Polymer Property : Tensile Strength, Ultimate = 13100 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	90.0 MPa	13100 psi	ASTM D638
PolyOne Lubri-Tech™ PK-000/15T Polyetheretherketone - 15% PTFE Lubricated  (discontinued **) Data provided by PolyOne.
Tensile Strength, Ultimate	90.0 MPa	13100 psi
Cookson Group Plaskon® 3200LS Mineral Filled Novolac Epoxy Molding Compound  (discontinued **) Test specimens were transfer molded and post cured 4 hours at 175°C.Exhibits exceptional reliability under very stringent testing. This material is designed to minimize stress on the encapsulated ..
Tensile Strength, Ultimate	90.0 MPa	13100 psi	ASTM D638
IDI Composites M-205 Thermoset Polyester, Sheet MECHANICAL - Versatile family of compounds designed to meet a variety of mechanical, electro-mechanical, and corrosion applications. Outstanding structural properties at lowest possible costs.Data p..
Tensile Strength, Ultimate	90.0 MPa	13100 psi
Haysite EHC Glass Reinforced Polyester Sheet, Electrical Grade (GPO1) This IEEE Class F 155ÂºC high strength material exhibits substantial resistance to cold flow or creep under heat and pressure. Suggested applications include motor slot wedges, washers, brush plat..
Tensile Strength, Ultimate	90.0 MPa	13100 psi
Haysite H-193 Corrosion Resistant Polyester/Glass Sheet A fiber glass reinforced thermoset polyester sheet having good corrosion resistance to numerous acids and alkalis. This material also exhibits a high level of flame retardancy and low smoke generati..
Tensile Strength, Ultimate	90.0 MPa @Temperature 22.0 Â°C	13100 psi @Temperature 71.6 Â°F	25mm flat samples, compression moulded; ISO 527-4
Menzolit MenzolitÂ® SMC 0412 Unsaturated Polyester UP SMC 0412 is a premium Class-A SMC for on-line painted conductive exterior body applications on cars. These compounds mould to parts with excellent surface quality and low surface conductivity for e..
Tensile Strength, Ultimate	90.0 MPa	13100 psi
Sawbones E-Glass-Filled Epoxy Sheets Primary UseE-glass-filled epoxy sheets are primarily used as an alternative test medium to human cortical bone.DescriptionE-glass-filled epoxy sheets are a mixture of short e-glass fibers and epoxy ..
Tensile Strength, Ultimate	90.0 MPa	13100 psi
Sawbones Third-Generation Simulated Cortical Bone E-glass-filled EpoxySawbonesÂ® Third-Generation Bones model natural cortical bone using a mixture of short e-glass fibers and epoxy resin pressure injected around a foam core. The mid-shaft area h..
Tensile Strength, Ultimate	90.0 MPa	13100 psi
Sawbones E-Glass-Filled Epoxy Cylinders Primary UseE-glass-filled epoxy cylinders are primarily used as an alternative test medium to human cortical bone.DescriptionThey are a mixture of short e-glass fibers and epoxy resin that has been ..
Tensile Strength, Ultimate	90.0 MPa	13100 psi	ISO 527-1, 2
Polyplastics Duranex® 361SA Polybutylene Terephthalate (PBT), Low density, Low wear, GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers ..
Tensile Strength, Ultimate	90.0 MPa @Temperature 160 °C	13100 psi @Temperature 320 °F	ISO 527-1/-2
DSM Stanyl® OCD2300 BLK PA46-GF50 50% Glass Reinforced, Heat Stabilized
Tensile Strength, Ultimate	90.0 MPa	13100 psi	cond; ISO 527-1/-2
DSM EcoPaXX® Q-KGS6 PA410-GF30 FR 30% Glass Reinforced, Flame Retardant (Halogen free)
Tensile Strength, Ultimate	90.0 MPa	13100 psi
BASF Luranyl® KR 2454/3 G4 Polyphenylene Ether + Styrene-Butadiene Blend, 20% Glass Fiber Reinforced Glass fiber reinforced grade containing halogen-free flame-retardant; for moldings with high heat resistance and stiffness (e.g. relay parts, controller and switch housings).Data was collected by IS..
Tensile Strength, Ultimate	90.0 MPa	13100 psi	ATSM D638
Ashley Polymers Ashlene® 528MS/528SMS Nylon 66, MoS2 Filled A general purpose Molybdenum-disulfide filled nylon resin.Data provided by the manufacturer
Tensile Strength, Ultimate	90.0 MPa	13100 psi	ATSM D638
Ashley Polymers Ashlene® P123WO PBT Polyester, 15% Glass Reinforced PBT polyester with 15% glass reinforcement, flame retardant.Data provided by the manufacturer
Tensile Strength, Ultimate	90.0 - 110 MPa	13100 - 16000 psi	ASTM D638
Chang Chun Plastic PBT4815 Fire Retardant & 15% Glass Fiber Enforced Grade PBT Information provided by Dowell Trading Company Ltd.
Tensile Strength, Ultimate	90.0 MPa	13100 psi	ASTM D638
Chem Polymer Chemlon 140 M Nylon 66, 40% Mineral Reinforced A 40% mineral reinforced nylon 66 exhibiting excellent stiffness in parts where control of warpage is essential.Data provided by the manufacturer, Chem Polymer.
Tensile Strength, Ultimate	90.0 MPa @Temperature 1093 °C	13100 psi @Temperature 1999 °F
ATI Allegheny Ludlum Altemp® HX Nickel-Based superalloy Characteristics: outstanding resistance to oxidation at high temperatures, exceptional strength at elevated temperatures, good fabricability, good machinability in annealed condition, work hardening..
Tensile Strength, Ultimate	90.0 MPa	13100 psi	ASTM D638
A. Schulman ComAlloy Hiloy® 629 Nylon 6/6, Mineral Reinforced Data provided by the manufacturer, ComAlloy International Company.40% Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Tensile Strength, Ultimate	90.0 - 110 MPa	13100 - 16000 psi	ASTM D638
Chang Chun Plastic PBT4115 Fire Retardant & 15% Glass Fiber Enforced Grade PBT Information provided by Dowell Trading Company Ltd.
Tensile Strength, Ultimate	90.0 MPa	13100 psi	ASTM D638
Chem Polymer Chemlon 104-13 G Nylon 66, 13% Glass Fiber Reinforced A toughened, 13% glass fiber reinforced nylon 66 exhibiting improved toughness and ductility, especially dry as molded.Data provided by the manufacturer, Chem Polymer.
Tensile Strength, Ultimate	90.0 - 110 MPa @Temperature 120 - 160 °C	13100 - 16000 psi @Temperature 248 - 320 °F	Average value: 100 MPa Grade Count:1
Overview of materials for Nylon 46, Flame Retarded + Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 46, Flame Retarded + Glass Fiber Reinforced". Each property range of values reported is minimum an..
Tensile Strength, Ultimate	90.0 MPa	13100 psi	ASTM data at 5 mm/min.
BASF Capron® 8331G HI HS BK-102 Impact Modified, 14% Glass-Filled Nylon 6 (Dry)  (discontinued **) Capron 8331G HI HS BK-102 is a black pigmented, heat stabilized, 30% glass reinforced, impact modified polyamide 6 injection molding compound developed for applications requiring improved dry as mol..
Tensile Strength, Ultimate	90.0 MPa	13100 psi	Same value from ASTM and ISO tests; 5 mm/min.
BASF Capron® 8333G HI Impact Modified, 33% Glass-Filled Nylon 6 (Conditioned)  (discontinued **) Capron 8333G HI is a 33% glass reinforced, impact modified polyamide 6 injection molding compound developed for applications requiring improved dry as molded toughness in combination with a balance ..
Tensile Strength, Ultimate	90.0 MPa	13100 psi	ASTM data at 5 mm/min.
BASF Capron® GR20 20% Glass-Filled Nylon 6 (Conditioned)  (discontinued **) Capron GR20 is a 20% glass reinforced polyamide 6 injection molding compound possessing a balance of engineering properties combined with excellent processability and surface aesthetics. It is also..
Tensile Strength, Ultimate	90.0 - 110 MPa	13100 - 16000 psi	Average value: 103 MPa Grade Count:3
Overview of materials for PEKK, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "PEKK, Unreinforced". Each property range of values reported is minimum and maximum values of appropriate..
Tensile Strength, Ultimate	90.0 - 96.0 MPa	13100 - 13900 psi	Typical
ATI Allegheny Ludlum AL 20™ Sheet and Strip Specialty Steel The N08020 alloy has been available for many years and has found applications in many environments, such as in chlorides and in sulfuric and sulfurous acids.Although AL 20 alloy was developed for im..
Tensile Strength, Ultimate	90.0 - 195 MPa	13100 - 28300 psi	Average value: 117 MPa Grade Count:44
Overview of materials for Polyethylene Terephthalate (PET), Glass/Mineral Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), Glass/Mineral Reinforced". Each property range of values reported is m..
Tensile Strength, Ultimate	90.0 MPa @Temperature 200 °C	13100 psi @Temperature 392 °F	ISO 527-1/-2
DSM Stanyl® TS200F6 PA46-GF30 30% Glass Reinforced