- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 113 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 113 °F Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 - 50.0 °C | 113 - 122 °F | ASTM D648-06 |
|
Proto3000 Objet Digital Materials™ DM_7210 Transparent Prototyping Polymer
Primary material: FullCure720Secondary material: TangoBlackDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to provide ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 - 50.0 °C | 113 - 122 °F | ASTM D648-06 |
|
Proto3000 Objet Digital Materials™ DM_7220 Transparent Prototyping Polymer
Primary material: FullCure720Secondary material: TangoBlackDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to provide ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 - 50.0 °C | 113 - 122 °F | ASTM D648-06 |
|
Proto3000 Objet Digital Materials™ DM_7230 Transparent Prototyping Polymer
Primary material: FullCure720Secondary material: TangoBlackDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to provide ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 - 50.0 °C | 113 - 122 °F | ASTM D648-06 |
|
Proto3000 Objet Digital Materials™ DM_8210 Rigid Opaque Prototyping Polymer
Primary material: VeroBlueSecondary material: VeroBlackDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to provide the ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 - 50.0 °C | 113 - 122 °F | ASTM D648-06 |
|
Proto3000 Objet Digital Materials™ DM_8310 Rigid Opaque Prototyping Polymer
Primary material: VeroWhitePlusSecondary material: VeroBlackDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to provide..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 - 50.0 °C | 113 - 122 °F | ASTM D648-06 |
|
Proto3000 Objet Digital Materials™ DM_Dots_7513 Transparent Prototyping Polymer
Primary material: FullCure720Secondary material: VeroBlackDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to provide t..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 - 50.0 °C | 113 - 122 °F | ASTM D648-06 |
|
Proto3000 Objet Digital Materials™ DM_Grid_7523 Transparent Prototyping Polymer
Primary material: FullCure720Secondary material: VeroBlackDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to provide t..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 - 50.0 °C | 113 - 122 °F | ASTM D648-06 |
|
Proto3000 Objet FullCure720 Transparent Prototyping Polymer
Objet’s FullCure® Materials family of proprietary acrylic-based photopolymer materials enables Objet users to create highly accurate, finely detailed 3D models and parts for a wide range of Rapid ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 - 50.0 °C | 113 - 122 °F | ASTM D648-06 |
|
Proto3000 Objet VeroBlack FullCure870 Rigid Opaque Prototyping Polymer
Objet’s FullCure® Materials family of proprietary acrylic-based photopolymer materials enables Objet users to create highly accurate, finely detailed 3D models and parts for a wide range of Rapid ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 - 50.0 °C | 113 - 122 °F | ASTM D648-06 |
|
Proto3000 Objet VeroClear FullCure810
Information provided by Proto3000 for their protoyping engineering services.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 - 50.0 °C | 113 - 122 °F | ASTM D648-06 |
|
Proto3000 Objet VeroGray FullCure850 Rigid Opaque Prototyping Polymer
Objet’s FullCure® Materials family of proprietary acrylic-based photopolymer materials enables Objet users to create highly accurate, finely detailed 3D models and parts for a wide range of Rapid ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 °C | 113 °F | ISO 75.1 |
|
Solvay Engineered Polymers DEXFLEX® E756 TPO
(discontinued **)
Description: DEXFLEX® E756 thermoplastic olefinic elastomer (TPO) is designed for extruded automotive air-bag covers. This material provides excellent rigidity, durability and low-temperature toug..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 °C | 113 °F | ASTM D648-98c |
|
DSM Somos® WaterClear® 10120 Epoxy Resin for Stereolithography
(discontinued **)
DescriptionDSM Somos® 10120 is a high-speed liquid photopolymer that produces strong, rigid, and durable parts with optical clarity using stereolithography machines. This material is especially us..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 - 54.0 °C | 113 - 129 °F | ASTM D648 |
|
DSM Somos® 7110 Epoxy Photopolymer, Green Parts
(discontinued **)
DescriptionDSM Somos® 7110 Photopolymer is a humidity-tolerant, high heat-deflection-temperature, low-curl, high-speed liquid that produces rigid, highly accurate parts. It produces exceptional, u..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 °C | 113 °F | |
|
LyondellBasell Lupolen® 3020 D LDPE
Blow molding, injection molding.Data was collected by ISO methods and originally provided by BASF. The Lupolen® product line is now produced by Basell.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 °C | 113 °F | |
|
LyondellBasell Lupolen® 3020 H LDPE, Film Grade
FilmData was collected by ISO methods and originally provided by BASF. The Lupolen® product line is now produced by Basell.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 °C | 113 °F | |
|
LyondellBasell Lupolen® 3025 K LDPE, Film Grade
FilmData was collected by ISO methods and originally provided by BASF. The Lupolen® product line is now produced by Basell.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 °C | 113 °F | |
|
LyondellBasell Lupolen® 3026 F LDPE, Film Grade
FilmData was collected by ISO methods and originally provided by BASF. The Lupolen® product line is now produced by Basell.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 °C | 113 °F | |
|
LyondellBasell Lupolen® 3032 D LDPE
Insulation for cableData was collected by ISO methods and originally provided by BASF. The Lupolen® product line is now produced by Basell.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 °C | 113 °F | |
|
LyondellBasell Lupolen® 3040 D LDPE, Film Grade
FilmData was collected by ISO methods and originally provided by BASF. The Lupolen® product line is now produced by Basell.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 °C | 113 °F | |
|
LyondellBasell Lupolen® 3226 K LDPE, Film Grade
FilmData was collected by ISO methods and originally provided by BASF. The Lupolen® product line is now produced by Basell.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 °C | 113 °F | |
|
LyondellBasell Lupolen® 3412 D LDPE
Telephone cable insulationData was collected by ISO methods and originally provided by BASF. The Lupolen® product line is now produced by Basell.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 °C | 113 °F | Unannealed; ASTM D648 |
|
Techmer ES HiFill® PA11 GB7 HS L 7% Glass Bead Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Bead, 7% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Heat Stabilized and LubricatedInformation provided by T..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 °C | 113 °F | Unannealed; ASTM D648 |
|
Techmer ES HiFill® PA11 GL8 HS UV
Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Graphite Powder Lubricant and UV StabilizerFeatures: Heat Stabilized. Good UV Resistance and LubricatedAppearance: Natural ColorIn..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 °C | 113 °F | Molded and tested in accordance with ASTM D4976; ASTM D648 |
|
Dow DNDA-8335 NT 7 Linear Low Density Polyethylene Resin
DOW DNDA-8335 NT 7 is produced using UNIPOL™ PE process technology. It is intended for use in general purpose injection molding applications. Information provided by Dow
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 °C | 113 °F | Molded and tested in accordance with ASTM D4976; ASTM D648 |
|
Dow DNDA-8350 NT 7 Linear Low Density Polyethylene Resin
DOW DNDA-8350 NT 7 is produced using UNIPOL™ PE process technology. It is intended for use in general purpose injection molding applications. Information provided by Dow
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 °C | 113 °F | ASTM D648 |
|
Aclo Accucomp Polyethylene LD0109L Low Density |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 - 50.0 °C | 113 - 122 °F | ASTM D648-06 |
|
Proto3000 Objet VeroWhitePlus FullCure835 Rigid Opaque Prototyping Polymer
Information provided by Proto3000 for their protoyping engineering services.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 °C | 113 °F | |
|
LATI Latistat 48/9900-03 EVA
Dissipative product based on Ethyl-Vinyl-Acetate (EVA). Unfilled. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termopl..
|
|||