Polymer Property : Tensile Modulus = 6.92 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Tensile Modulus	6.92 GPa @Thickness 6.40 mm	1000 ksi @Thickness 0.252 in	ASTM D638
SABIC Innovative Plastics Lexan® FL930 PC Various weight reductions at 0.250"" (6.35 mm) wall, 30% GR. Superior flex strength/modulus, good tensile strength. V-0/5VA at 0.250"" (6.35 mm).
Tensile Modulus	6.92 GPa @Thickness 6.40 mm	1000 ksi @Thickness 0.252 in	ASTM D638
SABIC Innovative Plastics Lexan® FL930 PC (Asia Pacific) Various weight reductions at 0.250"" (6.35 mm) wall, 30% GR. Superior flex strength/modulus, good tensile strength. V-0/5VA at 0.250"" (6.35 mm).
Tensile Modulus	6.92 GPa @Thickness 6.40 mm	1000 ksi @Thickness 0.252 in	ASTM D638
SABIC Innovative Plastics Lexan® FL933 PC Various weight reductions at 0.250"" wall. 30% GR. Superior flexural strength and modulus; good tensile strength. UV-stabilized.
Tensile Modulus	6.92 GPa	1000 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DF0046P PC LNP* Thermocomp* DF0046P is a compound based on Polycarbonate resin containing 20% Glass Fiber. Added features include: Exceptional Processing, Non-Brominated & Non-Chlorinated Flame Retardant.
Tensile Modulus	6.92 GPa	1000 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DF0046P PC (Asia Pacific) LNP* Thermocomp* DF0046P is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: Exceptional Processing, Flame Retardant, Non-Br..
Tensile Modulus	6.92 GPa	1000 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP MF006AS PP LNP THERMOCOMP* MF006AS is a compound based on Polypropylene resin containing 30% Glass Fiber. Added features of this material include: Heat Stabilized.
Tensile Modulus	6.92 GPa	1000 ksi	ISO 527
Azdel Plus R451-B02 45% Continuous Random Fiber Mat / PP Resin Matrix AZDEL® R451-B01 is a glass mat thermoplastic laminate based upon a random oriented continuous fiber mat contained within a polypropylene resin matrix. This composite material features high flow pr..
Tensile Modulus	6.92 GPa	1000 ksi	50 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Verton RV004ESV_GY7E070 PA 66 Preliminary data for 20% long glass fiber filled, single pellet color gray, PA66This data was supplied by SABIC-IP for the Americas region.