Polymer Property : Tensile Strength, Ultimate = 16000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	110 - 191 MPa	16000 - 27700 psi	Average value: 156 MPa Grade Count:11
Overview of materials for Polyaryletherketone (PAEK), Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyaryletherketone (PAEK), Glass Fiber Filled". Each property range of values reported is minimum and m..
Tensile Strength, Ultimate	110 MPa	16000 psi	ISO 527
Solvay TechnylÂ® C 216 Nylon 6, 30% Glass Fiber, EH50 Polyamide PA6, reinforced with 30% of glass fiber, for injection molding.It has good mechanical properties. It is used in all sectors of industry, offering an excellent combination between thermal ..
Tensile Strength, Ultimate	110 MPa	16000 psi	ISO 527
Wellman Wellamid® GF13-66 XE-N 13% Glass Fiber Reinforced Nylon 66, Lubricated & Heat Stabilized Typical Applications: Radio and TV components, dishwasher roller carriages, chain saw oil reservoirs, gears, housings, door & window latches, power hand tool housings, high temperature devices.Data ..
Tensile Strength, Ultimate	110 MPa	16000 psi	ASTM D638
Zhejiang Double Fish YS-G030 30% Long Fiber Glass Reinforced Polypropylene Features high strength, good surface quality, and easy processing. Typical applications include automobile (bumper back beam, arm rest core, instrument panel, mudflap), machinery, electronics, comm..
Tensile Strength, Ultimate	110 MPa	16000 psi	ASTM-D638
Toyobo VYLOPET® EMC320R Polyester Resin VYLOPET® is a polyester resin developed specifically for injection molding. Polyester resins have excellent heat resistance, rigidity, chemical resistance, and electric properties. Grade EMC320R ha..
Tensile Strength, Ultimate	110 MPa	16000 psi	ISO 527-1, 2
Polyplastics Duranex® C5315 Polybutylene Terephthalate (PBT), Higher gloss, Better surface appearance, 15% GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers ..
Tensile Strength, Ultimate	110 MPa	16000 psi	cond; ISO 527-1/-2
DSM Akulon® K224-G6-FC BK00001 PA6-GF30 30% Glass Reinforced, Food Contact Grade
Tensile Strength, Ultimate	110 MPa	16000 psi	cond; ISO 527-1/-2
DSM Akulon® K224-LG6 /E PA6-GF30 30% Glass Reinforced, Injection Molding, Improved UV-stability
Tensile Strength, Ultimate	110 MPa	16000 psi	ISO 527-1/-2
DSM Arnite® TV4 640 (PBT+PC) - GF20 20% Glass Reinforced
Tensile Strength, Ultimate	110 MPa	16000 psi	cond; ISO 527-1/-2
DSM EcoPaXX® Q-X07208 PA410-I-GF30 % Glass Reinforced, Impact Modified
Tensile Strength, Ultimate	110 MPa	16000 psi	cond; ISO 527-1/-2
DSM Novamid® 1010GH30 NAT PA6-GF30 30% Glass Reinforced, Heat Stabilized, Injection Molding
Tensile Strength, Ultimate	110 MPa @Temperature 160 °C	16000 psi @Temperature 320 °F	ISO 527-1/-2
DSM Stanyl® 46HF4530 PA46-GF30 30% Glass Reinforced, Heat Stabilized, High Flow, for E&E applications
Tensile Strength, Ultimate	110 MPa @Temperature 120 °C	16000 psi @Temperature 248 °F	ISO 527-1/-2
DSM Stanyl® OCD2300 BLK PA46-GF50 50% Glass Reinforced, Heat Stabilized
Tensile Strength, Ultimate	110 MPa	16000 psi	dry; ISO 527-1/-2
DSM Stanyl® TS271P4 PA46-MF20 20% Whisker Reinforced, Wear and Friction Modified
Tensile Strength, Ultimate	110 MPa	16000 psi
Cytec Thornel® VCK Carbon Fiber Cloth Data provided by the manufacturer, Amoco Performance Products, Inc.Carbon and graphite cloths, consisting entirely of flexible filaments, are produced by pyrolysis of rayon cloth at high temperature..
Tensile Strength, Ultimate	110 MPa	16000 psi	5 mm/min
Arkema Group Orgalloy® RS 6620 Nylon 66 Alloy, 20% Glass Fiber (Conditioned) RS 66 series, rigid polyamide 66 alloy: easy to process, chemical resistance (no known solvents) and low moisture absorption leading to stability of mechanical, electrical and dimensional propertie..
Tensile Strength, Ultimate	110 MPa	16000 psi	5mm/min; ISO 527
BASF Ultramid® 7423-2 NF3001 13% Glass Filled PA66 (Dry) Ultramid 7423-2 NF3001 is an impact modified, 13% glass reinforced, heat stabilized injection molding PA6/6.
Tensile Strength, Ultimate	110 MPa	16000 psi	ASTM D638
A. Schulman ComAlloy E-16831B Polycarbonate, Electrically Conductive - Carbon Fiber Filled Data provided by the manufacturer, ComAlloy International Company.The ComAlloy product line has been integrated into the A Schulman product line.
Tensile Strength, Ultimate	110 MPa	16000 psi	5 mm/min
Arkema Group Orgalloy® R 6030 Nylon 6 Alloy, 30% Glass fiber (Conditioned) Rigid polyamide 6 alloy: easy to process, low moisture absorption, chemical resistance (no known solvents).Special 30% glass fiber reinforced for overmolding with modified PP.ISO data provided by th..
Tensile Strength, Ultimate	110 MPa	16000 psi	ASTM D638
Adell AJ-14 Nylon 66, 20% Glass Reinforced; High Impact Data provided by Adell Plastics, Inc.
Tensile Strength, Ultimate	110 MPa	16000 psi	5mm/min; ISO 527
BASF Ultramid® B3ZG3 15% Glass Filled PA6 (Dry) Ultramid B3ZG3 is an impact-modified, 15% glass fiber reinforced injection molding PA6 grade.
Tensile Strength, Ultimate	110 MPa	16000 psi	ISO 527-1/-2
DSM Arnite® TV4 241 SL PBT-GF20 FR(17) 20% Glass Reinforced, Flame Retardant, UV Stabilized
Tensile Strength, Ultimate	110 MPa	16000 psi	Same value from ASTM and ISO tests; 5 mm/min.
BASF Capron® HPN 9315G Impact Modified, 15% Glass-Filled Nylon 6 (Dry)  (discontinued **) Capron HPN 9315G is a 15% glass reinforced, impact modified polyamide 6 injection molding grade resin in the High Productivity Nylon Series developed for applications requiring superior dry-as-molde..
Tensile Strength, Ultimate	110 MPa @Temperature 180 °C	16000 psi @Temperature 356 °F	ISO 527-1/-2
DSM Stanyl® TS200F10 PA46-GF50 50% Glass Reinforced