Polymer Property : Tensile Strength, Yield = 1450 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	10.0 - 20.0 MPa	1450 - 2900 psi	50 mm/min; ISO/R 527
Okulen® 500 - REG PE Multicoloured coarse OKULEN® 500 is a high molecular low pressure polyethylene with a molecular weight of approximately 500 g/mol. Applications include the food industyr and sports center construction. It does an excel..
Tensile Strength, Yield	10.0 MPa	1450 psi	ISO 527
Polimeri Europa Riblene® MP 20 Low Density Polyethylene - Injection Molding Riblene MP 20 is a medium fluidity low density polyethylene resin (LDPE).Parts made by Riblene MP 20 are characterized by a high flexibility.Main Applications: Riblene MP 20 is suitable for injecti..
Tensile Strength, Yield	10.0 MPa	1450 psi	ASTM D412
Precision Polymer Engineering E90K Ethylene Propylene Rubber General purpose, peroxide cured, Ethylene Propylene Terpolymer, 85-95 °IRHD. Terpolymer of ethylene, propylene and diene monomers. ASTM D2000/SAE J200 line call out M8CA910, A25, B35, C32, EA14, ..
Tensile Strength, Yield	10.0 MPa	1450 psi	ASTM D412
Precision Polymer Engineering Q90B Polyurethane Rubber Peroxide cured, Polyurethane Rubber, 85-95 °IRHD. Polyester-based urethane. To meet ASTM line call-out M5BG910, B14, EO14, EO34. ASTM & ISO designation = AU.Applications: Excellent abrasion resis..
Tensile Strength, Yield	10.0 MPa	1450 psi	ASTM D412
Precision Polymer Engineering S65T Silicone Rubber Translucent Silicone Rubber, 55-65 °IRHD. Silicone rubber having both methyl and vinyl substituent groups on the polymer chain. Formulated using only those ingredients determined by the United Sta..
Tensile Strength, Yield	10.0 MPa	1450 psi	ASTM D412
Precision Polymer Engineering V60F Fluoroelastomer Compound Peroxide/Litharge cured, Fluoroelastomer Rubber, 55-65 °IRHD. Tetrapolymer of vinylidene fluoride, hexafluoropropylene and tetrafluoroethylene and cure site monomer (CSM). To meet ASTM D2000 line c..
Tensile Strength, Yield	10.0 MPa	1450 psi	ASTM D412
Precision Polymer Engineering V70A Fluoroelastomer Compound Blue Fluoroelastomer Rubber, 65-75 °IRHD. Copolymer of vinylidene fluoride and hexafluoropropylene. To meet ASTM D2000 line call-out: M2HK710, A1-10, B38, EF31, EO78, F15, Z1, Z2, where Z1 = comp-..
Tensile Strength, Yield	10.0 MPa	1450 psi	ASTM D412
Precision Polymer Engineering V71H Fluoroelastomer Compound Green Fluoroelastomer Rubber, 70-75 °IRHD. Copolymer of vinylidene fluoride and hexafluoropropylene. Formulated using only those ingredients determined by the United States Federal Food and Drug Ad..
Tensile Strength, Yield	10.0 MPa	1450 psi	ASTM D412
Precision Polymer Engineering V75P Fluoroelastomer Compound Purple Fluoroelastomer Rubber, 70-80 °IRHD. Copolymer of vinylidene fluoride and hexafluoropropylene. To meet ASTM D2000 line call-out:- M2HK710, A1-10, B38, EF31, EO78, F15, Z1, Z2. Where Z1 = co..
Tensile Strength, Yield	10.0 MPa	1450 psi	ASTM D412
Precision Polymer Engineering V75Y Fluoroelastomer Compound Yellow Fluoroelastomer Rubber, 70-80 °IRHD. Copolymer of vinylidene fluoride and hexafluoropropylene. To meet ASTM D2000 line call-out:- M2HK710, A1-10, B38, EF31, EO78, F15, Z1, Z2. Where Z1 = co..
Tensile Strength, Yield	10.0 MPa	1450 psi	ASTM D412
Precision Polymer Engineering V80Q Fluoroelastomer Compound Black Fluoroelastomer Rubber, 75-85 °IRHD. Copolymer of vinylidene fluoride and hexafluoropropylene. Formulated using only those ingredients determined by the United States Food and Drug Administr..
Tensile Strength, Yield	10.0 MPa	1450 psi	ASTM D412
Precision Polymer Engineering V85K Fluoroelastomer Compound Fluoroelastomer Rubber, 80-90 °IRHD. Terpolymer of vinylidene fluoride, hexafluoropropylene and tetrafluoroethylene. To meet ASTM D2000 line call-out M3HK910, A1-10, B37, B38, EF31, EO78, Z1. Wher..
Tensile Strength, Yield	10.0 MPa	1450 psi	TPE-0153 (ASTM D 412)
Advanced Elastomer Systems Santoprene® 253-50 Thermoplastic Rubber  (discontinued **) A colorable thermoplastic flame retardant elastomer with good fluid resistance, formulated to replace thermoset elastomers such as EPDM, polychloroprene, and chlorosulfonated polyethylene. It can b..
Tensile Strength, Yield	10.0 MPa	1450 psi	ASTM D638
NOVA Chemicals Sclair® 8111 LLDPE Injection Molding Resin  (discontinued **) Features: Good processability, excellent impact resistance, excellent flexibility and freedom from warpage.Applications: Automotive splash-guards, large containers, closures and lids for food applic..
Tensile Strength, Yield	10.0 MPa	1450 psi	500 mm/min; ASTM D638
Eastman D4027-P Voridian Polyethylene  (discontinued **) VORIDIAN low density polyethylene D4027-P is a formulation suggested for extrusion coating applications that require clarity, high gloss and superior hot tack properties. Applications/UsesFood Packa..
Tensile Strength, Yield	10.0 MPa	1450 psi	500 mm/min (20 in./min.); ASTM D638, Type IV Specimen
Eastman 808A Polyethylene  (discontinued **) Low density polyethylene 808A is a general-purpose formulation used for injection molding and general-purpose extrusion.Unless otherwise noted, all tests are run at 23°C and 50% RH.Information from..
Tensile Strength, Yield	10.0 MPa	1450 psi	ASTM D638
Huntsman PE7018 Profile Extrusion Polyethylene  (discontinued **) Homopolymer and FDA compliant.Features: Excellent strength, good machinability, and foaming characteristics.Applications: Extrusion: profile extrusion.FDA Notes: Conforms to FDA regulation 21 CFR 17..
Tensile Strength, Yield	10.0 MPa	1450 psi	ASTM D638
Braskem BI 818 LDPE Injection Molding Polyethylene  (discontinued **) Applications: Injection molding; masterbatches. Information provided by Braskem
Tensile Strength, Yield	10.0 MPa	1450 psi
LyondellBasell LupolenÂ® 2441 D LDPE, Film Grade FilmData was collected by ISO methods and originally provided by BASF. The LupolenÂ® product line is now produced by Basell.
Tensile Strength, Yield	10.0 MPa	1450 psi
LyondellBasell LupolenÂ® 2452 D SW 413 LDPE Cable sheathingData was collected by ISO methods and originally provided by BASF. The LupolenÂ® product line is now produced by Basell.
Tensile Strength, Yield	10.0 MPa	1450 psi
KratonÂ® D1102 + LDPE blend (4/96) Blending KRATON D and G polymers with PE significantly improves the toughness at both room and low temperatures. KRATON polymers are block segments of styrene and rubber monomers (A-B, A-B-A, or [A..
Tensile Strength, Yield	10.0 MPa	1450 psi	9.8 in/min; ASTM D638
Teknor Apex Sinvicomp SIM 6019 Polyvinyl Chloride, Flexible Availability: Asia Pacific Features: High Strength Uses: Electrical/Electronic Applications < Forms: Pellets Processing Method: Injection MoldingInformation Provided by Teknor Apex
Tensile Strength, Yield	10.0 MPa	1450 psi	2"/min; ASTM D638
A. Schulman CP763-01 Extruded, Blow Molding and Injection Molding Grade Polyethylene DescriptionCP 763-01 is an extruded, blow molding, and injection molding grade of low density polyethylene having good processability and heat sealability. ApplicationCP 763-01 meets the specificat..
Tensile Strength, Yield	10.0 MPa	1450 psi	2"/min; ASTM D638
A. Schulman CP763-01 Extruded, Blow Molding and Injection Molding Grade Polyethylene DescriptionCP 763-01 is an extruded, blow molding, and injection molding grade of low density polyethylene having good processability and heat sealability. ApplicationCP 763-01 meets the specificat..
Tensile Strength, Yield	10.0 MPa	1450 psi
Trelleborg Neoprene® C738 Chloroprene CR or Chloroprene is a homopolymer of chloroprene or chlorobutadiene. NEOPRENE®PropertiesExcellent mechanical and abrasion properties even without reinforcing fillers.Reasonable resilience in grade..
Tensile Strength, Yield	10.0 MPa	1450 psi
Trelleborg R449 Natural Rubber Polyisoprene All information provided by Trelleborg
Tensile Strength, Yield	10.0 MPa	1450 psi	At 50 mm/min; ISO 527-2
Borealis Daplen™ AK4504 TPO Compound Daplen AK4504 is a 30% mineral and elastomer modified polypropylene compound intended for injection molding. Daplen AK4504 is a material with excellent impact/stiffness ratio. Thanks to its low th..
Tensile Strength, Yield	10.0 MPa	1450 psi	ASTM D638
Huntsman PE1061 Film Extrusion Polyethylene  (discontinued **) Homopolymer and FDA compliant.Features: Exceptional strength, good machinability and heat seal characteristics.Applications: Film extrusion: high clarity packaging, frozen food, produce bags, shrink..
Tensile Strength, Yield	10.0 MPa	1450 psi	ASTM-D638
Polyram RamOfin PPC370B73 Polypropylene, 73% Mineral Filled 73% mineral filled polypropylene for heavy density injection molding applicationsInformation provided by Polyram Ram On Ind.
Tensile Strength, Yield	10.0 MPa	1450 psi	ASTM D638
Huntsman PE8010 Specialty Polyethylene  (discontinued **) Homopolymer and FDA compliant.Features: Yields film with excellent draw down and machinability.Applications: Film extrusion: gel free film applications.FDA Notes: Conforms to FDA regulation 21 CFR 1..