Polymer Property : Tensile Modulus = 9.30 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Tensile Modulus	9.30 GPa	1350 ksi
Plastcom SLOVAMID 6 GF 30 FRA 5 PA6, 30% glass fibre, flame retardant FeaturesPA 6 for injection moulding, chemically reinforced with 30% glass fibre, with halogen flame retardant. Main features: flammability in accordance with UL 94 V0 at 1.6 mm, glow wire at 960°C,..
Tensile Modulus	9.30 GPa	1350 ksi	STN EN ISO 527-2
Plastcom SLOVASTER® B GF 30 FRK 3 Polybutylene Terephthalate, 30% Chemically Coupled Glass Fiber, Red Phosphorus Flame Retardant FeaturesPBT with the content of 30% chemically coupled glass fiber and flame retardant based on red phosphorus. Anisotropy of shrinkage enables injection moulding of round, cylindrical or other hol..
Tensile Modulus	>= 9.30 GPa	>= 1350 ksi	ISO 527-1,2
Qualchem Danamid AFGF-30 Polyamide 66, 30% Glass Fiber Reinforced with glass fiberInformation provided by Qualchem Zrt.
Tensile Modulus	>= 9.30 GPa	>= 1350 ksi	ISO 527-1,2
Qualchem Danamid AFGFH-30 Polyamide 66, 30% Glass Fiber Reinforced with glass fiber. Heat stabilized, for long-lasting use at 120-140°C.Information provided by Qualchem Zrt.
Tensile Modulus	9.30 GPa	1350 ksi	d.a.m.; ISO 527-1, -2; 1 mm/min
Lanxess DurethanÂ® BKV 130 DUS008 901510 Nylon 6, Glass Fiber Reinforced, Impact Modified PA 6, 30% glass fibers, injection molding, impact modifiedInformation provided by LANXESS.
Tensile Modulus	9.30 GPa	1350 ksi	ISO 527-1/-2
Lanxess DurethanÂ® BKV 30 EF 000000 Nylon 6, 30% Glass Fiber PA 6, injection molding grade, 30% glass fibers, low viscosity (Easy Flow)
Tensile Modulus	9.30 GPa	1350 ksi
Haveg 41N Phenolic; Silicate Reinforced Ablative Material A proprietary thermoset plastic consisting of a phenol-formaldehyde resin and non-asbestos silicate fillers converted to a permanent thermoset state under heat and pressure. It is designed for abla..
Tensile Modulus	9.30 GPa	1350 ksi	5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM 2300R PEI (Asia Pacific) 30% Glass fiber filled, standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.
Tensile Modulus	9.30 GPa	1350 ksi	5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM HU2300 PEI 30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP ..
Tensile Modulus	9.30 GPa	1350 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics ValoxÂ® 420 PBT 30% GR, excellent strength, stiffness and dimensional stability. High heat resistance. Appliance handles, spotlights, electric motors, connectors.
Tensile Modulus	9.30 GPa	1350 ksi	5 mm/min; ASTM D638
SABIC Innovative Plastics ValoxÂ® 420HP PBT 30% Glass filled PBT resin, FDA Food Contact compliant in limited colors. Effective March 2008 this grade will no longer be supported with biocompatibility information. Alternative grade Valox HX420..
Tensile Modulus	9.30 GPa	1350 ksi	1 mm/min; ISO 527
SABIC Innovative Plastics ValoxÂ® 420HP PBT 30% Glass filled PBT resin, FDA Food Contact compliant in limited colors. Effective March 2008 this grade will no longer be supported with biocompatibility information. Alternative grade Valox HX420..
Tensile Modulus	9.30 GPa	1350 ksi	5 mm/min; ASTM D638
SABIC Innovative Plastics ValoxÂ® 5031 PBT (Europe-Africa-Middle East) VALOX 5031 is a 30% glass reinforced PBT+PC blend with low warpage characteristics. Applications: appliance handles, automotive doorhandles. This grade is a 508 with reduced warpage.
Tensile Modulus	9.30 GPa	1350 ksi	50 mm/min; ASTM D 638
SABIC Innovative Plastics LNP Thermocomp MF0069S PP (Asia Pacific) LNP* Thermocomp* MF0069S is a compound based on Polypropylene resin containing Glass Fiber, Flame Retardant. Added features of this material include: Chemically Coupled, Flame Retardant, Heat Stabi..
Tensile Modulus	9.30 GPa	1350 ksi	5 mm/min; ASTM D638
SABIC Innovative Plastics ValoxÂ® HX420HP PBT Medium Flow, 30% Glass filled, Polybutylene Terephthalate (PBT) resin. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI)..
Tensile Modulus	9.30 GPa	1350 ksi	5 mm/min; ASTM D638
SABIC Innovative Plastics ValoxÂ® HX420HP PBT (Europe-Africa-Middle East) Medium Flow, 30% Glass filled, Polybutylene Terephthalate (PBT) resin. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI)..
Tensile Modulus	9.30 GPa	1350 ksi	ISO 527
CP-Polymer-Technik Wellamid® 6000 GVZ 30 HWCP 30% Glass Fiber Z-Qualities Nylon 6, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG
Tensile Modulus	9.30 GPa	1350 ksi	ISO 527
CP-Polymer-Technik Wellamid® 6000 GV 30 HWCP 30% Glass Fiber Nylon 6, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG
Tensile Modulus	9.30 GPa	1350 ksi	ISO 527
Azoty Tarnow™ TARNOFORM 300 GF6 POM 30% glass fiber reinforced injection molding grade, suitable for applications where increased strength and stiffness is required.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A...
Tensile Modulus	9.30 GPa	1350 ksi	1mm/min; ISO 527
BASF Ultramid® 8333G HI 33% Glass Filled PA6 (Dry) Ultramid 8333G HI is a 14% glass reinforced, impact modified PA6 injection molding compound developed for applications requiring improved dry as molded toughness in combination with a balance of st..