Polymer Property : Tensile Strength, Yield = 1700 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D412
Polymax® Maxelast® P3885M TPE, PP Overmold or Standalone use Polymax's TPE material complies with UL, VDE, FDA, RoHS and PAH's standards.Uses:Consumer ProductsToys & NoveltiesAuto PartsTool Hand GripsSporting GoodsWire & Cable ElectronicsMedical DevicesPlasti..
Tensile Strength, Yield	11.7 MPa	1700 psi	-10% change after 70 hours @ 100°C; ASTM D412
Precision Polymer Engineering N60W Nitrile Rubber White Nitrile Butadiene Rubber (NBR), 55-65 °IRHD. Copolymer of acrylonitrile and butadiene. Formulated using only those ingredients determined by the United States Food and Drug Administration (F..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D638
M. Holland Company LD800 LDPE  (discontinued **) Features: High Clarity, High Flow, Narrow Molecular Wt. Dist., Good Processability, Warp ResistantUses: Closure Caps, Drink LidsApprovals: FDA 21 CFR 177.1520(c) 2.2 and ASTM D 1248, I, Class A, Cat..
Tensile Strength, Yield	11.7 MPa	1700 psi	ISO 1184-1983E
LyondellBasell Montell 8340 Polybutene-1 Key Features: semi-crystalline low ethylene content random copolymer, miscible with polypropylenes, FDA acceptableApplications: minor additive in a polyethylene peel seal layerMeets FDA requirements..
Tensile Strength, Yield	11.7 MPa	1700 psi	ISO 1184-1983E
LyondellBasell Montell 8640 Polybutene-1 Key Features: semi-crystalline low ethylene content random copolymer, miscible with polypropylenes, FDA acceptableApplications: minor additive in a polyethylene peel seal layerMeets FDA requirements..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D638
LyondellBasell PetrotheneÂ® GA808091 Linear Low Density Polyethylene ApplicationsPETROTHENE GA 808-091 is a broad molecular weight, linear low density polyethylene resin designed for use as a base resin in wire and cable jacketing. An antioxidant package is added to..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D638
LyondellBasell PetrotheneÂ® GA808093 Linear Low Density Polyethylene ApplicationsPETROTHENE GA 808-093 is a broad molecular weight, linear low density polyethylene resin designed for use as a wire and cable insulation. An antioxidant package is added to ensure therm..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D638
Micropol E332 Rotational molding powder based on a random EVA copolymer Information provided by Micropol Limited
Tensile Strength, Yield	11.7 MPa	1700 psi	Elastic; ASTM D412
Multibase Multi-FlexÂ® G 7715 TPE Styrene Ethylene Butylene Styrene Block Copolymer Forms: PelletsProcessing Methods:Injection Molding Information provided by Multibase
Tensile Strength, Yield	11.7 MPa	1700 psi	@100% Elongation; ASTM D1414
Greene Tweed FLUORAZÂ® 890 Fluoroelastomer, FEPM Sanitary gaskets made from FluorazÂ® 890 are ideal for use in standard SIP and CIP applications where EPDMs and FKMs fail. While EDPMs and FKMs can provide a deal for extended periods, changes in..
Tensile Strength, Yield	11.7 MPa	1700 psi	Elastic; ASTM D412
Multibase Multi-FlexÂ® A 9002 Black TPE Thermoplastic Elastomer Forms: PelletsProcessing Methods:Injection Molding Information provided by Multibase
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D412
Teknor Apex APEXÂ® 3201-65 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMUses-Automotive Applications, Non-specific Food Applications, General Purpose, Medical Applications, Modeling..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D412
Teknor Apex APEXÂ® 3302-60 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTM Uses- Medical Applications, Tubing, Appearance-ClearForms-PelletsProcessing-ExtrusionInformation provided by..
Tensile Strength, Yield	11.7 MPa	1700 psi	Longitudinal
Saint-Gobain NortonÂ® FluorglasÂ® ChemfilmÂ® R167 Extruded Expanded PTFE Film (0.010" thick) Description: Expanded Unsintered Films are used in microwave and coaxial cable applications in which low dielectric constant and high velocities are required. R167-nominal density of 0.7 g/cc. R165-..
Tensile Strength, Yield	11.7 MPa	1700 psi
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 10 PHR Iceberg Clay Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	11.7 MPa	1700 psi
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 120 PHR Atomite Whiting Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	11.7 MPa	1700 psi	50 mm/min cross speed, ASTM D638
DuPont™ Surlyn® 9721 Ionomer Resin, Zinc Surlyn® 9721 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. The amount of MAA and neutr..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D638
ExxonMobil LDPE LD 101BA Wire & Cable Low Density Polyethylene Resin Product Description: LD 101BA Wire & Cable is anon-stabilized LDPE, designed for the production of Medium/High Voltage insulation using the direct peroxide addition. For cleanliness reasons, the mat..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D638
ExxonMobil LDPE LD 419.MV Low Density Polyethylene Resin Product Description: LD 419.MV is a LDPE designed for wire and cable applications and is suitable for making crosslinkable compounds for medium voltage insulation.Availability: Latin America, North ..
Tensile Strength, Yield	11.72 MPa	1700 psi	ASTM D638
ExxonMobil LL 6100.17 Injection Molding Resin Product Description: LL 6100 is a narrow molecular weight butane copolymer designed for applications that require easy processability. This resin offers outstanding toughness and tear resistance in ..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D638
ExxonMobil LL 6201.19 Injection Molding Resin Product Description: LL 6201 is a narrow molecular weight butane copolymer designed for applications that require excellent toughness. This resin offers easy processability for applications that req..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D638
ExxonMobil LLDPE LL 1002YB Wire & Cable Linear Low Density Polyethylene Resin Product Description: LL 1002YB is a C4 Ziegler Natta LLDPE for Low Voltage power cable and Telecom jacketing. The grade contains a higher level of antioxidants and has excellent Environmental Stress..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D638
ExxonMobil LLDPE LL 1004YB Wire & Cable Linear Low Density Polyethylene Resin (European Grade) Product Description: LL 1004YB is a C4 Ziegler Natta LLDPE, especially designed for Low Voltage power cable insulation, using the two-step silane cross-linking process. The grade contains a higher l..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D638
Entec Hypel® PELD50/.924 LDPE Available in North America Features: Food Contact Acceptable and Low DensityAgency Ratings: FDA 21 CFR 176.170, Table 2, Cond. B; Cond. C; Cond. D; Cond. E; Cond. F; Cond. G; Cond. H; and FDA 21 CF..
Tensile Strength, Yield	11.7 MPa	1700 psi	Molded and tested in accordance with ASTM D4976; ASTM D638
Dow DNDA-7144 NT 7 Linear Low Density Polyethylene Resin DOW DNDA-7144 NT 7 is produced using UNIPOL™ PE process technology. It is intended for use in injection molding applications such as large industrial containers and trash cans. Information provide..
Tensile Strength, Yield	11.7 MPa	1700 psi	Molded and tested in accordance with ASTM D4976; ASTM D638
Dow GRSN-9820 NT 7 Linear Low Density Polyethylene Granular Solid DOW GRSN-9820 NT 7 is produced using UNIPOL™ PE process technology and is supplied in granular form. This resin is specifically designed as a carrier resin for color concentrates and other master ..
Tensile Strength, Yield	11.7 MPa	1700 psi	2 in/min (50 mm/min); ASTM D638
Bapolene® 1072 Polyethylene, Injection Grade A high flow general purpose injection molding resin with good gloss, toughness and stress crack resistance. This product meets FDA standards for food contact applications.Applications: Housewares, ..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D-638
Axiall 2134N Moldings & Extrusions Flexible PVC 105C plug molding compound. UL recognized component for 94 V-2 in all colors (0.75 mm min. thickness) and 94 V-0 in black and white (1.5 mm min. thickness). UL QMFZ2 recognized component.Informati..
Tensile Strength, Yield	11.7 - 19.3 MPa	1700 - 2800 psi	ASTM D638
Arkema Group Kynar Super Flex® 2500 PVDF Copolymer  (discontinued **) Copolymer Series, Kynar® components are used extensively in the high purity semiconductor market, the pulp and paper industry, nuclear waste processing, and the general chemical processing industry..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D-638
Axiall 46234A Moldings & Extrusions Flexible PVC Automotive window encapsulation compound.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.