- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 110 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 110 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
|
RheTech Products T20P200-01BG 20% Talc Reinforced Polypropylene Copolymer, General Purpose Black, Blow Molding Grade
Applications: HVAC ductsSeat backsInjection molding conditions reported in table.Information provided by RheTech Products.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ISO 75A |
|
Polyplastic Armlen® PP MF 20-3IM Impact Modified Polypropylene
Impact modified polypropylene composite materialInformation provided by PolyPlastic Group.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | 120°C/h; ISO 75/1 |
|
Polykemi AB POLYlux 3809S F20 UV2 PC/PBT-Blend, Glass Fiber-Reinforced
Information provided by Polykemi AB
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
|
Polymer Resources PPX-MF-FR3 Modified-PPO, V-0 Flame Retardant, Mineral Reinforced
Modified-Polyphenylene Oxide, V-0 Flame Retardant, 230F HDT, Mineral ReinforcedFeatures: • Bromine Free • Chlorine Free • Self ExtinguishingProcess: Injection MoldingNotes: All physical, mecha..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
|
RheTech Products HP532-00 20% Talc Reinforced High Performance Polypropylene, Non-UV Stabilized, Natural
Applications: Interior trimCenter tail light bezelPackage trayInjection molding conditions reported in table.Information provided by RheTech Products.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
|
Flint Hills P4G4B-125A Homopolymer Polypropylene
Homopolymer, UL certified, and FDA compliant.Features: Nucleated and antistat.Applications: Injection molding: general purpose.Former Huntsman polypropylene products are now produced by Flint Hills ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | Unannealed; ASTM D648 |
|
Global PP-1102-K Polypropylene Homopolymer
Description-transparency, high stiffness, high heat resistantApplications-textile applications, bags, tape, sheetInformation provided by Global Polymers Corporation.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
110
°C <br>@Thickness 6.40 mm
|
230
°F <br>@Thickness 0.252 in
|
Unannealed; ASTM D648 |
|
LG Chemical XR440 ABS, Low Emission High Heat ABS
Feature: Injection Molding Grade, Low Emission High Heat ABSApplication: Automotives Interior housingCAS No. 25120-20-1, 9003-56-9, 25747-74-7, and 31621-07-5Information provided by LG Chemical
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ISO 75-1/-2 |
|
Lanxess Durethan® DP 2325 H3.0 000000 Nylon 66
PA 66, injection molding grade, non-reinforced, elastomer-modified, good heat-ageing resistance, extremely high notched impact strength even at dry state and at low temperatures
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
|
Hyosung Topilene J800R PP
J800R Injection Special Purpose GradeApplications:Electric home applianceHousewares applianceCharacteristics:Long-term heat resistanceInformation provided by Hyosung Corporation
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | |
|
LATI Latilub 73/13-01M POM, Molybdenum disulphide Filled
Self-lubricating product based on Polyoxymethylene (POM). Molybdenum disulphide. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati In..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
|
SABIC Innovative Plastics Valox® 359 PBT (Europe-Africa-Middle East)
VALOX 359 is an unreinforced, flame retarded, low warpage PBT injection moulding resin.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
|
Spartech Polycast UF96 Cell Cast Acrylic
Description: Cell Cast AcrylicInformation provided by Spartech.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics Xenoy® CL100 PBT+PC (Asia Pacific)
Xenoy CL100 is an unfilled, impact modified, UV-stabilized PC/PBT blend with excellent solvent resistance and good low-temperature ductility. It has a proven track record in unpainted exterior autom..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
110
°C <br>@Thickness 3.20 mm
|
230
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP ZF0049 PPE+PS
LNP* THERMOCOMP* ZF0049 is a compound based on PPE+PS resin containing 20% Glass Fiber. Added feature of this material is: Flame Retardant.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ISO 75-2 |
|
Borealis MB250WG Polypropylene Compound, Mineral Filled
MB250WG is a 20 % mineral filled polypropylene compound intended for injection molding. Applications: MB250WG has been developed especially for the white goods industry. Washing machine parts, and ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
|
A. Schulman POLYFORT™ FPP 1477 Mineral Filled, General-Purpose Polypropylene
DescriptionPolyfort® FPP 1477 is a 20% mineral filled, general-purpose polypropylene.Information provided by A. Schulman.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
|
Tipco Tipcolene® FPT 40 - 40% Talc Reinforced Polypropylene Homopolymer Compound
40% Talc Reinforced PP HomopolymerApplications: General PurposeProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
|
A. Schulman POLYFORT™ FPP 3716 Talc Filled Copolymer Polypropylene
DescriptionPolyfort® FPP 3716 is a 12% talc filled copolymer polypropylene product. Information provided by A. Schulman.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ISO 75 |
|
Unitika TERRAMAC TE-7000 Polylactic Acid (PLA)
Heat-resisting grade, Injection grade. Bio-based materials produced from annually renewable raw materials.Information provided by Unitika Ltd.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ISO 75-1,-2 |
|
Covestro Bayblend® FR3015 PC/ABS Blend
Main characteristics:• High toughness even at low temperatures• High dimensional accuracy and stability• Good paintability• Good flowabilityGrade characteristics:• Flame-retardant• Injec..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ISO 75-1/-2 |
|
Covestro Makroblend® S 7916 Polycarbonate + PBT, Impact Grade
ISO 7792-1-PBT/PC,MHPR,-020(PBT+PC)-blendsimpact modifiedInjection molding gradeexcellent chemical resistancehigh toughness at low temperaturesideal for painted applicationsunreinforcedPreprocessing..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
|
Carmel Olefins CAPILENE® U 77 A Polypropylene Homopolymer
Description: CAPILENE® U 77 A is a high melt flow rate homopolymer for injection molding of products with long flow length. It is specially formulated with antistatic and nucleating additives, al..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
|
Cheng Yu Plastic B610 PC/PBT |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
|
Cheng Yu Plastic C1200 PC/ABS |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
|
Asahi Kasei Thermylene® F6-10FG-0100 10% Glass Fiber Reinforced, Chemically Coupled
Information provided by Asahi Thermofil
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
|
Aaron Industries AAROLENE® ARPP H 200-1 PP Black Polypropylene Homopolymer Compounded Resin
AAROLENE® ARPP 200 Series Polypropylene Compounded ResinFeatures: A pre-colored, black homopolymer polypropylene resin specifically designed for all injection molding applications.High Flow
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
110
°C <br>@Thickness 0.125 mm
|
230
°F <br>@Thickness 0.00492 in
|
ASTM D648 |
|
Proto3000 PC-ABS Fused Deposition Modeling Polymer
Description: PC-ABS (polycarbonate-ABS) is one of the most widely used industrial thermoplastics. PC-ABS offers the most desirable properties of both materials - the superior strength and heat resis..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
|
Braskem H 501 HC Bioriented Film Polypropylene
Applications: High stiffness; barrier films for conversionInformation provided by Braskem
|
|||