Polymer Property : Tensile Strength, Ultimate = 18900 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	50.0 - 130 MPa @Temperature -20.0 - 100 °C	7250 - 18900 psi @Temperature -4.00 - 212 °F	Average value: 53.1 MPa Grade Count:1
Overview of materials for Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled".Specific grades with glass content between 5% ..
Tensile Strength, Ultimate	50.0 - 130 MPa @Temperature 125 - 275 °C	7250 - 18900 psi @Temperature 257 - 527 °F	Average value: 86.7 MPa Grade Count:1
Overview of materials for Polyetherketoneetherketoneketone (PEKEKK), Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetherketoneetherketoneketone (PEKEKK), Glass Fiber Filled". Each property range of values reported i..
Tensile Strength, Ultimate	73.0 - 130 MPa	10600 - 18900 psi	Average value: 106 MPa Grade Count:4
Overview of materials for PCT, 40% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "PCT, 40% Glass Reinforced". Specific grades with glass content between 35% and 44% are included. Each pr..
Tensile Strength, Ultimate	57.0 - 130 MPa	8270 - 18900 psi	Average value: 104 MPa Grade Count:23
Overview of materials for PBT + ASA Blend, Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "PBT + ASA Blend, Glass Fiber Reinforced". Each property range of values reported is minimum and maximum ..
Tensile Strength, Ultimate	86.0 - 130 MPa	12500 - 18900 psi	Average value: 111 MPa Grade Count:16
Overview of materials for Polyphenylene Sulfide (PPS) with 20% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 20% Glass Fiber Filler". Specific grades with glass content between 15%..
Tensile Strength, Ultimate	130 - 130 MPa @Temperature 130 - 175 °C	18900 - 18900 psi @Temperature 266 - 347 °F	Average value: 147 MPa Grade Count:1
Overview of materials for Nylon 66, 60% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 60% Glass Fiber Filled". Specific grades with glass content between 55% and 64% are included. ..
Tensile Strength, Ultimate	130 - 130 MPa @Time 1.80e+7 - 7.20e+7 sec	18900 - 18900 psi @Time 5000 - 20000 hour	Average value: 147 MPa Grade Count:1
Overview of materials for Nylon 66, 60% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 60% Glass Fiber Filled". Specific grades with glass content between 55% and 64% are included. ..
Tensile Strength, Ultimate	44.0 - 130 MPa	6380 - 18900 psi	Average value: 66.4 MPa Grade Count:15
Overview of materials for Nylon 612, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 612, Unreinforced". Each property range of values reported is minimum and maximum values of approp..
Tensile Strength, Ultimate	20.0 - 130 MPa @Temperature -40.0 - 120 °C	2900 - 18900 psi @Temperature -40.0 - 248 °F	Average value: 58.7 MPa Grade Count:11
Overview of materials for Nylon 6, Unreinforced, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Unreinforced, Flame Retardant". Each property range of values reported is minimum and maximum v..
Tensile Strength, Ultimate	120 - 130 MPa @Temperature 130 - 180 °C	17400 - 18900 psi @Temperature 266 - 356 °F	Average value: 98.0 MPa Grade Count:5
Overview of materials for Polyphthalamide (PPA), Glass Fiber 40% This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, Glass Fiber 40%". Specific grades with glass content between 35% and 44% are included. ..
Tensile Strength, Ultimate	120 - 130 MPa @Time 1.80e+7 - 7.20e+7 sec	17400 - 18900 psi @Time 5000 - 20000 hour	Average value: 98.0 MPa Grade Count:5
Overview of materials for Polyphthalamide (PPA), Glass Fiber 40% This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, Glass Fiber 40%". Specific grades with glass content between 35% and 44% are included. ..
Tensile Strength, Ultimate	6.89 - 130 MPa	1000 - 18900 psi	Average value: 80.8 MPa Grade Count:184
Overview of materials for Polypropylene with 30% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 30% Glass Fiber Filler". Specific grades with glass content between 25% and 34% are i..
Tensile Strength, Ultimate	0.750 - 130 MPa	109 - 18900 psi	Average value: 13.4 MPa Grade Count:541
Overview of materials for Thermoset Fluoroelastomer This property data is a summary of similar materials in the MatWeb database for the category "Thermoset Fluoroelastomer". Each property range of values reported is minimum and maximum values of appr..
Tensile Strength, Ultimate	40.7 - 130 MPa	5900 - 18900 psi	Average value: 66.1 MPa Grade Count:38
Overview of materials for Polybutylene Terephthalate (PBT), Glass Bead Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Glass Bead Filled". Each property range of values reported is minimum ..