Polymer Property : Tensile Strength, Ultimate = 34.5 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	34.5 MPa	5000 psi
Mykroy/Mycalex MM 600 Machining Grade Glass-bonded Mica Composite Formerly known as grade MM 1100. Synthetic mica filler. Does not burn. Excellent radiation resistance (3 x 10^10 Rads-Cobalt).This ceramoplastic material is a versatile and efficient insulating m..
Tensile Strength, Ultimate	34.5 MPa	5000 psi	ASTM D412
MF-5062 Polyurethane-based Biomedical Elastomer
Tensile Strength, Ultimate	34.5 MPa	5000 psi	TM R050-36
Resinlab® SEC1244 Silver Filled Epoxy Adhesive Resinlab™ SEC1244 is a silver filled, two component, elevated temperature curing epoxy adhesive. It provides excellent electrical conductivity useful in many electronic applications. It is a smooth..
Tensile Strength, Ultimate	34.5 - 90.0 MPa	5000 - 13100 psi	Average value: 52.7 MPa Grade Count:35
Overview of materials for Polyphenylene Ether, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, Molded". Each property range of values reported is minimum and maximum values of ap..
Tensile Strength, Ultimate	34.5 - 74.0 MPa	5000 - 10700 psi	Average value: 54.2 MPa Grade Count:7
Overview of materials for Polyphenylene Ether, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, Impact Grade". Each property range of values reported is minimum and maximum values..
Tensile Strength, Ultimate	34.5 - 48.3 MPa	5000 - 7000 psi	ASTM D638
Arkema Group Kynar Flex® 3120 PVDF Copolymer  (discontinued **) Copolymer Series, Kynar® components are used extensively in the high purity semiconductor market, the pulp and paper industry, nuclear waste processing, and the general chemical processing industry..
Tensile Strength, Ultimate	34.5 MPa	5000 psi	ASTM D638
Premix Premi-Glas® 8105 Glass Reinforced Polyester BMC  (discontinued **) Description: Premi-Glas® 8105 is a glass reinforced thermoset polyester Bulk Molding Compound designed for injection molding of automotive forward lighting reflectors. Key features and benefits: Ex..
Tensile Strength, Ultimate	34.5 MPa	5000 psi	Machine direction
Spartech CentrexÂ® R83/21 ABS Weather Resistant Sheet Data provided by the manufacturer.
Tensile Strength, Ultimate	34.5 MPa @Temperature 260 Â°C	5000 psi @Temperature 500 Â°F	ASTM D638
Saint-Gobain MeldinÂ® 7021 Direct Formed Graphite Filled Polyimide Finished parts and basic shapes made from 15% by weight graphite filled polyimide material for applications high wear resistance, good thermal oxidative stability, and high temperature resistance. ..
Tensile Strength, Ultimate	34.5 MPa	5000 psi	ASTM Data
Styron Magnumâ„¢ 8325 ABS, Sheet Coextrusion Grade MAGNUMÂ® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM ..
Tensile Strength, Ultimate	34.5 MPa	5000 psi	ASTM Data
Styron Magnumâ„¢ 9450P ABS, High Gloss MAGNUMÂ® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM ..
Tensile Strength, Ultimate	34.5 MPa	5000 psi	ASTM Data
Styron Magnumâ„¢ 9700HF ABS MAGNUMÂ® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM ..
Tensile Strength, Ultimate	34.5 MPa	5000 psi	ASTM Data
Styron Magnumâ„¢ 213 ABS, General Purpose MAGNUMÂ® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM ..
Tensile Strength, Ultimate	34.5 MPa	5000 psi	ASTM D412
Lubrizol Estane® 2103-84AEN Thermoplastic Polyurethane Elastomer Formerly PellethaneFeature: Contains UV Stabilizer, NSF Standard 61 certifiedAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Pelletha..
Tensile Strength, Ultimate	34.5 MPa	5000 psi	ASTM D638
Ecomass® 1066ZD96 Tungsten Filled Polyamide Nontoxic alternative to Lead (Pb), weighting and balancing applicationsHigh Specific GravityTungsten Powder Filled Polyamide (PA) AlloyGood ToughnessInformation provided by Technical Polymers
Tensile Strength, Ultimate	34.5 MPa	5000 psi	after optimum cure
Armstrong A-2/H20 Epoxy Adhesive This off-white paste epoxy is a versatile adhesive systems. The choice of one of four recommended Activators (A, E, W or H-20) makes A-2 Adhesive an ideal choice for many applications. A-2 with Ac..
Tensile Strength, Ultimate	34.5 - 48.3 MPa	5000 - 7000 psi
Bulk Molding Compounds BMC 102 Glass Filled Thermoset Polyester BMC 102 is a medium strength, glass fiber reinforced molding compound that meets Ford Specification ESF-M3D56-A. It can be supplied in bulk or extruded in pre-weighed slugs and is well suited for in..
Tensile Strength, Ultimate	34.5 - 48.3 MPa	5000 - 7000 psi
Bulk Molding Compounds BMC 2270 Mineral Filled, Glass Reinforced Polyester BMC 2270 molding compound is a mineral filled, glass-fiber-reinforced polyester compound suitable for compression and transfer molding. It is a general purpose material with medium impact strength a..
Tensile Strength, Ultimate	34.5 - 48.3 MPa	5000 - 7000 psi
Bulk Molding Compounds BMC 600 Mineral Filled, Glass Fiber Reinforced Polyester Compound BMC 600 molding compound is a mineral filled glass-fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding. It is a general purpose material with medium ..
Tensile Strength, Ultimate	34.5 - 48.3 MPa	5000 - 7000 psi
Bulk Molding Compounds BMC 600LS Mineral Filled, Glass Fiber Reinforced Polyester Compound BMC 600LS molding compound is a low-shrink, Mineral filled, glass-fiber-reinforced polyester compound suitable for compression, transfer and stuffer injection molding It is a general purpose materia..
Tensile Strength, Ultimate	34.5 MPa @Temperature 871 °C	5000 psi @Temperature 1600 °F
ATI Allegheny Ludlum AL 468™ Dual Stabilized- Low Titanium Stainless Steel Characteristics:good corrosion resistance in a wide range of environments, can be used in annealed cold formed or as-welded conditions. Applications: used in place of Type 304 in an oxidizing when ..
Tensile Strength, Ultimate	34.5 - 55.2 MPa	5000 - 8000 psi
Bulk Molding Compounds BMC 400 Thermoset Polyester, Low Shrink, High Strength, Electrical Grade BMC 400 is a high strength, low shrink molding compound. It can be supplied in bulk or extruded in pre-weighted slugs.Typical applications are circuit breakers, insulators, and power tool housings.
Tensile Strength, Ultimate	34.5 - 55.2 MPa	5000 - 8000 psi
Bulk Molding Compounds BMC 620 Mineral Filled, Glass Fiber Reinforced Polyester Compound BMC 620 molding compound is a mineral filled, glass fiber-reinforced polyester compound suitable for compression, and stuffer injection molding It is characterized by good moldability high impact st..
Tensile Strength, Ultimate	34.5 - 41.4 MPa	5000 - 6000 psi
Bulk Molding Compounds BMC 900 Thermoset Polyester, Soft Flow Encapsulation Grade BMC 900 is an encapsulation grade, soft flow material. As with all other BMCI compounds, this series can be supplied in logs, slugs or bulk.Typical applications are electrical coil encapsulations an..
Tensile Strength, Ultimate	34.5 - 72.0 MPa	5000 - 10400 psi	Average value: 48.7 MPa Grade Count:7
Overview of materials for Polypropylene with Glass Fiber + Bead Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with Glass Fiber + Bead Filler". Each property range of values reported is minimum and max..
Tensile Strength, Ultimate	34.5 MPa	5000 psi	ASTM Data
Styron Magnum™ 9025 ABS, High Gloss MAGNUM® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM AB..
Tensile Strength, Ultimate	34.5 MPa	5000 psi	ASTM D412
MF-5056 Polyurethane-based Biomedical Elastomer