Polymer Property : Tensile Strength, Yield = 16500 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 114 MPa | 16500 psi | ASTM D638 |
|
Polymer Resources PEI-G10 Polyetherimide, 10% Glass Reinforced
Polyetherimide, 10% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Poly..
|
|||
| Tensile Strength, Yield | 114 MPa | 16500 psi | ASTM D638 |
|
Polymer Resources TP-FRG30 Polybutylene Terephthalate, 30% Glass Reinforced, Flame Retardant
Polybutylene Terephthalate, 30% Glass Reinforced, Flame RetardantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples..
|
|||
| Tensile Strength, Yield | 114 MPa | 16500 psi | ASTM D638 |
|
Polymer Resources TPSF-FRG30 Polybutylene Terephthalate, Structural Foam, 30% Glass Reinforced, Flame Retardant
Polybutylene Terephthalate, Structural Foam, 30% Glass Reinforced, Flame RetardantProcess: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, ..
|
|||
| Tensile Strength, Yield | 114 MPa | 16500 psi | ISO 527 |
|
SABIC Innovative Plastics LNP LUBRICOMP DFL36ELH PC
LNP* Lubricomp* DFL36ELH is a compound based on Polycarbonate resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated, Low Extractible, Easy Moldi..
|
|||
| Tensile Strength, Yield | 114 MPa | 16500 psi | ISO 527 |
|
SABIC Innovative Plastics LNP LUBRICOMP DFL36XXJ PC
LNP* Lubricomp* DFL36XXJ is a compound based on Polycarbonate resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated, Low Extractable, Healthcare..
|
|||
| Tensile Strength, Yield | 114 MPa | 16500 psi | ASTM D638 |
|
Polymer Resources PPX/NY G20 Modified PPO, 20% Glass Reinforced PPX/Nylon 6,6 Alloy
(Unverified Data**)&l
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
|
|||
| Tensile Strength, Yield | 114 MPa | 16500 psi | ISO 527 |
|
SABIC Innovative Plastics LNP LUBRICOMP DFL36ELH PC (Asia Pacific)
LNP* Lubricomp* DFL36ELH is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Low Extractible.
|
|||
| Tensile Strength, Yield | 114 MPa | 16500 psi | 5 mm/min; ISO 527 |
|
SABIC Innovative Plastics Noryl PX7446 PPE+PS
This data was supplied by SABIC-IP for the Americas region.
|
|||
| Tensile Strength, Yield | 114 MPa | 16500 psi | Type I, 5 mm/min; ASTM D638 |
|
SABIC Innovative Plastics ULTEM 2100 PEI
10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. NSF 51 listing, WRAS certification in recognized colors.
|
|||
| Tensile Strength, Yield | 114 MPa | 16500 psi | Type I, 5 mm/min; ASTM D638 |
|
SABIC Innovative Plastics ULTEM 2100 PEI (Asia Pacific)
10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. NSF 51 listing, WRAS certification in recognized colors.
|
|||
| Tensile Strength, Yield | 114 MPa | 16500 psi | Type I, 5 mm/min; ASTM D638 |
|
SABIC Innovative Plastics ULTEM 2100F PEI
10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. US FDA and EU Food Contact Compliant, NSF 51 listing. WRAS certification in recognized col..
|
|||
| Tensile Strength, Yield | 114 MPa | 16500 psi | Type I, 5 mm/min; ASTM D638 |
|
SABIC Innovative Plastics ULTEM 2100F PEI (Asia Pacific)
10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. US FDA and EU Food Contact Compliant, NSF 51 listing, WRAS certification in recognized colors..
|
|||
| Tensile Strength, Yield | 114 MPa | 16500 psi | Type I, 5 mm/min; ASTM D 638 |
|
SABIC Innovative Plastics Ultem 2100N PEI (Asia Pacific)
10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacific region.
|
|||
| Tensile Strength, Yield | 114 MPa | 16500 psi | Type I, 5 mm/min; ASTM D638 |
|
SABIC Innovative Plastics ULTEM 2100R PEI (Asia Pacific)
10% Glass fiber filled, standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.
|
|||
| Tensile Strength, Yield | 114 MPa | 16500 psi | 5 mm/min; ISO 527 |
|
SABIC Innovative Plastics LNP LUBRICOMP WFL34 PBT
LNP LUBRICOMP* WFL34 is a compound based on PBT resin containing 20% Glass Fiber, 15% PTFE. Added feature of this grade is: Wear Resistant.
|
|||
| Tensile Strength, Yield | 114 MPa | 16500 psi | Type I, 5 mm/min; ASTM D638 |
|
SABIC Innovative Plastics ULTEM HU2100 PEI (Asia Pacific)
10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). US FDA and European Food Contact approved. For medical devices and pharmaceutical applications.Healthcare management of change, biocom..
|
|||
| Tensile Strength, Yield | 114 MPa | 16500 psi | Type I, 5 mm/min; ASTM D638 |
|
SABIC Innovative Plastics ULTEM HU2100 PEI (Europe-Africa-Middle East)
10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). US FDA and European Food Contact approved. For medical devices and pharmaceutical applications.Healthcare management of change, biocom..
|
|||
| Tensile Strength, Yield | 114 MPa | 16500 psi | Type I, 5 mm/min; ASTM D638 |
|
SABIC Innovative Plastics ULTEM HU2110 PEI
10% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP ..
|
|||
| Tensile Strength, Yield | 114 MPa | 16500 psi | Type I, 5 mm/min; ASTM D638 |
|
SABIC Innovative Plastics Valox® IQ420 PBT (Asia Pacific)
Environmentally responsible Valox iQ420 resin: iQ-PBT+ 30% glass fiber reinforcement. Targeted for use in electrical motors, connectors, pump housings, spotlights, appliance handles, etc.
|
|||
| Tensile Strength, Yield | 114 MPa | 16500 psi | Type I, 5 mm/min; ASTM D638 |
|
SABIC Innovative Plastics Valox® IQ420HP PBT (Asia Pacific)
Environmentally responsible, low carbon footprint Valox iQ* resin - Valox* iQ420HP resin is made using iQ-PBT resin and 30% glass fiber reinforcement. Valox* iQ420HP may be used for the production..
|
|||
| Tensile Strength, Yield | 114 MPa | 16500 psi | ASTM D638 |
|
Techmer ES HiFill® PC GF30 X 30% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightInformation provided by TP Composites, Inc.
|
|||
| Tensile Strength, Yield | 114 MPa | 16500 psi | ASTM D638 |
|
Techmer ES HiFill® PET GF20 UV BK 20% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 20% Filler by WeightAdditive: UV StabilizerAppearance: BlackInformation provided by TP Composites, Inc.
|
|||
| Tensile Strength, Yield | 114 MPa | 16500 psi | Type I, 5 mm/min; ASTM D 638 |
|
SABIC Innovative Plastics Ultem 2110N PEI (Asia Pacific)
10% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacific region.
|
|||
| Tensile Strength, Yield | 114 MPa | 16500 psi | ASTM D638 |
|
SABIC Innovative Plastics LNP STAT-KON DEL339XF PC (Asia Pacific)
LNP* Stat-kon* DEL339XF is a compound based on Polycarbonate resin containing PTFE, Flame Retardant, Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant,..
|
|||
| Tensile Strength, Yield | 114 MPa | 16500 psi | Type I, 5 mm/min; ASTM D638 |
|
SABIC Innovative Plastics Valox® IQ420HP PBT
Environmentally responsible, low carbon footprint Valox iQ* resin - Valox* iQ420HP resin is made using iQ-PBT resin and 30% glass fiber reinforcement. Valox* iQ420HP may be used for the production..
|
|||
| Tensile Strength, Yield | 114 MPa | 16500 psi | chs 2.0 in/min; ASTM D638 |
|
Diamond Polymers DIAMALOY FR530 PC/PBT Alloy, 30% Glass Filled Flame Retardant
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
|
|||
| Tensile Strength, Yield | 114 MPa | 16500 psi | ASTM D638 |
|
Ascend Performance Materials VYDYNE® R400G Nylon, Mineral and Glass Reinforced
Typical property data. VYDYNE is a registered trademark of Solutia Inc.
|
|||
| Tensile Strength, Yield | 114 MPa | 16500 psi | ASTM D638 |
|
Polymer Resources PEI-G10 Polyetherimide, 10% Glass Reinforced
(Unverified Data**)
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
|
|||
| Tensile Strength, Yield | 114 MPa | 16500 psi | Type I, 5 mm/min; ASTM D 638 |
|
SABIC Innovative Plastics Ultem 2110N PEI
10% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Americas region.
|
|||
| Tensile Strength, Yield | 114 MPa | 16500 psi | ASTM D638 |
|
Techmer ES HiFill® PP LGF40 CC HS BK 40% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 40% Filler by WeightAdditive: Heat StabilizerFeatures: Chemically Coupled and Heat StabilizedAppearance: Bla..
|
|||