Polymer Property : Shear Strength = 10.3 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Shear Strength	10.3 - 17.2 MPa	1500 - 2500 psi
ND Industries 533 Retaining Compound High strength sealing applications for non migration material
Shear Strength	>= 10.3 MPa	>= 1500 psi	Lap
Parker Chomerics CHO-BOND 592 Conductive Epoxy Highly conductive silver-filled epoxy adhesive which combines the best properties of metals and organics. This two-component system is unique in that it combines long pot life, good electrical condu..
Shear Strength	10.3 MPa	1500 psi	Cured 6 minutes at 130°C, Al/Al
Resin Technology Group TIGA 905 One-Part Silver Conductive Epoxy System Cure 6 minutes at 130°C or 3 minutes at 150°C.TIGA 905 is a stress-absorbing and electrically conductive, silver-filled epoxy adhesive recommended for solder replacement in microelectronic interco..
Shear Strength	>= 10.3 MPa	>= 1500 psi	Cured 10 minutes at 120°C, Al/Al (etched)
Resin Technology Group TIGA 951 One-Part Silver Conductive Epoxy System Cure 10 minutes at 120°CTIGA 951 is an electrically conductive, silver-filled epoxy adhesive recommended for electronic bonding and sealing applications. This one-part, smooth paste formulation of ..
Shear Strength	10.3 - 13.8 MPa	1500 - 2000 psi
ITW Plexus Plexusâ„¢ MA320 Methacrylate Adhesive Two-part adhesive designed for structural bonding of thermoplastic, metal, and composite assemblies.Excellent low temperature and toughness properties.Information provided by Illinois Tool Works.
Shear Strength	10.3 - 13.8 MPa	1500 - 2000 psi
ITW Plexus Plexusâ„¢ MA3940 Methacrylate Adhesive Two-part adhesive designed for structural bonding of thermoplastic, metal, and composite assemblies.Use with craze sensitive plastics.Information provided by Illinois Tool Works.
Shear Strength	10.3 - 12.4 MPa	1500 - 1800 psi
ITW Plexus Plexusâ„¢ MA422 Methacrylate Adhesive Two-part adhesive designed for structural bonding of thermoplastic, metal, and composite assemblies.All purpose adhesive, medium open time.Information provided by Illinois Tool Works.
Shear Strength	10.3 - 12.4 MPa	1500 - 1800 psi
ITW Plexus Plexusâ„¢ MA425 Methacrylate Adhesive Two-part adhesive designed for structural bonding of thermoplastic, metal, and composite assemblies.All purpose adhesive, long open time.Information provided by Illinois Tool Works.
Shear Strength	10.3 - 13.8 MPa	1500 - 2000 psi
ITW Plexus Plexusâ„¢ MA920 Methacrylate Adhesive Two-part adhesive designed for structural bonding of thermoplastic, metal, and composite assemblies.All purpose, low odor, short open time.Information provided by Illinois Tool Works.
Shear Strength	>= 10.3 MPa	>= 1500 psi	Bond, Al to Al, After 30 days at 400°F
Master Bond Supreme 33 High Temperature Resistant, Structural Adhesive Description: Master Bond Polymer System Supreme 33 is a unique, room temperature curing, toughened epoxy adhesive/sealant, offering high temperature resistance. This innovative system offers high bo..
Shear Strength	10.3 MPa	1500 psi	Lap
Epoxy Technology EPO-TEK® H20E-LV Electrically Conductive, Silver Epoxy Product Description: EPO-TEK® H20E-LV is a two component, 100% solids silver-filled epoxy system designed specifically for chip bonding in microelectronic and optoelectronic applications. It is a ..
Shear Strength	10.3 MPa @Temperature -55.0 °C	1500 psi @Temperature -67.0 °F	Overlap, Steel Solvent Wipe; ASTM D1002-72
3M Scotch-Weld™ 1751 B/A Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive 1751 B/A is a gray, aluminum filled, two-part, room temperature curing structural adhesive.Information provided by 3M
Shear Strength	10.3 MPa @Temperature -55.0 °C	1500 psi @Temperature -67.0 °F	Aluminum Overlap; ASTM D1002
3M Scotch-Weld™ 183 B/A Green Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive 1838 B/A is a controlled flow product. This epoxy adhesives are two-part, room temperature curing structural adhesives with high shear strengths and excellent envir..
Shear Strength	10.3 MPa	1500 psi	Overlap, Fiberglass
3M Scotch-Weld™ DP100 Plus Clear Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP100 Plus Clear is a fast setting, two-part, 1:1 mix ratio mercaptan-cured epoxy adhesive. It is a unique among fast setting mercaptan cure epoxies in that it comb..
Shear Strength	10.3 MPa	1500 psi	Overlap, Sanded Aluminum
3M Scotch-Weld™ DP190 Gray Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP190 Gray is a 1:1 mix ratio similar to Scotch-Weld™ Epoxy Adhesive 2216 B/A Gray and exhibits good peel, shear and environmental aging properties.Information pro..
Shear Strength	10.3 MPa	1500 psi	Overlap, PP, Cohesive Failure
3M Scotch-Weld™ DP8010 Structural Adhesive 3M™ Scotch-Weld™ Structural Plastic Adhesive DP-8010 is a two-part acrylic-based adhesive (10:1 ratio by volume) that can bond many low surface energy plastics, including many grades of Polypropyl..
Shear Strength	10.3 MPa	1500 psi	Overlap, Phenolic (IPA/abrade/IPA), Substrate Failure; ASTM D1002
3M Scotch-Weld™ DP920 Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP920 is a two-part, 2:1 mix ratio, toughened epoxy structural adhesive with a 20 minute work life. It exhibits excellent shear and peel strengths along with good i..
Shear Strength	10.3 MPa	1500 psi	Overlap, CRS-MEK/abrade/MEK-Adhesive/Cohesive Failure; ASTM D1002
3M Scotch-Weld™ LSB90 Flexible Epoxy 3M™ Scotch-Weld™ Epoxy Adhesive LSB90 is a high performance, two-part, flexible epoxy adhesive offering high shear and peel adhesion and very high levels of durability. It has a 90 minute worklife..
Shear Strength	10.3 MPa	1500 psi	Overlap, Steel; ASTM D1002-64
3M Scotch-Weld™ CA40H Instant Adhesive 3M™ Scotch-Weld™ Instant Adhesives are single component, high strength cyanoacrylate adhesives. Higher viscosity version of CA40 and better void filling capabilities.Information provided by 3M
Shear Strength	10.3 MPa	1500 psi	Overlap, Aluminum; ASTM D1002-64
3M Scotch-Weld™ CA40H Instant Adhesive 3M™ Scotch-Weld™ Instant Adhesives are single component, high strength cyanoacrylate adhesives. Higher viscosity version of CA40 and better void filling capabilities.Information provided by 3M
Shear Strength	10.3 MPa	1500 psi	Overlap, Sanded Aluminum
3M Scotch-Weld™ DP-105 Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP105 Clear is a fast setting, very flexible 1:1 mix ratio epoxy adhesive/sealant. Its flexibility when cured makes it ideal for applications involving dissimilar s..
Shear Strength	10.3 MPa	1500 psi	Overlap, 71°C 100% RH for 14 days, Mixed Mode of AF&CF
3M Scotch-Weld™ DP810 Tan Structural Adhesive 3M™ Scotch-Weld™ Low-Odor Acrylic Adhesives are two-part, 1:1 mix ratio, toughened structural adhesives with less odor than most acrylic adhesives. The adhesives have excellent shear and peel stre..
Shear Strength	10.3 MPa	1500 psi	Overlap at 20 minutes after bonding
3M Scotch-Weld™ DP810 Tan Structural Adhesive 3M™ Scotch-Weld™ Low-Odor Acrylic Adhesives are two-part, 1:1 mix ratio, toughened structural adhesives with less odor than most acrylic adhesives. The adhesives have excellent shear and peel stre..
Shear Strength	10.3 MPa	1500 psi	Overlap, CRS/CRS after 7 days of Immersion in Gasoline
3M Scotch-Weld™ DP820 Acrylic Adhesives 3M™ Scotch-Weld™ Acrylic Adhesive DP820 is a two-part, 1:1 mix ratio, toughened acrylic structural adhesives. They exhibit excellent shear and peel strengths along with good impact and durability ..
Shear Strength	10.3 MPa	1500 psi	Overlap, FR-4/FR-4 tested after tap water 1 wk/RT
3M Scotch-Weld™ DP820 Acrylic Adhesives 3M™ Scotch-Weld™ Acrylic Adhesive DP820 is a two-part, 1:1 mix ratio, toughened acrylic structural adhesives. They exhibit excellent shear and peel strengths along with good impact and durability ..
Shear Strength	10.3 MPa @Temperature 81.0 - 83.0 °C	1500 psi @Temperature 178 - 181 °F	Stored 1 year, 22-26°C, Minimum MIL-A-8623 Type III Requirement
3M Scotch-Weld™ EC-1386 Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive EC-1386 is a one-part, 100% solids, thermosetting liquid adhesive.Information provided by 3M
Shear Strength	10.3 MPa @Temperature -55.0 °C	1500 psi @Temperature -67.0 °F	Aluminum Overlap; ASTM D1002
3M Scotch-Weld™ 3501 B/A Gray Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive 3501 B/A Gray is a rapid room temperature curing, two-part epoxy adhesives for use in bonding many metals, wood, and a variety of plastics. Equal parts by volume ar..
Shear Strength	10.3 MPa	1500 psi	Overlap, Stainless Steel/Stainless Steel
3M Scotch-Weld™ DP110 Translucent Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP110 Translucent and Gray are two-part epoxy adhesive which combine a fast cure with flexibilityInformation provided by 3M
Shear Strength	10.3 MPa	1500 psi	Overlap, Galvanized Steel/Galvanized Steel
3M Scotch-Weld™ DP110 Translucent Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP110 Translucent and Gray are two-part epoxy adhesive which combine a fast cure with flexibilityInformation provided by 3M
Shear Strength	10.3 MPa	1500 psi	Overlap, Copper/Copper
3M Scotch-Weld™ DP110 Translucent Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP110 Translucent and Gray are two-part epoxy adhesive which combine a fast cure with flexibilityInformation provided by 3M