- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 137 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 137 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) |
137
°C <br>@Thickness 6.40 mm
|
279
°F <br>@Thickness 0.252 in
|
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Lexan® 105 PC
General purpose low flow Polycarbonate powder gradeThis data was supplied by SABIC-IP for the Americas region.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
137
°C <br>@Thickness 6.40 mm
|
279
°F <br>@Thickness 0.252 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® 133 PC
Nonhalogenated. 3.5 MFR. UV-stabilized.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
137
°C <br>@Thickness 6.40 mm
|
279
°F <br>@Thickness 0.252 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® 153R PC
Nonhalogenated. 2.5 MFR. Blowmolding/extrusion. UV-stabilized. Internal mold release.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
137
°C <br>@Thickness 6.40 mm
|
279
°F <br>@Thickness 0.252 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® 201R PC
7.0 MFR, for thicker sections without sinks. Improved flame retardance. Internal mold release.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
137
°C <br>@Thickness 6.40 mm
|
279
°F <br>@Thickness 0.252 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® 241 PC (Asia Pacific)
10.5 MFR. Improved flame retardance.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
137
°C <br>@Thickness 6.40 mm
|
279
°F <br>@Thickness 0.252 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® 923 PC (Asia Pacific)
Opaque colors, low viscosity, superior flame retardance. Decreased smoke and lowered toxic gas emission. UV-stabilized.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
137
°C <br>@Thickness 6.40 mm
|
279
°F <br>@Thickness 0.252 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® HP4R PC (Asia Pacific)
Medium flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains a hig..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
137
°C <br>@Thickness 6.40 mm
|
279
°F <br>@Thickness 0.252 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® HPS2S PC (Asia Pacific)
Med/high flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, steam, e-beam, and gamma steriliza..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
137
°C <br>@Thickness 6.40 mm
|
279
°F <br>@Thickness 0.252 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® HPS2S PC (Europe-Africa-Middle East)
Med/high flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, steam, e-beam, and gamma steriliza..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
137
°C <br>@Thickness 6.40 mm
|
279
°F <br>@Thickness 0.252 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® IFX5420Z PC (Asia Pacific)
Lexan* IFX5420Z is a medium viscosity, release containing, injection moldable polycarbonate grade suitable for use in industry protective eye-ware welding applications. This grade meets the transmis..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
137
°C <br>@Thickness 6.40 mm
|
279
°F <br>@Thickness 0.252 in
|
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Lexan® IR2840 PC
7.0 MFR, for thicker sections without sinks. Internal mold release. FDA food contact compliant, natural only.Effective January 15th, 2007 this grade will no longer be supported with biocompatibilit..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
137
°C <br>@Thickness 6.40 mm
|
279
°F <br>@Thickness 0.252 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® OQ4320R PC (Asia Pacific)
Optical grade with UV cut-off up to 400 nm; greater optical purity than standard grades. For sunglass and sunvisor markets. Internal mold release.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 137 °C | 279 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP COLORCOMP D1000FH PC (Asia Pacific)
LNP COLORCOMP* D1000FH is a compound based on Polycarbonate resin containing Unfilled Custom Color. Added features of this material include: Low Extractible.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
137
°C <br>@Thickness 6.40 mm
|
279
°F <br>@Thickness 0.252 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® 101 PC
UL rated HB as of 10/97. 200 series recommended when V-2 rating required. Nonhalogenated, 7.0 MFR, for thicker sections without sinks.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
137
°C <br>@Thickness 6.40 mm
|
279
°F <br>@Thickness 0.252 in
|
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Lexan® 151 PC (Asia Pacific)
Nonhalogenated. 2.5 MFR. Blowmolding/extrusion.This data was supplied by SABIC-IP for the Asia Pacific region.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
137
°C <br>@Thickness 6.40 mm
|
279
°F <br>@Thickness 0.252 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® 243 PC
10.5 MFR. UV-stabilized. Improved flame retardance.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
137
°C <br>@Thickness 6.40 mm
|
279
°F <br>@Thickness 0.252 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® 920A PC (Asia Pacific)
Low viscosity injection moldable, flame retardant PC. Exceptional surface appearance. Clear, tints and opaque colors.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
137
°C <br>@Thickness 6.40 mm
|
279
°F <br>@Thickness 0.252 in
|
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Lexan® FL2003 PC (Asia Pacific)
Various weight reductions at 0.250" (6.35mm) wall. Low temperature impact and high heat resistant. Excellent surface. UV-stabilized.This data was supplied by SABIC-IP for the Asia Pacific region...
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
137
°C <br>@Thickness 6.40 mm
|
279
°F <br>@Thickness 0.252 in
|
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Lexan® FXE143R PC
UV stabilized PC resin for "Illuminate"/Edge Glow Visual Effect. Medium viscosity (10.5 MFR). Nonhalogenated.This data was supplied by SABIC-IP for the Americas region.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
137
°C <br>@Thickness 6.40 mm
|
279
°F <br>@Thickness 0.252 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® HPS6R PC
Low/med flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). Contains a higher amount of mold release t..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
137
°C <br>@Thickness 3.20 mm
|
279
°F <br>@Thickness 0.126 in
|
Unannealed; ASTM D648 |
|
LG Chemical LUPOL GP3202Z PP+MF20%
Description: Injection Molding, PP+MF20%, Good WeatherabilityApplication: Electrical, Electronic and Automotive Interior PartsCAS: 9003-07-0 and 14807-96-6Information provided by LG Chemical
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
137
°C <br>@Thickness 3.20 mm
|
279
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP DL0049EF PC
LNP* Lubricomp* DL0049EF is a compound based on Polycarbonate resin containing 20% PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Retardant
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
137
°C <br>@Thickness 3.20 mm
|
279
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP DZL34E PC (Asia Pacific)
LNP* Lubricomp* DZL34E is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
137
°C <br>@Thickness 3.20 mm
|
279
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRILOY D2000P PC
LNP LUBRILOY* D2000P is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Exceptional Processing, Wear Resistant.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
137
°C <br>@Thickness 6.40 mm
|
279
°F <br>@Thickness 0.252 in
|
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Valox® 357U PBT
Unreinforced PBTP, UL94 V-0/5VA rated. Improved UV resistant version of VALOX 357. Nonblooming flame retardant.This data was supplied by SABIC-IP for the Americas region.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
137
°C <br>@Thickness 6.40 mm
|
279
°F <br>@Thickness 0.252 in
|
ASTM D648 |
|
Samsung Cheil Industries Infino® GW-1030S PC, Unreinforced Recycled
Eco-friendly Post-Consumer recycled content.Information provided by Samsung Cheil Industries.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 137 °C | 279 °F | ISO 75-1,-2 |
|
Covestro Makrolon® 2805 MAS145 Polycarbonate
Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Med..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
137
°C <br>@Thickness 6.40 mm
|
279
°F <br>@Thickness 0.252 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® 940 PC
Opaque colors, medium viscosity, superior flame retardance.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 137 °C | 279 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP LUBRICOMP DL0039EF PC
LNP* Lubricomp* DL-0039EF is a compound based on Polycarbonate resin containing 15% PTFE. Characteristics of this grade include: Flame Retardant and Internally Lubricated.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
137
°C <br>@Thickness 3.20 mm
|
279
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP DL0039EF PC
LNP* Lubricomp* DL-0039EF is a compound based on Polycarbonate resin containing 15% PTFE. Characteristics of this grade include: Flame Retardant and Internally Lubricated.
|
|||