- Polymer Property : Tensile Strength, Yield = 1160 psi
Polymer Property : Tensile Strength, Yield = 1160 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | -20% change after 70 hours @ 125°C; ASTM D412 |
|
Precision Polymer Engineering E60Q Ethylene Propylene Rubber
Peroxide cured, Ethylene Propylene Terpolymer, 60 °IRHD. Terpolymer of ethylene, propylene and diene monomers. Formulated using only those ingredients determined by the United States Federal Food ..
|
|||
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | -20% change after 70 hours @ 100°C; ASTM D412 |
|
Precision Polymer Engineering E80K Ethylene Propylene Rubber
General purpose, peroxide cured, Ethylene Propylene Terpolymer, 75-85 °IRHD. Terpolymer of ethylene, propylene and diene monomers. To meet ASTM D2000/SAE J200 line call-out MCA810, A25, B35, F17...
|
|||
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | -20% change after 70 hours @ 125°C; ASTM D412 |
|
Precision Polymer Engineering E90Q Ethylene Propylene Rubber
Peroxide cured, Ethylene Propylene Terpolymer, 85-95 °IRHD. Terpolymer of ethylene, propylene and diene monomers. Formulated using only those ingredients determined by the United States Federal Fo..
|
|||
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | ASTM D412 |
|
Precision Polymer Engineering H50B Epichlorohydrin
Peroxide Cured, Epichlorohydrin Rubber, 45-55 °IRHD. Terpolymer of epichlorohydrin, ethylene oxide and an unsaturated monomer. ASTM and ISO designation = GECO.Applications: Excellent resistance t..
|
|||
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | ISO 527 |
|
Polimeri Europa Riblene® MY 00 Low Density Polyethylene - Injection Molding
Riblene MY 00 is a very high flowability low density polyethylene resin (LDPE).Main Applications: Riblene MY 00 is suitable for hot melts.Information provided by Polimeri Europa.
|
|||
| Tensile Strength, Yield | >= 8.00 MPa | >= 1160 psi | -20% change after 70 hours @ 100°C; ASTM D412 |
|
Precision Polymer Engineering N70L Nitrile Rubber
Nitrile Butadiene Rubber (NBR), 70 °IRHD. Low- Med acrylonitrile (ACN) content. Copolymer of acrylonitrile and butadiene. To meet: ASTM D2000/SAE J200 line call-out: M5BG710, A14, B14, EO14, EO34..
|
|||
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | -20% change after 70 hours @ 100°C; ASTM D412 |
|
Precision Polymer Engineering N80L Nitrile Rubber
Nitrile Butadiene Rubber, 75-85 °IRHD. Low acrylonitrile (ACN) content. Copolymer of acrylonitrile and butadiene. To meet ASTM D2000 line call-out M6BG814, A14, B14, EO14, EO34, F17.Applications: T..
|
|||
| Tensile Strength, Yield | 8.00 - 12.0 MPa | 1160 - 1740 psi | ±20% change after 70 hours @ 100°C; ASTM D412 |
|
Precision Polymer Engineering N90K Nitrile Rubber
Peroxide cured Nitrile Rubber, 85-95 °IRHD. Copolymer of acrylonitrile and butadiene. ASTM designation = NBR. ISO designation = NBR. ASTM D2000/SAE J200 line call-out M7BG910, B14, EA14, EF11, EF21..
|
|||
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | ASTM D412 |
|
Precision Polymer Engineering S60A Silicone Rubber
Blue Silicone Rubber, 55-65 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. Formulated using only those ingredients determined by the United States Fe..
|
|||
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | ASTM D412 |
|
Precision Polymer Engineering S60Y Silicone Rubber
Yellow Silicone Rubber, 55-65 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. Formulated using only those ingredients determined by the United States ..
|
|||
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | ASTM D412 |
|
Precision Polymer Engineering S60Z Silicone Rubber
Grey Silicone Rubber, 55-65 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. Formulated using only those ingredients determined by the United States Fo..
|
|||
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | ASTM D412 |
|
Precision Polymer Engineering S65R Silicone Rubber
Low Compression Set, Red Silicone Rubber, 61-70 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. Formulated using only those ingredients determined by t..
|
|||
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | ASTM D412 |
|
Precision Polymer Engineering S70T Silicone Rubber
Translucent Silicone Rubber, 66-75 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. ASTM & ISO designation = VMQ.Applications: Excellent heat resistanc..
|
|||
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | ASTM D412 |
|
Precision Polymer Engineering S70Z Silicone Rubber
Grey Silicone Rubber, 66-75 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. Formulated using only those ingredients determined by the United States Fe..
|
|||
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | ASTM D412 |
|
Precision Polymer Engineering S72R Silicone Rubber
Orange Silicone Rubber, 65-75 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. Formulated using only those ingredients determined by the United States ..
|
|||
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | ASTM D412 |
|
Precision Polymer Engineering V75E Fluoroelastomer Compound
Special steam resistant, Green Fluoroelastomer Rubber, 71-80 °IRHD. Copolymer of vinylidene fluoride and hexafluoropropylene. To meet ASTM D2000 line call-out:- M2HK710, A1-10, B38, EF31, EO78, F1..
|
|||
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | 20 in/min, injection molded, type 1 specimen; ASTM D638 |
|
Phillips Sumika Marlex® CHP-010 Thermoplastic Polyolefin
(discontinued **)
Applications: Soft interior trimSoft touch overmoldingInformation provided by Chevron Phillips.Phillips Sumika Polypropylene Company has been shut down, as announced in 2011.
|
|||
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | -20% change after 168 hours @ 125°C; ASTM D412 |
|
Precision Polymer Engineering E50E Ethylene Propylene Rubber
Ethylene Propylene Terpolymer, 46-55 °IRHD. Terpolymer of ethylene, propylene and diene monomers. To meet Aerospace Specification DTD5597A Grade 50.Applications: For sealing applications where goo..
|
|||
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | 500 mm/min (20 in./min.); Type IV Specimen; ASTM D638 |
|
Eastman 812A Polyethylene
(discontinued **)
Polyethylene 812A is a natural low density material with a 200 melt index. This high-flow formulation is used for specialty injection molding applications in the medical market.Unless otherwise not..
|
|||
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | ASTM D638 |
|
Huntsman PE1651 EVA Film Extrusion
(discontinued **)
6.5% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Yields film with outstanding low temperature strength, excellent clarity, and good heat seal.Applications: Film extrusion: ice bags, liqui..
|
|||
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | 50 mm/min; ASTM D638 |
|
ICO Polymers ICOTEXâ„¢ 520-5019 300 Micron LDPE Powder
Description: ICOTEX 520-5019 is a low density polyethylene powder that has been developed to meet the special requirements of the textile coating industry. Key Characteristics: good melt flow and a ..
|
|||
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | 100%; ASTM D412 |
|
Teknor Apex APEX® 3211-80 Polyvinyl Chloride, Flexible
Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMUses-Automotive Applications, Non-specific Food Applications, General Purpose, Medical Applications, Modeling..
|
|||
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | ASTM D412 |
|
Vicone High Performance Rubber VicoSil™ KC605Q-OR High Performance Silicone Rubber
Information provided by Vicone
|
|||
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | ISO 527-2 |
|
Total LDPE 1200 MN 18 C Low Density Polyethylene - Injection Molding and Compounding
LDPE 1200 MN 18 C is a low density polyethylene made by a high pressure autoclave process without antioxidant.Application examples: flexible molding, handles, closures, household items, toys, variou..
|
|||
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | ISO 527-2 |
|
Total LDPE 1700 MN 18 C Low Density Polyethylene - Injection Molding and Compounding
LDPE 1700 MN 18 C is a low density polyethylene made by a high pressure autoclave process without antioxidant. Grade for easy flow injection molding of flexible parts, powder production for grindin..
|
|||
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | |
|
Trelleborg Hypalon® H611 Chlorosulphonated Polyethylene
PropertiesExcellent resistance to oxidation and has outstanding resistance to atmospheric conditions and in particular strong sunlight and ozone.CSM compounds resist fire and are self extinguishing ..
|
|||
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | |
|
Trelleborg Hypalon® H711 Chlorosulphonated Polyethylene
PropertiesExcellent resistance to oxidation and has outstanding resistance to atmospheric conditions and in particular strong sunlight and ozone.CSM compounds resist fire and are self extinguishing ..
|
|||
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | |
|
Trelleborg S650 Silicone Rubber
PropertiesExcellent resistance to heat (dry air), at +200°C continuous and +220°C intermittent.Remains flexible at low temperatures of -70°C.Resistant to ultra-violet light, ozone and weathering...
|
|||
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | |
|
Trelleborg S750 Silicone Rubber
PropertiesExcellent resistance to heat (dry air), at +200°C continuous and +220°C intermittent.Remains flexible at low temperatures of -70°C.Resistant to ultra-violet light, ozone and weathering...
|
|||
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | 50 mm/min |
|
Arkema Group Evatane® 1005 VN 3 Ethylene Vinyl Acetate
EVA copolymer made by high pressure tubular process. Applications Grade for flexible, very transparent film with high strength, shrinking at low temperature. Examples: curtain stretch, coextrusion, ..
|
|||