Polymer Property : Tensile Strength, Ultimate = 110 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	110 MPa	16000 psi	ASTM D638
Shell Carilon® DB6F5G40 Polyketone, Flame-Retarded (V-0), 20% Glass-Reinforced Injection Molding Grade  (disco Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON Polymer DB6F5G40 is a flame-retarded, 20 percent glass-fiber-reinforced, injection molding grade with mecha..
Tensile Strength, Ultimate	110 MPa	16000 psi	ISO 527
LATI LAESTRA G/30 30% Glass Fiber Reinforced Syndiotactic Polystyrene (SPS)  (discontinued **) Description: Laestra compounds are syndiotactic polystyrene (SPS) products. SPS is a polymer offering a combination of properties unavailable with other materials. It exhibits a melting point of 270..
Tensile Strength, Ultimate	110 - 159 MPa	16000 - 23000 psi	Average value: 137 MPa Grade Count:14
Overview of materials for Polyetherimide (PEI), 20% Glass Fiber This property data is a summary of similar materials in the MatWeb database for the category "Polyetherimide, 20% Glass Fiber". Specific grades with glass content between 15% and 24% are included. E..
Tensile Strength, Ultimate	110 - 110 MPa @Temperature >=130 °C	16000 - 16000 psi @Temperature >=266 °F	Average value: 128 MPa Grade Count:1
Overview of materials for Nylon 66/6, 40% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 40% Glass Fiber Reinforced". Specific grades with glass content between 35% and 44% are incl..
Tensile Strength, Ultimate	110 MPa	16000 psi	ASTM D638
Global 508 30% Glass Filled PBT Gray Information provided by Global Polymers Corporation.
Tensile Strength, Ultimate	110 MPa @Temperature 1095 Â°C	16000 psi @Temperature 2003 Â°F
Haynes 556Â® alloy, hot rolled, solution annealed plate, 6.4-12.7 mm (1/2 in.) thick Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Tensile Strength, Ultimate	110 MPa	16000 psi	ISO 527
Solvay TechnylÂ® C 216 Nylon 6, 30% Glass Fiber, EH50 Polyamide PA6, reinforced with 30% of glass fiber, for injection molding.It has good mechanical properties. It is used in all sectors of industry, offering an excellent combination between thermal ..
Tensile Strength, Ultimate	110 MPa	16000 psi	ISO 527
Wellman Wellamid® FRGF25-66-N Flame Retardant Nylon 66, Lubricated, 25% Glass Fiber Typical Applications: Electrical terminal blocks, electric fan switch housings, coil forms, multi-pin electrical connectors, electric fan switch housings, TV tuner components, automotive switch hous..
Tensile Strength, Ultimate	110 MPa	16000 psi	cond; ISO 527-1/-2
DSM Akulon® K224-G6-FC BK00001 PA6-GF30 30% Glass Reinforced, Food Contact Grade
Tensile Strength, Ultimate	110 MPa	16000 psi	cond; ISO 527-1/-2
DSM Akulon® K224-G6-FC NA99001 PA6-GF30 30% Glass Reinforced, Food Contact Grade
Tensile Strength, Ultimate	110 MPa	16000 psi	ISO 527-1/-2
DSM Arnite® TV4 241 SN PBT-GF20 FR(17) 20% Glass Reinforced, Flame Retardant
Tensile Strength, Ultimate	110 MPa @Temperature 160 °C	16000 psi @Temperature 320 °F	ISO 527-1/-2
DSM Stanyl® 46HF4530 PA46-GF30 30% Glass Reinforced, Heat Stabilized, High Flow, for E&E applications
Tensile Strength, Ultimate	110 MPa @Temperature 160 °C	16000 psi @Temperature 320 °F	ISO 527-1/-2
DSM Stanyl® TW272B6 (PA46+PTFE)-CF30 30% Carbon Reinforced, Heat Stabilized, Wear and Friction Modified
Tensile Strength, Ultimate	110 MPa	16000 psi	5 mm/min
Arkema Group Orgalloy® RS 6020 Nylon 6 Alloy, 20% Glass Fiber (Conditioned) RS 60 series, rigid polyamide 6 alloy: easy to process, chemical resistance (no known solvents) and low moisture absorption leading to stability of mechanical, electrical and dimensional properties...
Tensile Strength, Ultimate	110 MPa	16000 psi	5 mm/min
Arkema Group Rilsan® BZM 23 G9 Nylon 11, 23% Glass Fiber Filled (Dry) Designation ISO 1874-PA11,MS,18-040,(G+C)(F+D)(25+05)Rigid grade with glass fiber (23%) and graphite filler for injection molding. Available color: steel black gray. Additive free.Rigidity. Low fric..
Tensile Strength, Ultimate	110 - 140 MPa	16000 - 20300 psi	ASTM D638
Chang Chun Plastic PBT3030 30% Glass Fiber Enforced PBT Information provided by Dowell Trading Company Ltd.
Tensile Strength, Ultimate	110 MPa	16000 psi	ASTM D638
Chem Polymer Chemlon 115 G Nylon 66, 15% Glass Fiber Reinforced A 15% glass fiber reinforced nylon 66 offering improved creep resistance, stiffness, tensile strength and dimensional stability over unmodified nylon 66 materials. This product offers slight improv..
Tensile Strength, Ultimate	110 MPa	16000 psi	ASTM D638
A. Schulman ComAlloy Hiloy® 512 Polycarbonate, Glass Reinforced, UL Data provided by the manufacturer, ComAlloy International Company.20% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Tensile Strength, Ultimate	110 MPa	16000 psi	5 mm/min
Arkema Group Orgalloy® R 6030 Nylon 6 Alloy, 30% Glass fiber (Conditioned) Rigid polyamide 6 alloy: easy to process, low moisture absorption, chemical resistance (no known solvents).Special 30% glass fiber reinforced for overmolding with modified PP.ISO data provided by th..
Tensile Strength, Ultimate	110 MPa	16000 psi	ASTM D638
Adell AJ-14 Nylon 66, 20% Glass Reinforced; High Impact Data provided by Adell Plastics, Inc.
Tensile Strength, Ultimate	110 MPa	16000 psi	ASTM D638
Adell AJ-34 Nylon 66, 20% Glass Reinforced; High Impact Data provided by Adell Plastics, Inc.
Tensile Strength, Ultimate	110 MPa	16000 psi	ATSM D638
Ashley Polymers Ashlene® 520-25GU Nylon 66, 25% Glass Reinforced Nylon 66, 25% glass reinforced resin, utility grade.Data provided by the manufacturer
Tensile Strength, Ultimate	110 MPa	16000 psi	ATSM D638
Ashley Polymers Ashlene® 830L-13G Nylon 6, 13% Glass Reinforced A 13% glass fiber reinforced Nylon 6 designed to provide a high flexural modulus and good dimensional stability while maintaining the ease of processing associated with Nylon 6 type materials.Data p..
Tensile Strength, Ultimate	110 MPa @Temperature 180 °C	16000 psi @Temperature 356 °F	ISO 527-1/-2
DSM Stanyl® TS200F10 PA46-GF50 50% Glass Reinforced