Polymer Property : Tensile Modulus = 508 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Tensile Modulus	3.50 GPa	508 ksi
Plastcom SLOVAMID 66 OB PA66, optically brightened FeaturesPA 66 for injection moulding, optical brightened, for mouldings with high surface brightness, with increased toughness and modulus of elasticity in tension in comparison with the basic type...
Tensile Modulus	3.50 GPa	508 ksi	5 mm/min; ASTM D638
SABIC Innovative Plastics Cycoloy® CM6140 PC+ABS (Europe-Africa-Middle East) Cycoloy resin grade CM6140 is a flame retardant, filled PC/ABS blend. It is of non-brominated & non-chlorinated FR system to meet UL94 V0 at 0.8mm. Key features include thin wall FR, higher stiffnes..
Tensile Modulus	3.50 GPa	508 ksi	ISO 527
Nilit FRIANYL A63 HH-KV15 Nylon 6.6 for injection molding, 15% glass ball reinforced Nylon 6.6 for injection molding, heat and hydrolysis stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Tensile Modulus	3.50 GPa	508 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics Extem UH1016M TPI Blend High heat amorphous TPI Blend, Chemical ResistantThis data was supplied by SABIC-IP for the Americas region.
Tensile Modulus	3.50 GPa	508 ksi	ISO 527-1/-2
Quadrant EPP Ertalyte® PET, cast (ISO Data) The specific properties of this virgin crystalline PET make it especially suitable for the manufacture of mechanical precision parts which have to sustain high loads and/or are subject to wear.
Tensile Modulus	3.50 GPa	508 ksi	ISO 527-1/2
Radici Radiflam® AFR (dry) Nylon 66 PA66 Self-extinguishing without halogens or phosphorousInformation provided by Radici group.
Tensile Modulus	3.50 GPa	508 ksi	50 mm/min; ASTM D638
Solvay Specialty Polymers KetaSpire® KT-820 Polyetheretherketone (PEEK)  (Unverified Data**) KetaSpire KT-820 is a low flow grade of unreinforced polyetheretherketone (PEEK) supplied in a lubricated pellet form. KetaSpire PEEK is produced to the highest industry standards and is characteriz..
Tensile Modulus	3.50 GPa	508 ksi	50 mm/min; ASTM D638
Solvay Specialty Polymers KetaSpire® KT-820 NL Polyetheretherketone (PEEK)  (Unverified Data**) KetaSpire KT-820 NL is a low flow grade of unreinforced polyetheretherketone (PEEK) supplied in non-lubricated, natural-color pellet form. KetaSpire PEEK is produced to the highest industry standard..
Tensile Modulus	3.50 GPa	508 ksi	ISO 527
Nilit FRIANYL A63 KV15 Nylon 6.6 for injection molding, 15% glass ball reinforced Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Tensile Modulus	3.50 GPa	508 ksi	ISO 527-1/-2
DSM Akulon® F223-DH (Dry) Low/Medium Viscosity, Heat Stabilized Nylon 6 (North America)  (discontinued **) Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis..
Tensile Modulus	3.50 GPa	508 ksi	ASTM D638
Loxim 210 01HB Polybutylene Terephthalate Information provided by Loxim Industries
Tensile Modulus	3.50 GPa	508 ksi
LATI Laticonther 52/11 CP1/600 F3 PP Homopolymer High thermal conductivity product based on Polypropylene homopolymer (PPh). Special filler. Potentially suitable for food/medical contact application.Availability: Africa & Middle East; Asia Pacific..
Tensile Modulus	3.50 GPa	508 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP RAL22S PA 66 LNP* LUBRICOMP* RAL22S is a compound based on Nylon 66 resin containing 10% PTFE, 10% Aramid. Added features of this material include: Wear Resistant.
Tensile Modulus	3.50 GPa	508 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP RAL22S PA 66 (Asia Pacific) LNP* Lubricomp* RAL22S is a compound based on Nylon 66 resin containing PTFE, Aramid Fiber. Added features of this material include: Internally Lubricated.
Tensile Modulus	3.50 GPa	508 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics ULTEM 1100F PEI (Europe-Africa-Middle East) Standard flow Polyetherimide (Tg 217C). Resin is RoHS compliant. UL94 V0, V2 and 5VA listing. US FDA and EU Food Contact compliant. Effective June, 2007 this grade will no longer be supported with b..
Tensile Modulus	3.50 GPa	508 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics Ultem 1110R PEI Enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Americas region.
Tensile Modulus	3.50 GPa	508 ksi	ISO 527
Styron CALIBREâ„¢ 7101-8 Polycarbonate CALIBREâ„¢ 7101-8 glass-reinforced resin offers increased modulus and improved heat distortion resistance, with minimal shrinkage. It also offers outstanding UL-94 flammability ratings. CALIBRE..
Tensile Modulus	3.50 GPa	508 ksi	ISO 527-1/-2
Unitika A175G15 PA66, 15% Glass Fiber Reinforced, Conditioned Information provided by Unitika Ltd.
Tensile Modulus	3.50 GPa	508 ksi	conditioned; ISO 527-1/-2
EMS-Grivory Grivory® EBV-2H PA6-GF20 Product description: Grilon EBV-2H is a high viscosity, heat stabilized PA6 extrusion blow molding grade with 20% glass fibers. Grilon EBV-2H has the following important properties: High melt streng..
Tensile Modulus	3.50 GPa	508 ksi	ISO 527
CP-Polymer-Technik Wellamid® 6000/52 GV 15 HWCP 15% Glass Fiber Nylon 6, Low Temperature Impact Modified, Heat Stabilized, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG
Tensile Modulus	3.50 GPa	508 ksi	ISO 527
CP-Polymer-Technik Wellamid® 6000/52 GV 15 HWUVCP 15% Glass Fiber Nylon 6, Low Temperature Impact Modified, UV Stabilized, Heat Stabilized, Conditioned Information provided by CP-Polymer-Technik GmbH & Co. KG
Tensile Modulus	3.50 GPa	508 ksi	50%RH; ISO 527-1/-2
DuPont Performance Polymers Zytel® 73G15L NC010 Nylon 6  (Unverified Data**) 15% Glass Reinforced Polyamide 6Zytel 73G15L NC010 is a 15% glass fiber reinforced polyamide 6 resin for injection molding.Information provided by DuPont Performance Polymers
Tensile Modulus	3.50 GPa	508 ksi	ISO 527
Eurotec® Tecomid® NA30 NL RM PA6.6, MoS2 modified, natural Information provided by Eurotec®
Tensile Modulus	3.50 GPa	508 ksi	ISO 527-2
Ascend Performance Materials Vydyne® ECO315 BK06 Nylon 66/6, Flame Retardant, Conditioned Vydyne® ECO315 BK06 is a non-halogenated, unfilled, flame-retardant PA66/6 copolymer with excellent toughness and ductility. It is lubricated for machine feed and easy mold release and has Underwri..
Tensile Modulus	3.50 GPa	508 ksi	ISO 527-2
Ascend Performance Materials Vydyne® M344 BLK Nylon 66, Flame Retardant, DAM Vydyne® M344 BLK is a halogenated, unfilled, flame-retardant PA66/6 copolymer designed with excellent strength and toughness. It is lubricated for machine feed and easy mold release and has Underwr..
Tensile Modulus	3.50 GPa	508 ksi	ISO 527-2
CENTROPLAST CENTROMID 6 G Polyamide 6 Cast This material has good machinability and can be bonded or welded. Its applications include sliding bearings, hammerheads, and toothed gears.Information provided by CENTROPLAST Engineering Plastics ..
Tensile Modulus	3.50 GPa	508 ksi	1[mm/min]; ISO 527-1/2
Akro-Plastic Akromid® S3 GF15 1 (3223) PA 6.10 Conditioned, 15% Glass Filled A characteristic property of AKROMID® S (PA 6.10) is that it has a renewable-resource content of up to 70 % and therefore fulfils the current definition of a bioplastic. The plant-based raw materia..
Tensile Modulus	3.50 GPa	508 ksi	ISO 527-1/-2
DSM Akulon® F223-DH Nylon 6 (European Grade) (Dry)  (discontinued **) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier ..
Tensile Modulus	3.50 GPa	508 ksi	ASTM D638
Gharda Chemicals GATONE™ 5600PF Polyetheretherketone (PEEK)  (discontinued **) Characteristics: Outstanding Chemical Resistance Outstanding Wear Resistance Outstanding Resistance to HydrolysisExcellent Mechanical Properties Outstanding Thermal properties Very good Dielectric..
Tensile Modulus	3.50 GPa	508 ksi	ISO 527-2
Ascend Performance Materials Vydyne® M344 Nylon 66/6, ignition resistant, DAM Vydyne® M344 is a halogenated, unfilled, flame-retardant PA66/6 copolymer designed with excellent strength and toughness. It is lubricated for machine feed and easy mold release and has an Underwri..