- Polymer Property : Flexural Modulus = 999 ksi
Polymer Property : Flexural Modulus = 999 ksi Product List
Mechanical PropertiesTips: 30 items are displayed at most.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Modulus | 6.89 GPa | 999 ksi | ASTM D790 |
|
PolyOne Gravi-Tech™ GRV-PS-027-BA-WHT Polybutylene Terephthalate (PBT)
Information provided by PolyOne
|
|||
| Flexural Modulus | 6.89 GPa | 999 ksi | ASTM D790 |
|
PolyOne Edgetek® ES-30GF/000 Black Polyethersulfone (PESU)
Edgetek™ ES-30GF/000 Black XP120031Information provided by PolyOne
|
|||
| Flexural Modulus | 6.89 GPa | 999 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
|
SABIC Innovative Plastics Lexan® JK2000 PC+ABS (Asia Pacific)
Lexan* JK2000 compound is a glass reinforced, non-Br and non-Cl FR polycarbonate blends designed for thinwall molding applications.
|
|||
| Flexural Modulus | 6.89 GPa | 999 ksi | 6.4 mm; ASTM D790 |
|
SABIC Innovative Plastics Lexan® FL930 PC
Various weight reductions at 0.250"" (6.35 mm) wall, 30% GR. Superior flex strength/modulus, good tensile strength. V-0/5VA at 0.250"" (6.35 mm).
|
|||
| Flexural Modulus | 6.89 GPa | 999 ksi | ASTM D 790 |
|
MRC Polymers MAXNITEâ„¢ 550 GF30 PET, 30% Glass Mineral Reinforced
Information provided by MRC Polymers Inc.
|
|||
| Flexural Modulus | 6.89 GPa | 999 ksi | ASTM D790 |
|
SABIC Innovative Plastics LNP LUBRICOMP RFL34 PA 66
LNP* LUBRICOMP* RFL34 is a compound based on Nylon 66 resin containing 20% Glass Fiber, 15% PTFE. Added feature of this material is: Wear Resistant.
|
|||
| Flexural Modulus | 6.89 GPa | 999 ksi | ASTM D790 |
|
SABIC Innovative Plastics LNP LUBRICOMP RFL34 PA 66 (Asia Pacific)
LNP* Lubricomp* RFL34 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
|
|||
| Flexural Modulus | 6.89 GPa | 999 ksi | 2 mm/min; ISO 178 |
|
SABIC Innovative Plastics ULTEM 2200F PEI
20% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming. US FDA Food Contact compliant in recognized colors.
|
|||
| Flexural Modulus | 6.89 GPa | 999 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
|
SABIC Innovative Plastics ULTEM 2210EPR PEI
20% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 and 5VA listing.
|
|||
| Flexural Modulus | 6.89 GPa | 999 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
|
SABIC Innovative Plastics ULTEM 2210EPR PEI (Asia Pacific)
20% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 and 5VA listing.
|
|||
| Flexural Modulus | 6.89 GPa | 999 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
|
SABIC Innovative Plastics ULTEM 2210K PEI (Asia Pacific)
20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming.
|
|||
| Flexural Modulus | 6.89 GPa | 999 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
|
SABIC Innovative Plastics ULTEM 2210R PEI
20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.
|
|||
| Flexural Modulus | 6.89 GPa | 999 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
|
SABIC Innovative Plastics ULTEM 2210R PEI (Asia Pacific)
20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.
|
|||
| Flexural Modulus | 6.89 GPa | 999 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
|
SABIC Innovative Plastics ULTEM CRS5201R PEI
20% Glass fiber filled, standard flow Polyetherimide copolymer (Tg 225C) with internal mold release and enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO Conforming.
|
|||
| Flexural Modulus | 6.89 GPa | 999 ksi | 2.6 mm/min, 100 mm span; ASTM D 790 |
|
SABIC Innovative Plastics Ultem CRS5211 PEI
20% Glass fiber filled, enhanced flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO Conforming, UL94 V0 and 5VA listing.Th..
|
|||
| Flexural Modulus | 6.89 GPa | 999 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
|
SABIC Innovative Plastics ULTEM CRS5211R PEI
20% Glass fiber filled, enhanced flow Polyetherimide copolymer (Tg 225C) with internal mold release and enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO conforming.
|
|||
| Flexural Modulus | 6.89 GPa | 999 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
|
SABIC Innovative Plastics ULTEM CRS5211R PEI (Asia Pacific)
20% Glass fiber filled, enhanced flow Polyetherimide copolymer (Tg 225C) with internal mold release and enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO conforming.
|
|||
| Flexural Modulus | 6.89 GPa | 999 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
|
SABIC Innovative Plastics ULTEM HU2210 PEI
20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP ..
|
|||
| Flexural Modulus | 6.89 GPa | 999 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
|
SABIC Innovative Plastics Valox® 508 PBT+PC
30% GR PBT+PC. Excellent mechanical and thermal performance. Non-flame retardant. Reduced warpage characteristics. Applications same as VALOX 420.
|
|||
| Flexural Modulus | 6.89 GPa | 999 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
|
SABIC Innovative Plastics Valox® 508R PBT+PC
30% GR PBT+PC. Excellent mechanical and thermal performance. Non-FR. Reduced warpage characteristics. Applications same as VALOX 420R.
|
|||
| Flexural Modulus | 6.89 GPa | 999 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
|
SABIC Innovative Plastics Valox® 553 PBT+PC
30% GR PBT+PC, UL94 V-0. Reduced warpage characteristics.Applications; appliance handles, spotlights, electric motors, pump housings, etc.
|
|||
| Flexural Modulus | 6.89 GPa | 999 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
|
SABIC Innovative Plastics Valox® 830 PBT
30% GR PBTP, excellent surface finish. Typical applications are hot air gun housing assemblies, industrial glue guns, appliance housings and handles.
|
|||
| Flexural Modulus | 6.89 GPa | 999 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
|
SABIC Innovative Plastics Valox® 830R PBT (Asia Pacific)
30% glass filled, release grade, polyester alloy.This data was supplied by SABIC-IP for the Asia Pacific region.
|
|||
| Flexural Modulus | 6.89 GPa | 999 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
|
SABIC Innovative Plastics Valox® HR426 PBT (Asia Pacific)
AUTOMOTIVE. 30% GR, hydrolytically stable PBT. Excellent strength, stiffness and dimensional stability.
|
|||
| Flexural Modulus | 6.89 GPa | 999 ksi | ASTM D790 |
|
SABIC Innovative Plastics LNP THERMOCOMP LF004E PEEK (Asia Pacific)
LNP* Thermocomp* LF004E is a compound based on Polyetheretherketone resin containing Glass Fiber. Added features of this material include: Easy Molding.
|
|||
| Flexural Modulus | 6.89 GPa | 999 ksi | ASTM D790 |
|
SABIC Innovative Plastics LNP VERTON MX02795 PP (Asia Pacific)
LNP* Verton* MX02795 is a compound based on Polypropylene resin containing Long Glass Fiber. Added features of this material include: Chemically Coupled, Heat Stabilized, UV Stabilized.
|
|||
| Flexural Modulus | 6.89 GPa | 999 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
|
SABIC Innovative Plastics Valox® 508 PBT+PC (Asia Pacific)
30% GR PBT+PC. Excellent mechanical and thermal performance. Non-flame retardant. Reduced warpage characteristics. Applications same as VALOX 420.
|
|||
| Flexural Modulus | 6.89 GPa | 999 ksi | ASTM D790 |
|
SABIC Innovative Plastics LNP STAT-KON RE002 PA 66 (Asia Pacific)
LNP* Stat-kon* RE002 is a compound based on Nylon 66 resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
|
|||
| Flexural Modulus | 6.89 GPa | 999 ksi | tangent; ASTM D790 |
|
A. Schulman POLYPUR™ FPU 1515 Thermoplastic Polyurethane Compound
Information provided by A. Schulman.
|
|||
| Flexural Modulus | 6.89 GPa | 999 ksi | tangent; ASTM D790 |
|
A. Schulman POLYPUR™ FPU 1515 Thermoplastic Polyurethane Compound
Information provided by A. Schulman.
|
|||