Polymer Property : Film Tensile Strength at Break, MD = 28000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, MD	193 MPa	28000 psi	ASTM D882A
DuPont Teijin Films Melinex® 453 Polyester Film, 300 Gauge Melinex® 453 is an excellent handling, high clarity film with one side pre-treated to promote adhesion to most printing inks and Industrial coatings.Typical Applications: Melinex® 453 is used as a..
Film Tensile Strength at Break, MD	193 MPa	28000 psi	ASTM D882A
DuPont Teijin Films Melinex® 453 Polyester Film, 700 Gauge Melinex® 453 is an excellent handling, high clarity film with one side pre-treated to promote adhesion to most printing inks and Industrial coatings.Typical Applications: Melinex® 453 is used as a..
Film Tensile Strength at Break, MD	193 MPa	28000 psi	ASTM D882A
DuPont Teijin Films Melinex® 454 Polyester Film, 200 Gauge Melinex® 454 is an excellent handling, high clarity film with both sides pre-treated to promote adhesion to most printing inks and Industrial coatings.Typical Applications: Melinex® 454 is used as..
Film Tensile Strength at Break, MD	193 MPa	28000 psi	ASTM D882A
DuPont Teijin Films Melinex® 455 Polyester Film Melinex® 455 is a high clarity polyester film pretreated on one side for slip. It has excellent handling characteristics.General Product Info: Two smooth coatable surfacesLow surface resistivityCan..
Film Tensile Strength at Break, MD	193 MPa	28000 psi	ASTM D882A
DuPont Teijin Films Melinex® 581 Polyester Film A super clear, one side C-Sub pretreated film for adhesion of hydrophilic coatings.Approvals: UL Recognition - Product has been registered with Underwriters LaboratoriesInformation provided by DuPon..
Film Tensile Strength at Break, MD	193 MPa	28000 psi	ASTM D882A
DuPont Teijin Films Melinex® 582 Polyester Film, 400 Gauge Melinex® 582 is a high clarity polyester film which is two-side hydrophilic pretreated to promote adhesion to many industrial aqueous coating and inks.Approvals: UL Recognition - Product has been r..
Film Tensile Strength at Break, MD	193 MPa	28000 psi	ASTM D882A
DuPont Teijin Films Melinex® 583 Polyester Film, 300 Gauge Melinex® 583 is a high clarity, differentially treated polyester film. One side is hydrophilic pretreated to promote adhesion to many industrial aqueous coatings and inks, and the opposite side is ..
Film Tensile Strength at Break, MD	193 MPa	28000 psi	ASTM D882A
DuPont Teijin Films Melinex® SWC Polyester Film, 48 Gauge A narrow width film with consistently good handling properties; transparent in thin gauges, slightly hazy in thick gauges, ideally suited for wire and cable wrapping and insulation.Information provi..
Film Tensile Strength at Break, MD	193 MPa	28000 psi	ASTM D882A
DuPont Teijin Films Melinex® SWC Polyester Film, 500 Gauge A narrow width film with consistently good handling properties; transparent in thin gauges, slightly hazy in thick gauges, ideally suited for wire and cable wrapping and insulation.Information provi..
Film Tensile Strength at Break, MD	193 MPa	28000 psi	ASTM D882A
DuPont Teijin Films Melinex® SWC Polyester Film, 92 Gauge A narrow width film with consistently good handling properties; transparent in thin gauges, slightly hazy in thick gauges, ideally suited for wire and cable wrapping and insulation.Information provi..
Film Tensile Strength at Break, MD	193 MPa	28000 psi	ASTM D882A
DuPont Teijin Films Mylar® A Polyester Film, 142 Gauge Mylar® A films are tough, general purpose films that are transparent in 48 through 92 gauge and translucent in heavier gauges. They have a rough surface to provide ease of handling, good adhesion, ..
Film Tensile Strength at Break, MD	193 MPa	28000 psi	ASTM D882A
DuPont Teijin Films Mylar® AHS1 Polyester Film, 92 Gauge Mylar® AHS1 is a strong, tough, and durable PET film with an unusual balance of properties. It is used for many industrial and electrical applications. General Product Info: Mylar® ASH1 has a tens..
Film Tensile Strength at Break, MD	193 MPa	28000 psi	ASTM D882A
DuPont Teijin Films Mylar® C Polyester Film, 48 Gauge Mylar® Type C films are available in a wide range of generally thinner gauges (typically 10 through 92) that offer excellent electrical properties, combined with superior strength and dimensional s..
Film Tensile Strength at Break, MD	193 MPa	28000 psi	ASTM D882A
DuPont Teijin Films Mylar® EL Polyester Film, 200 Gauge Mylar® EL films, typically 48 through 500 gauge are strong, tough, general -purpose films for electrical/electronic uses. Heavier gauges of Mylar® EL films are similar to Mylar® MO films. Availab..
Film Tensile Strength at Break, MD	193 MPa	28000 psi	ASTM D882A
DuPont Teijin Films Mylar® EL Polyester Film, 75 Gauge Mylar® EL films, typically 48 through 500 gauge are strong, tough, general -purpose films for electrical/electronic uses. Heavier gauges of Mylar® EL films are similar to Mylar® MO films. Availab..
Film Tensile Strength at Break, MD	193 MPa	28000 psi	ASTM D882A
DuPont Teijin Films Mylar® EL Polyester Film, 92 Gauge Mylar® EL films, typically 48 through 500 gauge are strong, tough, general -purpose films for electrical/electronic uses. Heavier gauges of Mylar® EL films are similar to Mylar® MO films. Availab..
Film Tensile Strength at Break, MD	193 MPa	28000 psi	ASTM D882A
DuPont Teijin Films Mylar® MDA Polyester Film, 75 Gauge Mylar® MDA films are tough, general purpose films that are transparent in 48 through 92 gauge and translucent in heavier gauges. They have a rough surface to provide ease of handling, good adhesion..
Film Tensile Strength at Break, MD	193 MPa	28000 psi	ASTM D882A
DuPont Teijin Films Mylar® RSX951 Polyester Film, 105 Gauge Mylar® RSX951 is a silicone coated polyester film designed for use as a release liner in various casting applications. The silicone release coating is applied to the film during the film production..
Film Tensile Strength at Break, MD	193 MPa	28000 psi	ASTM D882A
DuPont Teijin Films Mylar® RSX951 Polyester Film, 120 Gauge Mylar® RSX951 is a silicone coated polyester film designed for use as a release liner in various casting applications. The silicone release coating is applied to the film during the film production..
Film Tensile Strength at Break, MD	193 MPa	28000 psi	ASTM D882A
DuPont Teijin Films Mylar® RSX951 Polyester Film, 140 Gauge Mylar® RSX951 is a silicone coated polyester film designed for use as a release liner in various casting applications. The silicone release coating is applied to the film during the film production..
Film Tensile Strength at Break, MD	193 MPa	28000 psi	ASTM D882A
DuPont Teijin Films Mylar® RSX951 Polyester Film, 175 Gauge Mylar® RSX951 is a silicone coated polyester film designed for use as a release liner in various casting applications. The silicone release coating is applied to the film during the film production..
Film Tensile Strength at Break, MD	193 MPa	28000 psi	ASTM D882A
DuPont Teijin Films Mylar® RSX951 Polyester Film, 48 Gauge Mylar® RSX951 is a silicone coated polyester film designed for use as a release liner in various casting applications. The silicone release coating is applied to the film during the film production..
Film Tensile Strength at Break, MD	193 MPa	28000 psi	ASTM D882A
DuPont Teijin Films Mylar® RSX951 Polyester Film, 92 Gauge Mylar® RSX951 is a silicone coated polyester film designed for use as a release liner in various casting applications. The silicone release coating is applied to the film during the film production..
Film Tensile Strength at Break, MD	193 MPa	28000 psi	ASTM D882A
DuPont Teijin Films Mylar® WC Polyester Film, 92 Gauge Mylar® WC films are general-purpose electrical grade films, similar to Mylar® EL. These clear to hazy films are tough and durable as a core wrap. They offer good dielectrics and good handling char..
Film Tensile Strength at Break, MD	193 MPa	28000 psi	ASTM D882A
DuPont Teijin Films Mylar® WC11/WC22 Polyester Film, 284 Gauge Mylar® type WC11 films are general-purpose electrical grade films, similar to Mylar® EL. These clear to hazy films are tough and durable as a core wrap. They offer good dielectric and good handlin..
Film Tensile Strength at Break, MD	193 MPa	28000 psi	ASTM D882A
DuPont Teijin Films Melinex® 516 Polyester Film Melinex® 516 is a high clarity polyester film which is pretreated on both sides for slip to combine good handling properties with high clarity and brilliance.Typical Applications: Some typical uses..
Film Tensile Strength at Break, MD	193 MPa	28000 psi	ASTM D882A
DuPont Teijin Films Mylar® MDA Polyester Film, 92 Gauge Mylar® MDA films are tough, general purpose films that are transparent in 48 through 92 gauge and translucent in heavier gauges. They have a rough surface to provide ease of handling, good adhesion..
Film Tensile Strength at Break, MD	193 MPa	28000 psi	ASTM D882A
DuPont Teijin Films Mylar® WC Polyester Film, 142 Gauge Mylar® WC films are general-purpose electrical grade films, similar to Mylar® EL. These clear to hazy films are tough and durable as a core wrap. They offer good dielectrics and good handling char..
Film Tensile Strength at Break, MD	193 MPa	28000 psi	ASTM D882A
DuPont Teijin Films Mylar® MDA Polyester Film, 200 Gauge Mylar® MDA films are tough, general purpose films that are transparent in 48 through 92 gauge and translucent in heavier gauges. They have a rough surface to provide ease of handling, good adhesion..
Film Tensile Strength at Break, MD	193 MPa	28000 psi	ASTM D882A
DuPont Teijin Films Melinex® 454 Polyester Film, 142 Gauge Melinex® 454 is an excellent handling, high clarity film with both sides pre-treated to promote adhesion to most printing inks and Industrial coatings.Typical Applications: Melinex® 454 is used as..