Polymer Property : Flexural Modulus = 11.7 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	11.7 GPa	1700 ksi	ASTM D790
Premix Premi-Glas® 3101-25 Polyester BMC Premi-Glas® 3101-25 is a 25% glass reinforced thermoset Bulk Molding Compound designed for electrical and flame retardant applications. Key features and benefits are: Underwriters Laboratories, UL ..
Flexural Modulus	11.7 - 31.0 GPa	1700 - 4500 ksi	Average value: 22.6 GPa Grade Count:17
Overview of materials for Liquid Crystal Polymer (LCP), Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), Carbon Fiber Filled". Each property range of values reported is minimum an..
Flexural Modulus	11.7 - 22.8 GPa	1700 - 3300 ksi	Average value: 18.1 GPa Grade Count:46
Overview of materials for Nylon 66, 60% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 60% Glass Fiber Filled". Specific grades with glass content between 55% and 64% are included. ..
Flexural Modulus	11.7 GPa	1700 ksi	ISO 178
SABIC Innovative Plastics LNP THERMOCOMP EF006ER PEI LNP* Thermocomp* EF006ER is a compound based on Polyetherimide resin containing 30% Glass Fiber. Added features of this material include: Easy Molding, Mold Release.
Flexural Modulus	11.7 GPa	1700 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP RX00713H PA 66 LNP* Thermocomp* RX00713H is a compound based on Nylon 6/6 containing proprietary fillers. Characteristics of this grade are: Healthcare.
Flexural Modulus	11.7 GPa	1700 ksi	ASTM D790
Sumitomo Bakelite North America E 9405H-1 Glass Filled Electrical Encapsulation Grade Epoxy E-9504H-1 is glass fiber filled epoxy molding compound designed for encapsulation of delicate electrical components as well as large coils. Excellent thermal shock, moldability, and retention of ele..
Flexural Modulus	11.7 GPa	1700 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL GFN1740V PPE+PS (Europe-Africa-Middle East) Noryl* GFN1740V Polyphenylene Oxide (PPO) + Polystyrene (PS) resin is a 40 % Glass Reinforced, injection moldable grade with improved hydrolytic stability and with a Tensile Modulus > 11000 MPa; thi..
Flexural Modulus	11.7 GPa	1700 ksi	ASTM D790
PlastxWorld CEVIAN® B6528 40% GF PBT/ABS Alloy Glass fiber and mineral filled, low warpage and flame retarded PBT/ABS.Information provided by PlastxWorld Inc.
Flexural Modulus	11.7 GPa	1700 ksi	ASTM D790
Chase Plastics CP Pryme® N340HL (Dry) Nylon 6, 40% Glass Fiber Reinforced, Heat Stabilized, Lubricated, Recycled Content Features: Heat stabilizedLubricatedRecycled contentForm: PelletsInformation provided by Chase Plastics.
Flexural Modulus	11.7 GPa	1700 ksi	ASTM D790
A. Schulman SCHULAMID® 66 GF40H 40% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman.
Flexural Modulus	11.7 - 12.4 GPa	1700 - 1800 ksi
Bulk Molding Compounds BMC T15(GP) General Purpose Molding Compound BMC T15(GP) is a high strength, low shrink general purpose molding compound. Due to the excellent flow and controlled reactivity, BMC T15(GP) is well suited for a variety of applications. It is av..
Flexural Modulus	11.7 - 13.1 GPa	1700 - 1900 ksi
Bulk Molding Compounds BMC 1401 Encapsulating Material, Electrical Grade BMC 1401 is an electrical grade of encapsulating material characterized by a balance of soft flow and cure rate to ensure complete and proper encapsulation without voiding. Generally too soft for co..
Flexural Modulus	11.7 - 13.1 GPa	1700 - 1900 ksi
Bulk Molding Compounds BMC 300 Mineral Filled, Glass Reinforced Polyester BMC 300 is a general purpose, mineral filled, glass fiber-reinforced polyester that is suitable for compression, transfer and stuffer injection molding. Our Granite-X series of molding compounds bel..
Flexural Modulus	11.7 GPa	1700 ksi	Crosswise; ASTM D790
G-5 Fiberglass Melamine Laminate Sheet This material is very hard, flame resistant, and has excellent electrical properties. G-5 has high arc and heat resistance. It used for switch board panels, arc barriers, circuit breaker parts, and ..
Flexural Modulus	11.7 GPa	1700 ksi	ISO 178
SABIC Innovative Plastics LNP VERTON NV008E PC/ABS (Asia Pacific) LNP* Verton* NV008E is a compound based on PC/ABS resin containing Long Glass Fiber. Added features of this material include: Easy Molding.
Flexural Modulus	11.7 GPa	1700 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL FE1740PW PPE+PS (Europe-Africa-Middle East) Noryl* FE1740PW Polyphenylene Oxide (PPO) + Polystyrene (PS) resin is a 40 % Glass Reinforced, injection moldable grade with improved hydrolytic stability and with a Tensile Modulus > 11000 MPa; thi..
Flexural Modulus	11.7 GPa	1700 ksi	Tangent; ISO 178
Premix Premi-Glas® 1281-32 VE Glass Reinforced Vinyl Ester SMC  (discontinued **) Description: Premi-Glas® 1281-32 VE SMC is a high strength glass reinforced vinyl ester sheet molding compound formulated for under-the-hood automotive applications. Key features and benefits: Desi..