Polymer Property : Fracture Toughness = 4.00 MPa-mÂ½ Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Fracture Toughness	4.00 MPa-mÂ½	3.64 ksi-inÂ½
ICE Hot Pressed SiC Data provided by the manufacturer, International Ceramic Engineering.
Fracture Toughness	4.00 MPa-m½	3.64 ksi-in½	ASTM C1421
M Cubed Technologies SSC-702 Reaction-Bonded Silicon Carbide Medium-grained reaction-bonded SiC for high wear applications. Bullnoses, fan liners, hydrocyclone liners, etc. Can be cast into very large shapes (greater than 4 ft. square, 5-6 inches thick)Info..
Fracture Toughness	4.00 MPa-m½	3.64 ksi-in½	ASTM C1421
M Cubed Technologies SSC-802 Reaction-Bonded Silicon Carbide Medium-grained reaction-bonded SiC for high wear applications. Bullnoses, fan liners, hydrocyclone liners, etc. Can be cast into very large shapes (greater than 4 ft. square, 5-6 inches thick)Info..
Fracture Toughness	4.00 MPa-m½	3.64 ksi-in½	ASTM C1421
M Cubed Technologies SSC-FG Reaction-Bonded Silicon Carbide, Fine-Grained Fine-grained reaction-bonded SiC. Used for mechanical seals and other SiC applications that require a high surface finish/tight tolerances. Si content can be tailored for the application.Informati..
Fracture Toughness	4.00 MPa-m½	3.64 ksi-in½	ASTM C1421
M Cubed Technologies SSC-903 Reaction-Bonded Silicon Carbide Coards-grained reaction-bonded SiC for high wear applications. Bullnoses, fan liners, hydrocyclone liners, etc. Can be cast into very large shapes (greater than 4 ft. square, 5-6 inches thick)Info..
Fracture Toughness	4.00 - 5.00 MPa-m½	3.64 - 4.55 ksi-in½
CoorsTek AD-94 Alumina (nom. 94% Al2O3) Thermal Shock Delta Tc = 250°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar..
Fracture Toughness	4.00 - 5.00 MPa-m½	3.64 - 4.55 ksi-in½
CoorsTek AD-96 Alumina (nom. 96% Al2O3) Thermal Shock Delta Tc = 250°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar..
Fracture Toughness	4.00 - 5.00 MPa-m½	3.64 - 4.55 ksi-in½
CoorsTek AD-995 Alumina (nom. 99.5% Al2O3) Thermal Shock Delta Tc = 200°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar..
Fracture Toughness	4.00 - 5.00 MPa-m½	3.64 - 4.55 ksi-in½	Klc; Notched Beam
CoorsTek AD-996 99.6% Alumina
Fracture Toughness	4.00 - 5.00 MPa-m½	3.64 - 4.55 ksi-in½
CoorsTek AD-998 Alumina(nom. 99.8% Al2O3) Thermal Shock Delta Tc = 200°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar..
Fracture Toughness	4.00 - 5.00 MPa-m½	3.64 - 4.55 ksi-in½	Klc; Notched Beam
CoorsTek CAP 3 99.5% Alumina Ceramic Armor Material CoorsTek CeraShield™ ceramics provide: low weight, high hardness, controlled, uniform microstructure, dimensional stability over wide temperature range, compatibility for use in finished armor sys..
Fracture Toughness	4.00 - 5.00 MPa-m½	3.64 - 4.55 ksi-in½	Klc; Notched Beam
CoorsTek CAP 4 98.5% Alumina Ceramic Armor Material CoorsTek CeraShield™ ceramics provide: low weight, high hardness, controlled, uniform microstructure, dimensional stability over wide temperature range, compatibility for use in finished armor sys..
Fracture Toughness	4.00 - 5.00 MPa-m½	3.64 - 4.55 ksi-in½
CoorsTek Direct Sintered Silicon Carbide, SC DS (SC-30, UltraSiC™) Thermal Shock Delta Tc = 300°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar..
Fracture Toughness	4.00 - 5.00 MPa-m½	3.64 - 4.55 ksi-in½	Klc; Notched Beam
CoorsTek FG-98 98% Alumina Ceramic Armor Material CoorsTek CeraShield™ ceramics provide: low weight, high hardness, controlled, uniform microstructure, dimensional stability over wide temperature range, compatibility for use in finished armor sys..
Fracture Toughness	4.00 - 5.00 MPa-m½	3.64 - 4.55 ksi-in½
CoorsTek FG-995 Alumina (nom. 98.5% Al2O3) Thermal Shock Delta Tc = 200°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar..
Fracture Toughness	4.00 - 5.00 MPa-m½	3.64 - 4.55 ksi-in½	Notched Beam
CoorsTek PlasmaPure™ Alumina (nom. 99.8% Al2O3) Thermal Shock Delta Tc = 200°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar..
Fracture Toughness	4.00 - 5.00 MPa-m½	3.64 - 4.55 ksi-in½	Klc; Notched Beam
CoorsTek PlasmaPure-UC™ 99.9% Alumina
Fracture Toughness	4.00 - 5.00 MPa-m½	3.64 - 4.55 ksi-in½
CoorsTek Reaction Bonded Silicon Carbide, SCRB (SC-2) Thermal Shock Delta Tc = 400°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a shar..
Fracture Toughness	4.00 - 5.00 MPa-m½	3.64 - 4.55 ksi-in½	Klc; Notched Beam
CoorsTek Z-PLUS™ 94 Zirconia-Impr. Alumina Ceramic Armor Material CoorsTek CeraShield™ ceramics provide: low weight, high hardness, controlled, uniform microstructure, dimensional stability over wide temperature range, compatibility for use in finished armor sys..