Polymer Property : Tensile Strength, Ultimate = 107000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	740 MPa <br>@Temperature 760 Â°C	107000 psi <br>@Temperature 1400 Â°F
Haynes 25 alloy, cold worked sheet, 20 % cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980Â°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga..
Tensile Strength, Ultimate	735 MPa	107000 psi
Haynes HR-120Â® alloy, solution heat-treated Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts ..
Tensile Strength, Ultimate	740 MPa	107000 psi
Haynes 556Â® alloy, all-weld metal GTAW Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Tensile Strength, Ultimate	735 MPa <br>@Temperature 650 Â°C	107000 psi <br>@Temperature 1200 Â°F
Haynes HastelloyÂ® B-3Â® alloy, 6.3 mm plate The attributes of Corrosion-Resistant HASTELLOYÂ® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and ..
Tensile Strength, Ultimate	738 MPa	107000 psi
Haynes HastelloyÂ® C-4 alloy, all-weld metal, as welded, GTAW Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900Â°F (649 to 1038Â°C) rang..
Tensile Strength, Ultimate	735 MPa	107000 psi
Haynes HR-120Â® alloy, solution heat-treated plate Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts ..
Tensile Strength, Ultimate	735 MPa	107000 psi	Annealed
Special Metals BRIGHTRAYÂ® Alloy S Electrical Resistance Alloy A nickel-chromium electrical-resistance alloy for use at temperatures up to 2100Â°F (1150Â°C) under continuous operating conditions. It is similar to BRIGHTRAY alloy C but does not contain rare..
Tensile Strength, Ultimate	738 MPa	107000 psi
Special Metals INCONELÂ® 690 Nickel Superalloy, Hot Rolled Flat, 0.62 inch (16 mm) Diameter Composition adjustments for nuclear applications: 28-31 Cr; 0.04 max C; 0.10 max Co.Tensile strength (ultimate and yield) and elongation values reported here are typical for Hot Rolled Flat, 0.62 in..
Tensile Strength, Ultimate	738 MPa	107000 psi	post-weld heat-treated
Universal Wire Works E91T1-B3 Flux Cored Carbon Steel Tubular Electrode Alloy 91T1-B3 is a low alloy steel electrode for single and multiple pass welding of 2.25% chromium, 1 % molybdenum high temperature creep resistant steels in all positions. The fast freezing slag s..
Tensile Strength, Ultimate	738 MPa	107000 psi
Crucible Steel 440B Chromium Steel Crucible 440B Is a hardenable chromium steel which is cutlery grade having high attainable hardness and toughness. This grade is magnetic at all times. Information provided by Crucible Specialty Me..
Tensile Strength, Ultimate	>= 740 MPa	>= 107000 psi
CLAL-MSX DECLAFOR® 1015 TDX Wire quenched/Cold Rolled Copper Alloy Main Characteristic: Age hardening alloyBeriyllium free alloyGood machinabilityHigh mechanical propertiesTypical Applications:Coaxial connectorsSpectacles partsSliding contacts partsAll kind of turn..
Tensile Strength, Ultimate	740 - 860 MPa	107000 - 125000 psi
CLAL-MSX NICLAFOR® 1000 TF Quenched/Precipitation Heat Treated, Rolled Copper Alloy Finished parts can be produced with: reduction in sections, high mechanical properties even at high temperature, high spring properties, high conductivity, good resistance to corrosion, low permeabi..
Tensile Strength, Ultimate	737 MPa	107000 psi
ATI Allegheny Ludlum AL 409 Cb™ Brazeable Ferritic Stainless Steel, 43.6% Cold Work AL 409 Cb™ is normally 12.5% chromium ferritic stainless steel with columbium stabilization and with restricted titanium and aluminum contents. As a result of these alloying adjustments, the braze..
Tensile Strength, Ultimate	738 MPa <br>@Temperature 23.0 °C	107000 psi <br>@Temperature 73.4 °F
ATI Allegheny Ludlum Stainless Steel Free Machining Grade Type 416, Tempered at 649°C (1200°F) (UNS S41600) Allegheny Ludlum's 416 is a free-machining stainless steel specifically designed to exhibit improved machinability. These modifications retain, in so far as possible, the good mechanical properties..
Tensile Strength, Ultimate	738 MPa <br>@Temperature 93.0 °C	107000 psi <br>@Temperature 199 °F
Haynes Hastelloy® C-22® alloy, 6.4-19.1 mm thick plate, solution heat treated HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al..