- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 111 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 111 °F Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 44.0 °C | 111 °F | ASTM D648 |
|
DuPont 20 Series 2020 Specialty Polyethylene Resin
(discontinued **)
DuPont 2020T and 2020 specialty low density polyethylene resins are products characterized by low melt index and intermediate crystallinity. These products, produced via a unique polymerization proc..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 44.0 °C | 111 °F | ASTM D648 |
|
DuPont™ Surlyn® 8527 Ionomer Resin, Sodium
(discontinued **)
Surlyn® 8527 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with sodium ions. The amount of MAA and neu..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 43.9 °C | 111 °F | ISO 75B-1, -2 |
|
LyondellBasell Hifaxâ„¢ A Thermoplastic Polyolefin Elastomer
Description: Hifaxâ„¢ CA 10 A is a thermoplastic polyolefin which has been developed for the extrusion and calendering of soft film and sheet. Thanks to its high rubber content "Hifax" CA 10 A fe..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
44.0
°C @Thickness 3.20 mm |
111
°F @Thickness 0.126 in |
ISO 75 |
|
A. Schulman FORMION™ FI 335 Ionomer
Information provided by A. Schulman.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
44.0
°C @Thickness 3.20 mm |
111
°F @Thickness 0.126 in |
ISO 75 |
|
A. Schulman FORMION™ FI 335 Ionomer
Information provided by A. Schulman.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 44.0 °C | 111 °F | ASTM D648 |
|
DuPont 20 Series 2010 Specialty Polyethylene Resin
DuPont 2010 specialty low density polyethylene resin is characterized by low melt index and intermediate crystallinity. This product, produced via a unique polymerization process, has outstanding fl..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 44.0 °C | 111 °F | ASTM D648 |
|
DuPont 20 Series 2020T Specialty Polyethylene Resin
DuPont 2020T and 2020 specialty low density polyethylene resins are products characterized by low melt index and intermediate crystallinity. These products, produced via a unique polymerization proc..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 44.0 °C | 111 °F | ASTM D648 |
|
DuPont 20 Series 20-6064 Specialty Polyethylene Resin
DuPont 20-6064 specialty low density polyethylene resin is characterized by low melt index and intermediate crystallinity. This product, produced via a unique polymerization process, has outstanding..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 44.0 °C | 111 °F | ASTM D648 |
|
DuPont 20 Series DPE 20 Specialty Polyethylene Resin
DuPont 20 specialty low density polyethylene resin is characterized by low melt index and intermediate crystallinity. This product, produced via a unique polymerization process, has outstanding flex..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
44.0
°C @Thickness 3.20 mm |
111
°F @Thickness 0.126 in |
ISO 75 |
|
A. Schulman FORMION™ FI 335 Ionomer
Information provided by A. Schulman.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
44.0
°C @Thickness 3.20 mm |
111
°F @Thickness 0.126 in |
ISO 75 |
|
A. Schulman FORMION™ FI 335 Ionomer
Information provided by A. Schulman.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
44.0
°C @Thickness 3.20 mm |
111
°F @Thickness 0.126 in |
ISO 75 |
|
A. Schulman FORMION™ FI 335 Ionomer
Information provided by A. Schulman.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
44.0
°C @Thickness 3.20 mm |
111
°F @Thickness 0.126 in |
ISO 75 |
|
A. Schulman FORMION™ FI 335 Ionomer
Information provided by A. Schulman.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 44.0 °C | 111 °F | ASTM D648 |
|
DuPont™ Surlyn® 8920 Ionomer Resin, Sodium
Surlyn® 8920 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with sodium ions. The amount of MAA and neu..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 44.0 °C | 111 °F | ASTM D648 |
|
DuPont™ Surlyn® 8940 Ionomer Resin, Sodium
Surlyn® 8940 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with sodium ions. The amount of MAA and neu..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 44.0 °C | 111 °F | ASTM D648 |
|
DuPont™ Surlyn® 9910 Ionomer Resin, Zinc
Surlyn® 9910 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. The amount of MAA and neutr..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 44.0 °C | 111 °F | ASTM D648 |
|
DuPont™ Surlyn® PC100 Ionomer Resin, Highest Clarity, Sodium
Surlyn® PC100 luxury molding resin is a "select" grade of Surlyn® 8920, controlled to achieve the highest possible optical clarity in molded perfume jars and caps. It complies with the provisions ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 44.0 °C | 111 °F | |
|
Spartech Spectrum® S630 MDPE Polyolefin Sheet
(discontinued **)
Data provided by the manufacturer.
|
|||