Polymer Property : Tensile Strength, Ultimate = 120 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	120 MPa	17400 psi	CD; DIN EN ISO 527
Propex Fabrics Curv™ C100A Polypropylene/Polypropylene Thermoformable Composite Curv™ key features include weight savings, total recyclability, no glass content, thermoformable, high impact strength, inertness, and abrasion resistance.Data provided by BP Amoco; Curv was spun o..
Tensile Strength, Ultimate	120 MPa	17400 psi	ASTM data at 5 mm/min.
BASF Capron® GR40 HS 40% Glass-Filled Nylon 6 (Conditioned)  (discontinued **) Capron GR40 HS is a heat stabilized 40% glass reinforced polyamide 6 injection molding compound offering the highest level of strength, stiffness, high temperature performance and dimensional stabil..
Tensile Strength, Ultimate	120 MPa	17400 psi	ASTM data at 5 mm/min.
BASF Capron® SEG3 H1 15% Glass-Filled Nylon 6 (Dry)  (discontinued **) Capron SEG3 H1 is a 15% glass reinforced nylon 6 injection molding compound exhibiting. It exhibits exceptional surface aesthetics at the slower fill speeds associated with the gas assist injection ..
Tensile Strength, Ultimate	120 MPa @Temperature 1090 Â°C	17400 psi @Temperature 2000 Â°F
Kennametal Stellite StelliteÂ® 6K 1.6 mm thick sheet 13.3 mm^3 volume loss--abrasive wear data. Applications include agitators, augers, ball mills, banbury mills, cams, crusher bearings, dryers, dry presses, dump cars, fans, filters, food machinery, g..
Tensile Strength, Ultimate	120 MPa	17400 psi
GBC Grade 85 Alumina Data provided by the manufacturer, GBC Materials Corporation.
Tensile Strength, Ultimate	120 MPa	17400 psi	ISO 527-1, 2
Polyplastics Duranex® 3200 Polybutylene Terephthalate (PBT), Standard, 20% GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers ..
Tensile Strength, Ultimate	120 MPa	17400 psi	dry; ISO 527-1/-2
DSM Akulon® Ultraflow K-FHGM35 PA6-(GF+MD)40 15% Glass Reinforced, Heat Stabilized, High Flow
Tensile Strength, Ultimate	120 MPa	17400 psi	ISO 527-1/-2
DSM Arnite® TV6 240 PBT-GF20 20% Glass Reinforced
Tensile Strength, Ultimate	120 MPa	17400 psi	cond; ISO 527-1/-2
DSM Novamid® 1010GN2-30 NAT/BK37 PA6-GF30 FR(17) 30% Glass Reinforced, Flame Retardant
Tensile Strength, Ultimate	120 MPa	17400 psi	cond; ISO 527-1/-2
DSM Novamid® 1015G35 NAT PA6-GF35 35% Glass Reinforced, Injection Molding
Tensile Strength, Ultimate	120 MPa	17400 psi	cond; ISO 527-1/-2
DSM Novamid® 1015GH35 BK37 PA6-GF35 35% Glass Reinforced, Heat Stabilized, Injection Molding
Tensile Strength, Ultimate	120 MPa	17400 psi	cond; ISO 527-1/-2
DSM Novamid® 1017GH33 BK701 PA6-GF33 33% Glass Reinforced, Heat Stabilized, Injection Molding
Tensile Strength, Ultimate	120 MPa	17400 psi	cond; ISO 527-1/-2
DSM Novamid® 3010GN30 NAT PA66-GF30 FR(17) 30% Glass Reinforced, Flame Retardant
Tensile Strength, Ultimate	120 MPa	17400 psi	5mm/min; ISO 527
BASF Ultramid® B3GM35 Q611 15/25% Glass/Mineral Filled PA6 (Dry) Ultramid B3GM35 Q611 is a 40% combined glass-fiber and mineral reinforced injection molding PA6 grade.
Tensile Strength, Ultimate	120 MPa	17400 psi	5mm/min; ISO 527
BASF Ultramid® B3WGM24 BK30564 10/20% Glass/Mineral Filled PA6 (Dry) Ultramid B3WGM24 BK30564 is a 30% glass/mineral filled heat stabilized injection molding PA6 grade for industrial articles having medium to high rigidity and high dimensional stability.
Tensile Strength, Ultimate	120 MPa @Temperature 649 °C	17400 psi @Temperature 1200 °F
ATI Allegheny Ludlum AL 453™ Stainless Steel Single phase iron-chromium ferritic stainless steel alloy. Should be annealed between 1450 and 1600°F and quickly cooled. Information provided by Allegheny Ludlum
Tensile Strength, Ultimate	120 MPa	17400 psi	5 mm/min
Arkema Group Orgalloy® RS 6030 AT Nylon 6 Alloy, 30% Glass Fiber (Conditioned) RS 60 series, rigid polyamide 6 alloy: easy to process, chemical resistance (no known solvents) and low moisture absorption leading to stability of mechanical, electrical and dimensional properties...
Tensile Strength, Ultimate	120 MPa	17400 psi	ISO 527-1/-2
DSM Arnite® TV6 241 SN PBT-GF20 FR(17) 20% Glass Reinforced, Flame Retardant
Tensile Strength, Ultimate	120 MPa	17400 psi	cond; ISO 527-1/-2
DSM Novamid® 3021GH30 BK629 PA66-GF30 30% Glass Reinforced, Heat Stabilized
Tensile Strength, Ultimate	120 MPa	17400 psi	ASTM data at 5 mm/min.
BASF Capron® GR40 40% Glass-Filled Nylon 6 (Conditioned)  (discontinued **) Capron GR40 is a 40% glass reinforced polyamide 6 injection molding compound offering the highest level of strength, stiffness, high temperature performance and dimensional stability. It is also ava..
Tensile Strength, Ultimate	120 MPa	17400 psi	ASTM D638
Solvay Specialty Polymers Ixef® 2530/X9027 Polyarylamide, 55% Mineral + Glass Fiber, at Equilibrium (65% RH)   The IXEF compounds are a family of semi-crystalline polyarylamide thermoplastics reinforced with glass fibers and/or mineral fillers for injection molding.Data provided by the manufacturer, Solvay A..
Tensile Strength, Ultimate	120 MPa @Temperature 90.0 °C	17400 psi @Temperature 194 °F	ISO 527
LATI LARTON G/50 50% Glass Fiber Filled Polyphenylene sulfide (PPS)  (discontinued **) Description: Larton thermoplastics are polyphenylene sulfide (PPS) products. They are distinguished by a group of very interesting properties combined with easy moldability. Larton parts feature: ex..
Tensile Strength, Ultimate	120 MPa	17400 psi	5mm/min; ISO 527
BASF Nypel® 2367G HS BK 15/25% Glass/Mineral Filled PA6 (Dry) Nypel 2367G HS BK-4 is a black pigmented, heat stabilized, 40% mineral and glass fiber reinforced injection molding compound based on recycled PA6 feedstocks. It possesses a balance of engineering ..
Tensile Strength, Ultimate	120 MPa @Temperature 160 °C	17400 psi @Temperature 320 °F	ISO 527-1/-2
DSM Stanyl® TS200F10 PA46-GF50 50% Glass Reinforced
Tensile Strength, Ultimate	120 - 130 MPa @Temperature 130 - 180 °C	17400 - 18900 psi @Temperature 266 - 356 °F	Average value: 98.0 MPa Grade Count:5
Overview of materials for Polyphthalamide (PPA), Glass Fiber 40% This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, Glass Fiber 40%". Specific grades with glass content between 35% and 44% are included. ..
Tensile Strength, Ultimate	120 - 130 MPa @Time 1.80e+7 - 7.20e+7 sec	17400 - 18900 psi @Time 5000 - 20000 hour	Average value: 98.0 MPa Grade Count:5
Overview of materials for Polyphthalamide (PPA), Glass Fiber 40% This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, Glass Fiber 40%". Specific grades with glass content between 35% and 44% are included. ..
Tensile Strength, Ultimate	120 MPa @Temperature 1093 °C	17400 psi @Temperature 1999 °F
Haynes 230® alloy, cold rolled and 1232°C solution annealed sheet Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat..