Polymer Property : Flexural Modulus = 9.00 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	7.00 - 9.00 GPa	1020 - 1310 ksi	Injection; ISO 178
Raschig Group DECAL® 1760 Phenolic Glass-fiber reinforced phenolic molding compound. Very good electrical properties, good chemical resistance and mechanical properties. This product meets the allowed upper limits for heavy metals an..
Flexural Modulus	6.00 - 9.00 GPa	870 - 1310 ksi	Compression; ISO 178
Raschig Group DECAL® 666/8 Phenolic Glass-fiber reinforced phenolic molding compound with mineral fillers. High heat resistance, reduced mould shrinkage and post-shrinkage, good chemical resistance and mechanical properties. This prod..
Flexural Modulus	8.00 - 9.00 GPa	1160 - 1310 ksi	Injection and Compression; ISO 178
Raschig Group MELOPAS® 2010 MF Melamine Organically and inorganically filled Melamine molding compound. Excellent surface hardness, good mechanical strength, good electrical properties. This product meets the allowed upper limits for heav..
Flexural Modulus	8.00 - 9.00 GPa	1160 - 1310 ksi	Injection and Compression; ISO 178
Raschig Group MELOPLAS® 150 MF Wood flour-reinforced MF molding compound in dark colors. High surface hardness, high mechanical strength, good electrical properties. Self-extinguishing (V-O/1,6 according to UL 94), UL-listed. Fr..
Flexural Modulus	8.00 - 9.00 GPa	1160 - 1310 ksi	Injection and Compression; ISO 178
Raschig Group MELOPLAS® 152 MF Cellulose-reinforced MF molding compound in white and colored shades. Very good electrical properties, high surface hardness, good abrasion- and UV-stability, very good resistance to chemicals - al..
Flexural Modulus	8.00 - 9.00 GPa	1160 - 1310 ksi	Injection and Compression; ISO 178
Raschig Group MELOPLAS® 152.7 MF Cellulose-reinforced MF molding compound in white and colored shades. High surface hardness, very good UV stability, very good resistance to chemicals also to foodstuff ingredients, physiologically..
Flexural Modulus	7.00 - 9.00 GPa	1020 - 1310 ksi	Injection and Compression; ISO 178
Raschig Group MELOPLAS® 181 MF Cellulose-reinforced, phenol-modified MF molding compound (MPF) in white and colored shades. High surface hardness, good electrical properties, good mechanical strength, high UV and heat resistanc..
Flexural Modulus	8.00 - 9.00 GPa	1160 - 1310 ksi	Injection and Compression; ISO 178
Raschig Group MELOPLAS® 181.5 MF Cellulose-reinforced, phenol-modified MF molding compound (MPF) in white and colored shades. Very good electrical properties, high surface hardness, good mechanical strength, high UV and heat resis..
Flexural Modulus	7.00 - 9.00 GPa	1020 - 1310 ksi	Compression; ISO 178
Raschig Group MELOPLAS® 182 MF Wood flour-reinforced and inorganically filled, phenol-modified MF molding compound (MPF) in dark colors. Improved dimensional stability and electrical properties as compared with MP 180, high surf..
Flexural Modulus	8.00 - 9.00 GPa	1160 - 1310 ksi	Injection and Compression; ISO 178
Raschig Group MELOPLAS® 183 MF Cellulose-reinforced and inorganically filled, phenol-modified MF molding compound (MPF) in white and colored shades. Improved dimensional stability and electrical properties as compared with MP 18..
Flexural Modulus	7.00 - 9.00 GPa	1020 - 1310 ksi	Injection and Compression; ISO 178
Raschig Group MELOPLAS® 3025 MF Cellulose-reinforced and inorganically filled MF molding compound in white and colored shades. High surface hardness, good UV and heat stability, very good resistance to chemicals - also to foodstu..
Flexural Modulus	6.00 - 9.00 GPa	870 - 1310 ksi	Compression; ISO 178
Raschig Group RALUPOL® 2100 UP Polyester Organically and inorganically filled polyester molding compound. Low post-shrinkage, very good electrical values, good mechanical strength. This product meets the allowed upper limits for heavy meta..
Flexural Modulus	0.373 - 9.00 GPa	54.0 - 1310 ksi	Average value: 4.01 GPa Grade Count:61
Overview of materials for Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled".Specific grades with glass content between 5% ..
Flexural Modulus	2.60 - 9.00 GPa	377 - 1310 ksi	Average value: 4.96 GPa Grade Count:18
Overview of materials for Polyetherimide (PEI), 10% Glass Fiber This property data is a summary of similar materials in the MatWeb database for the category "Polyetherimide, 10% Glass Fiber". Specific grades with glass content between 5% and 14% are included. Ea..
Flexural Modulus	6.80 - 9.00 GPa	986 - 1310 ksi	Average value: 7.82 GPa Grade Count:31
Overview of materials for Phenolic, Novolac, Woodflour Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Woodflour Filled". Each property range of values reported is minimum and maximum valu..
Flexural Modulus	1.80 - 9.00 GPa	261 - 1310 ksi	Average value: 4.94 GPa Grade Count:10
Overview of materials for Nylon 6, Mineral Reinforced, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Mineral Reinforced, Impact Grade". Each property range of values reported is minimum and maximu..
Flexural Modulus	2.76 - 9.00 GPa	400 - 1310 ksi	Average value: 5.00 GPa Grade Count:14
Overview of materials for Nylon 66, Mineral Filled, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Mineral Filled, Impact Grade". Each property range of values reported is minimum and maximum v..
Flexural Modulus	7.50 - 9.00 GPa	1090 - 1310 ksi	ISO 178
Vyncolit 2923 W Novolac Phenolic Mineral filled phenolic molding compound with excellent heat resistance and dimensional stability.Information provided by Vyncolit, a Sumitomo Bak Group
Flexural Modulus	7.00 - 9.00 GPa	1020 - 1310 ksi	ISO 178
Vyncolit 4451 XB Novolac Phenolic Organic and mineral filled phenolic molding compound with excellent mechanical properties (highest notched impact strength).USES: Fuse holders, brush holders, circuit breakers, automotive ignition a..
Flexural Modulus	7.50 - 9.00 GPa	1090 - 1310 ksi	ISO 178
Vyncolit 2950 W Novolac Phenolic Mineral and glass fiber filled phenolic molding compound with a very high strain to failure in flexure. UL listed.USES: Armature insulation.Information provided by Vyncolit, a Sumitomo Bak Group
Flexural Modulus	7.00 - 9.00 GPa	1020 - 1310 ksi	Injection and Compression; ISO 178
Raschig Group MELOPLAS® 180 MF Wood flour-reinforced, phenol-modified MF molding compound (MPF) in dark colors. High surface hardness, good mechanical strength and electrical properties, good heat resistance. Self-extinguishing ..
Flexural Modulus	6.00 - 9.00 GPa @Temperature 80.0 - 80.0 °C	870 - 1310 ksi @Temperature 176 - 176 °F	Average value: 7.78 GPa Grade Count:9
Overview of materials for Polypropylene, Long Glass Fiber 50% This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Long Glass Fiber 50%". Specific grades with glass content between 45% and 54% are include..
Flexural Modulus	0.239 - 9.00 GPa	34.7 - 1310 ksi	Average value: 2.42 GPa Grade Count:208
Overview of materials for Polypropylene, Mineral Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Mineral Reinforced". Each property range of values reported is minimum and maximum values..