vyncolit X689 Novolac Phenolic Glass fiber filled and molybdeendisulfide modified phenolic molding compound with excellent mechanical and thermal properties and lower thermal expansion coefficient. It has excellent friction prop..
Tensile Strength at Break	90.0 MPa	13100 psi	ISO 527-1/-2
Unitika CX-2500 PA6, Dry Transparent nylonInformation provided by Unitika Ltd.
Tensile Strength at Break	90.0 MPa	13100 psi	ASTM D 638
Cossa Polimeri ESTAPROP H 0560 HFC Polypropylene, 30% Glass Filled PP homopolymer 30% chemically coupled glass fiber reinforcedGood stiffness, excellent impact strengthInformation provided by Cossa Polimeri S.r.l.
Tensile Strength at Break	90.0 MPa	13100 psi	5 mm/min; ISO 527
CP-Polymer-Technik Wellamid® 6000/51 GV 30 HWCP 30% Glass Fiber Nylon 6, Low Temperature Impact Modified, Heat Stabilized, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG
Tensile Strength at Break	90.0 MPa	13100 psi	5 mm/min; ISO 527
CP-Polymer-Technik Wellamid® 6600 MF30 HWCP 30% Milled Glass Fiber Nylon 66, Heat Stabilized, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG
Tensile Strength at Break	90.0 MPa	13100 psi	ISO 527
Eurotec® Tecodur® PB70 GR10 NL100 PBT, 10% glass fiber reinforced, natural Information provided by Eurotec®
Tensile Strength at Break	90.0 MPa	13100 psi	Conditioned; ISO R 527
Addiplast Addinyl A2I V25 Flame Retardant Nylon 66, 25% Glass Filled Flame retardant, 25% glass fiber reinforced, halogen freeInformation provided by Addiplast.
Tensile Strength at Break	90.0 MPa	13100 psi	0.2 in/min; ASTM Test
BASF Ultramid® 8202C HS PA6 (Dry) Ultramid 8202C HS is a heat stabilized, low viscosity, PA6 injection molding homopolymer possessing a modified crystalline structure for increased property performance and faster cycles. It is also..
Tensile Strength at Break	90.0 MPa	13100 psi	type I; ASTM D638
BLUESTAR LXS 314 G20 PPE-HIPS, 20% Glass Filled Typical Applications: Water industrial partsInformation provided by Polymer Technology and Services, LLC (PTS).
Tensile Strength at Break	90.0 MPa	13100 psi	5 mm/min; ISO 527
Eurostar Staramide BG3ST43 PA6, 15% Glass Fiber Filled, Impact Modified, Injection Molded BG3ST43 is an Impact Modified and Glass Fiber Reinforced, Polyamide 6 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier.