Polymer Property : Flexural Yield Strength = 155 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	155 MPa	22500 psi	2 mm/min; ISO 178
SABIC Innovative Plastics EXTEM UH1006 TPI Blend High Heat Amorphous TPI Blend, Excellent Chemical Resistance, High Continuous Use Temperature (CUT), Best-in-class FR, OSU and LOI. Material is UL-listed. This material is RoHS compliant and also ha..
Flexural Yield Strength	155 MPa	22500 psi	2 mm/min; ISO 178
SABIC Innovative Plastics EXTEM UH1016 TPI Blend High heat amorphous TPI Blend, Chemical Resistant, High Flow
Flexural Yield Strength	155 MPa	22500 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Extem UH1016M TPI Blend High heat amorphous TPI Blend, Chemical ResistantThis data was supplied by SABIC-IP for the Americas region.
Flexural Yield Strength	155 MPa	22500 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Extem UH1016M TPI Blend (Asia Pacific) High heat amorphous TPI Blend, Chemical ResistantThis data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Yield Strength	155 MPa	22500 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Extem UH1016M TPI Blend (Europe-Africa-Middle East) High heat amorphous TPI Blend, Chemical ResistantThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Flexural Yield Strength	155 MPa	22500 psi	2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics EXTEM VH1003 PEI Copolymer Transparent, Thermoplastic Polyimide (TPI) resin with a glass transition temperature (Tg) of 247C. This product has thinwall FR capability and has a UL94 V0 listing. This material is RoHS compliant..
Flexural Yield Strength	155 MPa	22500 psi	2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics EXTEM VH1003F PEI Copolymer (Europe-Africa-Middle East) Transparent, Thermoplastic Polyimide (TPI) resin. Glass transition Temp. (Tg) of 247°C. Global Food Contact Approval. Resin is subject to Commerce Control Laws U.S. 15CFR Chapter VII, Part 774 and ..
Flexural Yield Strength	155 MPa	22500 psi	2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics EXTEM VH1003M PEI Copolymer Transparent, Thermoplastic Polyimide (TPI) resin with a glass transition temperature (Tg) of 247C. Internal mold release. This product has thinwall FR capability and has a UL94 V0 listing. This mate..
Flexural Yield Strength	155 MPa	22500 psi	2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics EXTEM VH1003M PEI Copolymer (Europe-Africa-Middle East) Transparent, Thermoplastic Polyimide (TPI) resin. Glass transition Temp. (Tg) of 247°C. Internal mold release. This resin has thinwall FR capability and has a UL94 V0 listing. Resin is halogen free..
Flexural Yield Strength	155 MPa	22500 psi	2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics EXTEM VH1003F PEI Copolymer (Asia Pacific) Transparent, Thermoplastic Polyimide (TPI) resin. Glass transition Temp. (Tg) of 247°C. Global Food Contact Approval. Resin is subject to Commerce Control Laws U.S. 15CFR Chapter VII, Part 774 and ..
Flexural Yield Strength	155 MPa	22500 psi	ASTM D790
PolyOne Stat-Tech™ PF-05CF/000 EM FR Flame Retardant Polysulfone - 5% Carbon Fiber  (discontinued **) Data provided by PolyOne.
Flexural Yield Strength	155 - 290 MPa	22500 - 42000 psi	Average value: 214 MPa Grade Count:15
Overview of materials for Liquid Crystal Polymer (LCP), Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), Carbon Fiber Filled". Each property range of values reported is minimum an..
Flexural Yield Strength	155 MPa	22500 psi
Idemitsu Kosan XarecÂ® EA 513 SPS, 30% Glass Filled
Flexural Yield Strength	155 MPa	22500 psi
Idemitsu Kosan XarecÂ® EA 522 SPS, 22% Glass Filled Crystalline Polymer, Glass Filled, Ignition Resistant, Impact Modified. Used in Electronic and Electrical applications
Flexural Yield Strength	155 MPa	22500 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ULTEM 4002 PEI PTFE filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL 94 V0 and 5VA listing in recognized colors.
Flexural Yield Strength	155 MPa	22500 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM DU319 PEI Transparent Polyetherimide blend. ECO Conforming. US FDA and EU Food Contact Compliant in recognized colors.
Flexural Yield Strength	155 MPa	22500 psi	2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics ULTEM XH6050 PEI Copolymer Transparent, enhanced flow Polyetherimidesulfone copolymer (Tg 247C). ECO Conforming, UL94 V0 listing. Resin is subject to U.S. Commerce Control Laws (15CFR Chapter VII, Part 774).
Flexural Yield Strength	155 MPa	22500 psi	2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics ULTEM XH6050 PEI Copolymer (Asia Pacific) Transparent, enhanced flow Polyetherimidesulfone copolymer (Tg 247C). ECO Conforming, UL94 V0 listing. Resin is subject to U.S. Commerce Control Laws (15CFR Chapter VII, Part 774).
Flexural Yield Strength	155 MPa	22500 psi	2.6 mm/min, 100 mm span; ASTM D 790
SABIC Innovative Plastics Ultem XH6050 PEI Copolymer (Europe-Africa-Middle East) Transparent, enhanced flow Polyetherimidesulfone copolymer (Tg 247C). ECO Conforming, UL94 V0 listing. Resin is subject to U.S. Commerce Control Laws (15CFR Chapter VII, Part 774).This data was su..
Flexural Yield Strength	155 MPa	22500 psi	2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics ULTEM XH6050F PEI Copolymer Transparent, enhanced flow Polyetherimidesulfone copolymer (Tg 247C). ECO Conforming. US FDA Compliant. Resin is subject to U.S. Commerce Control Laws (15CFR Chapter VII, Part 774).
Flexural Yield Strength	155 MPa	22500 psi	2.6 mm/min, 100 mm span; ASTM D 790
SABIC Innovative Plastics Ultem XH6050F PEI Copolymer (Europe-Africa-Middle East) Transparent, enhanced flow Polyetherimidesulfone copolymer (Tg 247C). ECO Conforming. US FDA Compliant. Resin is subject to U.S. Commerce Control Laws (15CFR Chapter VII, Part 774).This data was ..
Flexural Yield Strength	155 MPa	22500 psi	2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics NORYL GTX GTX810 PPE+PS+PA 10% Glass Reinforced PPE+PA Alloy.
Flexural Yield Strength	155 MPa	22500 psi	2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics ULTEM XH6050M PEI Copolymer (Asia Pacific) Enhanced flow Polyetherimidesulfone copolymer (Tg 247C) with internal mold release. ECO Conforming, UL94 V0 listing. Resin is subject to U.S. Commerce Control Laws (15CFR Chapter VII, Part 774).
Flexural Yield Strength	155 MPa	22500 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Noryl GFN1420V PPE+PS (Asia Pacific) Noryl* GFN1420V resin is a high flow blend of polyphenylene ether (PPE) and polystyrene (PS) resin that contains 20 % glass reinforcement. The resin is suitable for injection molding and is designe..
Flexural Yield Strength	155 MPa	22500 psi	ISO 178
Wellman EcoLon® MRGF1518-BK Mineral/Glass Fiber Reinforced Nylon 66, Lubricated, Heat Stabilized, PCR Typical Applications: Lawn and garden equipment, automotive trim, bezels, wheel covers, window frames, gas tank filler housings, brackets, metalized lighting reflectors for automotive, automotive co..
Flexural Yield Strength	155 MPa	22500 psi	3.94" span; ASTM D790
Westlake Plastics Tempalux® 5000 Polyetherimide An amorphous thermoplastic polyetherimide, stock shapes from ULTEM® resin possess a combination of useful characteristics, including high heat resistance, high strength at elevated temperatures, hi..
Flexural Yield Strength	155 MPa	22500 psi	ASTM D790
E-Polymers Tekaloy® G70GR , 30% Glass Reinforced PC/ABS Alloy 30% Glass Fiber reinforced, High stiffness, Dimensional stabilityInformation provided by E-Polymers Co. Ltd.
Flexural Yield Strength	155 MPa	22500 psi
3M Filtek™ Z250 Universal Restorative Dental Composite 3M™ Filtek™ Z250 universal restorative is an esthetic, light cured, radiopaque composite specifically designed for use in anterior or posterior direct or indirect restorations. Bonding to tooth s..
Flexural Yield Strength	155 MPa	22500 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Noryl GFN1420V PPE+PS Noryl* GFN1420V resin is a high flow blend of polyphenylene ether (PPE) and polystyrene (PS) resin that contains 20 % glass reinforcement. The resin is suitable for injection molding and is designe..
Flexural Yield Strength	155 - 430 MPa	22500 - 62400 psi	Average value: 304 MPa Grade Count:32
Overview of materials for Polyphthalamide (PPA), Carbon Fiber + PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, Carbon Fiber + PTFE Filled". Each property range of values reported is minimum and maxi..