Polymer Property : Tensile Creep Modulus, 1000 hours = 1500 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Tensile Creep Modulus, 1000 hours	1500 MPa @Temperature 23.0 °C	218000 psi @Temperature 73.4 °F	ISO 899
DuPont Performance Polymers Delrin® FG900P NC010 Acetal Homopolymer  (Unverified Data**) Delrin® FG900P is a low viscosity acetal homopolymer, with improved thermal stability. It has been developed for consideration into applications such as parts for the food industry.Information prov..
Tensile Creep Modulus, 1000 hours	1500 MPa	218000 psi
Arkema Group Oroglas® MI-4T Acrylic, Heat Resistant  (discontinued **) OROGLAS MI-4T is an acrylic grade that associates improved impact resistance with high heat resistance.Key features improved impact resistance: up to 4 times more impact resistant than standard acr..
Tensile Creep Modulus, 1000 hours	1500 MPa	218000 psi	ISO 899
Aardvark Polymers AARTELÂ® 2000 Rotational Molding Resin AartelÂ® 2000 POM is a premium homopolymer acetal for rotational molding applications. AartelÂ® 2000 offers high performance properties and is a high flow, fast cycling polymer.Information prov..
Tensile Creep Modulus, 1000 hours	1500 MPa	218000 psi	ISO 899-1
Lanxess PocanÂ® S 7926 000000 PBT PBT, non-reinforced, injection molding, extrusion, flame retardant, impact modified
Tensile Creep Modulus, 1000 hours	1500 MPa	218000 psi
Styrolution NOVODURÂ® P2H-AT ABS, Injection Grade Standard injection molding grade, easy flow, high gloss, hard, antistatic.Applications: Telephones, household goods, video and audio industry, office equipment.
Tensile Creep Modulus, 1000 hours	1500 MPa	218000 psi
Covestro Bayblend® T 45 MN Polycarbonate/ABS Blend High impact and notched impact strength, little risk of brittle fracture, high dimensional accuracy, good platable.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was sep..
Tensile Creep Modulus, 1000 hours	1500 MPa @Temperature 23.0 °C	218000 psi @Temperature 73.4 °F	ISO 899
DuPont Performance Polymers Delrin® 300PE NC010A Acetal Homopolymer Delrin® 300PE NC010A is a medium-high viscosity acetal homopolymer, an enhanced version with extremely low VOC emissions. It has improved processing thermal stability, good mechanical properties, a..
Tensile Creep Modulus, 1000 hours	1500 MPa @Temperature 23.0 °C	218000 psi @Temperature 73.4 °F	ISO 899
DuPont Performance Polymers Delrin® 100PE NC010A Acetal Homopolymer Delrin® 100PE NC010A is a high viscosity acetal homopolymer, an enhanced version of Delrin® 100P with extremely low VOC emissions. It has improved processing thermal stability, good mechanical pro..
Tensile Creep Modulus, 1000 hours	1500 MPa @Strain <=0.500 %	218000 psi @Strain <=0.500 %	ISO 899-1
BASF Ultramid® B3UG4 BK 23215 20% Glass Filled PA66 FR (Conditioned) Description: Halogen-free and phosphorus free flame retardant injection-molding grade with outstanding free-flow properties, good electrical properties and low smoke density; resistant to glow wire..
Tensile Creep Modulus, 1000 hours	1500 - 1900 MPa	218000 - 276000 psi	Average value: 1770 MPa Grade Count:3
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Molded This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Molded". Each property range of values reported is minimum and ma..
Tensile Creep Modulus, 1000 hours	1500 MPa @Temperature 23.0 °C	218000 psi @Temperature 73.4 °F	ISO 899
DuPont Performance Polymers Delrin® FG100P NC010 Acetal Homopolymer  (Unverified Data**) Delrin® FG100P is a high viscosity acetal homopolymer, with improved thermal stability for use in easy to fill molds. It has been developed for consideration into applications such as parts for the..