- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 115 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 115 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) |
115
°C @Thickness 3.20 mm |
239
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Cycoloy® C1950 PC+ABS
Low viscosity injection molding resin.This data was supplied by SABIC-IP for the Americas region.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | 120°C/h; ISO 75/1 |
|
Polykemi AB POLYfill PPC T4030 E20 Polypropylene Copolymer, Mineral Reinforced, Elastomer Modified
Information provided by Polykemi AB
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | 120°C/h; ISO 75/1 |
|
Polykemi AB POLYfill PPH TS4020D Polypropylene Homopolymer, Mineral Reinforced, Detergent Resistant
Information provided by Polykemi AB
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75-1/-2 |
|
DuPont Performance Polymers Crastin® S600F40 NC010 PBT
(Unverified Data**)
Crastin® S600F40 NC010 is an unreinforced, lubricated, low viscosity polybutylene terephthalate resin for injection molding.Information provided by DuPont Performance Polymers
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
|
PolyMirae Moplen EP540T Injection Molding Grade Polypropylene
Moplen EP540T is the polypropylene block copolymer manufactured by PMC under the license of BASELL using the Spheripol process. Moplen EP540T is a block copolymer particularly suitable for injection..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
115
°C @Thickness 3.20 mm |
239
°F @Thickness 0.126 in |
ASTM D648 |
|
Covestro Bayblend® 2153 Polycarbonate + ABS Blend, General Purpose
(discontinued **)
Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This produ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
115
°C @Thickness 6.40 mm |
239
°F @Thickness 0.252 in |
Unannealed; ASTM D648 |
|
LG Chemical Lupox® TE5000G PBT+PC
Description: Injection Molding, PBT+PC, High Impact, Dimensional Stability, Good WeatherabilityApplication: Automotive (Door Garnish, Door Handle)CAS No. 24968-12-5 and 103598-77-2Information provid..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 - 120 °C | 239 - 248 °F | ASTM D1525, HDT Method B |
|
Loxim 841 02T HB Polypropylene Compound, 40% Talc Filled, Flame Retardant
Information provided by Loxim Industries
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75-1/-2 |
|
Lanxess Durethan® T 40 ZS 000000 Partially aromatic polyamide
Partially aromatic polyamide, injection molding and extrusion grade, easy release, transparent in all wall thicknesses, isotropic shrinkage, mechanical and electrical properties largely unaffected b..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO Method 75 |
|
LyondellBasell Astryn BB724AC Polypropylene Copolymer
Key Features: medium high melt flow, high modulus, mineral-filled polypropylene copolymer, high rigidity, good impact resistance, good processabilityApplications: automotive heater and A/C ductworkD..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
115
°C @Thickness 3.20 mm |
239
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Valox® 309 PBT
PBT, For compounding only. Not intended for Injection Molding. Melt viscosity: 250C at 21.6 kgf is 3500-4500. Available in Natural (1001) only.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
|
SABIC Innovative Plastics Xenoy® 1760T PBT+PC (Europe-Africa-Middle East)
XENOY 1760T is developed as a easy flow material, for applications such as doorhandles and mirror housings. It is a 11% glass reinforced material with excellent strength and dimensional stability.Th..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
|
A. Schulman POLYFORT™ FXP 2779U UV Stabilized Copolymer Polypropylene
DescriptionPolyfort® FXP 2779U is a 20% talc-filled, UV stabilized copolymer polypropylene.Information provided by A. Schulman.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | |
|
Total PPH 3762 Polypropylene, Extrusion Grade
Homopolymer fiber grade for staple fiber and multifilament yarnsFading Resistance - FINA 3762 is formulated to resist gas fading while maintaining excellent processing stability up to 250oC.Process ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
|
A. Schulman POLYFORT™ FPP 1182 Talc Fortified Impact Resistant Polypropylene
DescriptionPolyfort® FPP 1182 is a 20% talc fortified impact resistant polypropylene.Information provided by A. Schulman.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
|
A. Schulman POLYFORT™ FPP 1182 Talc Fortified Impact Resistant Polypropylene
DescriptionPolyfort® FPP 1182 is a 20% talc fortified impact resistant polypropylene.Information provided by A. Schulman.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
|
A. Schulman POLYFORT™ FPP 1182 Talc Fortified Impact Resistant Polypropylene
DescriptionPolyfort® FPP 1182 is a 20% talc fortified impact resistant polypropylene.Information provided by A. Schulman.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75-1/-2 |
|
EMS-Grivory Grivory® 2D 25 W 20 X black PA612-I
Product Description: Grilamid 2D 25 W 20 X black 9992 is a semi-flexible high viscosity, plasticized, high impact, heat and UV resistant extrusion grade based on polyamide 612 (PA612). Unique proper..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75-1/-2 |
|
EMS-Grivory Grivory® L 20 G grey 9280 PA12
Product Description: Grilamid L 20 G grey 9280 is a medium viscosity, unreinforced, heat stabilized polyamide 12 for injection molding and cable sheathing. The main features of this product are: Low..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75-1/-2 |
|
EMS-Grivory Grivory® L 20 G HL PA12
Product Description: Grilamid L 20 GHL is a, medium viscosity injection molding grade, based on Polyamide 12 (PA12). Grilamid L 20 GHL is UV-stabilized, and heat stabilized The special features of G..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75-1/-2 |
|
EMS-Grivory Grivory® XE 4071 black 9992 PA612
Product description: Grilamid XE 4071 BLACK 9992 is an impact modified unreinforced high viscosity polyamide 612 (PA612) extrusion grade with superior heat and hydrolysis resistance. Compared to sta..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75-1/-2 |
|
DuPont Performance Polymers Crastin® FGS600F40 NC010 Polybutylene Terephthalate (PBT)
(Unverified Data**)
Unreinforced Low Viscosity Polybutylene Terephthalate Developed for Food Contact Applications Crastin FGS600F40 NC010 is an unreinforced low viscosity polybutylene terephthalate resin for injection ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
|
Aclo Accutech Polypropylene Copolymer HP0334W20L Wollastonite Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
|
Aclo Accutech Polypropylene Homopolymer HP0334T20L Talc Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
|
Aclo Accutech Polypropylene Homopolymer HP0339T10L1 Talc Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | 120°C/h; ISO 75/1 |
|
Polykemi AB POLYfill PPH TS8020 Polypropylene Homopolymer, Mineral Reinforced
Information provided by Polykemi AB
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | 120°C/h; ISO 75/1 |
|
Polykemi AB POLYfill PPHC T8020 Polypropylene, Mineral Reinforced
Information provided by Polykemi AB
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | |
|
Asahi Kasei Xyron® AT610 Modified Polyphenylene Ether
Applications: Information provided by Asahi Kasei
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
115
°C @Thickness 3.20 mm |
239
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Cycoloy® CX1440 PC+ABS (Asia Pacific)
CYCOLOY CX1440 is a general purpose PC+ABS blend specially developped for thin wall applications requiring weld line strength and high flow with a good balance of properties
|
|||