Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 138 °C Product List

Thermal Properties

Tips: 30 items are displayed at most.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	138 °C	280 °F	Edgew 120104 sp=100mm; ISO 75/Be
SABIC Innovative Plastics Lexan® 103R PC (Europe-Africa-Middle East) LEXAN 103R is a high viscosity multi purpose U.V. stabilized grade and contains a release agent to ensure easy processing. LEXAN 103R is available in transparent, translucent and opaque colours.
Deflection Temperature at 0.46 MPa (66 psi)	138 °C	280 °F	Edgew 120104 sp=100mm; ISO 75/Be
SABIC Innovative Plastics Lexan® 164H PC (Europe-Africa-Middle East) LEXAN 164H resin is a medium viscosity multi purpose grade, containing a release agent to ensure easy processing. It is FDA food contact compliant in limited colors.
Deflection Temperature at 0.46 MPa (66 psi)	138 °C @Thickness 3.20 mm	280 °F @Thickness 0.126 in	unannealed; ASTM D 648
SABIC Innovative Plastics Lexan® 945ASR PC Lexan* 945ASR Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating and is available in transparent and t..
Deflection Temperature at 0.46 MPa (66 psi)	138 °C @Thickness 3.20 mm	280 °F @Thickness 0.126 in	unannealed; ASTM D 648
SABIC Innovative Plastics Lexan® 945ASR PC (Europe-Africa-Middle East) Lexan* 945ASR Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating and is available in transparent and t..
Deflection Temperature at 0.46 MPa (66 psi)	138 °C	280 °F	ASTM D648
Polymer Resources PCSF-FR G30 Polycarbonate, 30% Glass Reinforced Structural Foam Grade Process: Foam MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Foam grades tested with foamed parts with a 10% weight reduction rel..
Deflection Temperature at 0.46 MPa (66 psi)	138 °C @Thickness 3.20 mm	280 °F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics Lexan® FXD103R PC FXD103R is a Light Diffusion effect, which is part of the VisualFX family. These effects have been developed to meet increasing Aesthetic demands in the Marketplace. Color Package may affect propert..
Deflection Temperature at 0.46 MPa (66 psi)	138 °C	280 °F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics Lexan® IR2840 PC (Europe-Africa-Middle East) IR 2840 resin is a medium-low flow (MFR = 6.5 at 300?C/1.2kg), heat stabilized, polycarbonate product with mold release designed for use in the general purpose molding market. Food contact approved..
Deflection Temperature at 0.46 MPa (66 psi)	138 °C	280 °F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics Lexan® PC1000 PC (Asia Pacific) PC1000 resin is a medium-low flow (MFR = 10 at 300?C/1.2kg), heat stabilized, polycarbonate product designed for use in the custom compounding market. It does not contain UV stabilizer or mold rele..
Deflection Temperature at 0.46 MPa (66 psi)	138 °C	280 °F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics Lexan® PC1000R PC (Asia Pacific) PC1000R resin is a medium-low flow (MFR = 10 at 300?C/1.2kg), heat stabilized, polycarbonate product with mold release designed for use in the general purpose molding market.
Deflection Temperature at 0.46 MPa (66 psi)	138 °C	280 °F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics Lexan® VR2220 PC (Europe-Africa-Middle East) VR2220 resin is a medium-low flow (MFR = 10 at 300ºC/1.2kg), heat and UV stabilized, polycarbonate product with mold release designed for use in the general purpose molding market.
Deflection Temperature at 0.46 MPa (66 psi)	138 °C @Thickness 3.20 mm	280 °F @Thickness 0.126 in	ASTM D648
SABIC Innovative Plastics Lexan® VR2220 PC (Europe-Africa-Middle East) VR2220 resin is a medium-low flow (MFR = 10 at 300ºC/1.2kg), heat and UV stabilized, polycarbonate product with mold release designed for use in the general purpose molding market.
Deflection Temperature at 0.46 MPa (66 psi)	138 °C @Thickness 3.20 mm	280 °F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics LNP COLORCOMP D10006U PC LNP* COLORCOMP* D10006U is an unfilled Polycarbonate. Added features include: Lasermarking Capability, UL Listed.
Deflection Temperature at 0.46 MPa (66 psi)	138 °C	280 °F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP Colorcomp DX98735 PC LNP COLORCOMP* DX98735 is a compound based on Polycarbonate resin containing Proprietary Fillers.This data was supplied by SABIC-IP for the Americas region.
Deflection Temperature at 0.46 MPa (66 psi)	138 Â°C	280 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics PC0700 PC (Europe-Africa-Middle East) PC0700 resin is a low flow (MFR = 7 at 300?C/1.2kg), heat stabilized, polycarbonate product designed for use in the custom compounding market. It does not contain UV stabilizer or mold release. It..
Deflection Temperature at 0.46 MPa (66 psi)	138 Â°C	280 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics PC0703 PC (Europe-Africa-Middle East) PC0703 resin is a low flow (MFR = 7 at 300?C/1.2kg), heat and UV stabilized, polycarbonate product designed for use in the extrusion market.
Deflection Temperature at 0.46 MPa (66 psi)	138 Â°C	280 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics PC0800 PC (Asia Pacific) PC0800 resin is a low flow (MFR = 8 at 300?C/1.2kg), heat stabilized, polycarbonate product designed for use in the custom compounding market. It does not contain UV stabilizer or mold release.
Deflection Temperature at 0.46 MPa (66 psi)	138 Â°C	280 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics PC1000 PC (Asia Pacific) PC1000 resin is a medium-low flow (MFR = 10 at 300?C/1.2kg), heat stabilized, polycarbonate product designed for use in the custom compounding market. It does not contain UV stabilizer or mold rele..
Deflection Temperature at 0.46 MPa (66 psi)	138 Â°C @Thickness 3.20 mm	280 Â°F @Thickness 0.126 in	ASTM D 648
SABIC Innovative Plastics PC1000R PC (Asia Pacific) PC1000R resin is a medium-low flow (MFR = 10 at 300ÂºC/1.2kg), heat stabilized, polycarbonate product with mold release designed for use in the general purpose molding market.This data was supplie..
Deflection Temperature at 0.46 MPa (66 psi)	138 Â°C @Thickness 3.20 mm	280 Â°F @Thickness 0.126 in	ASTM D648
SABIC Innovative Plastics PC1000R PC (Asia Pacific) PC1000R resin is a medium-low flow (MFR = 10 at 300?C/1.2kg), heat stabilized, polycarbonate product with mold release designed for use in the general purpose molding market.
Deflection Temperature at 0.46 MPa (66 psi)	138 Â°C @Thickness 3.20 mm	280 Â°F @Thickness 0.126 in	unannealed; ASTM D 648
SABIC Innovative Plastics LNP Lubricomp ZFL34 PPO LNP* Lubricomp* ZFL34 is a compound based on Modified PPO containing glass fiber and PTFE.This data was supplied by SABIC-IP for the Americas region.
Deflection Temperature at 0.46 MPa (66 psi)	138 Â°C	280 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
SABIC Innovative Plastics LNP LUBRILOY Z2000 PPO LNP* LUBRILOY* Z2000 is a compound based on PPO resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant.
Deflection Temperature at 0.46 MPa (66 psi)	138 Â°C @Thickness 6.40 mm	280 Â°F @Thickness 0.252 in	ASTM D648
Samsung Cheil Industries InfinoÂ® CF-1030 PC, Unreinforced High Impact Information provided by Samsung Cheil Industries.
Deflection Temperature at 0.46 MPa (66 psi)	138 °C	280 °F
Covestro Makrolon® 2803 Polycarbonate, Injection Grade Medium flowing injection molding grade with UV stabilizer.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name ..
Deflection Temperature at 0.46 MPa (66 psi)	138 °C	280 °F	ISO 75-1,-2
Covestro Makrolon® ET2613 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Extrusion• Medium vi..
Deflection Temperature at 0.46 MPa (66 psi)	138 °C @Thickness 0.125 mm	280 °F @Thickness 0.00492 in	ASTM D648
Proto3000 PC Fused Deposition Modeling Polymer Description: A true industrial thermoplastic, PC (polycarbonate) is widely used in automotive, aerospace, medical and many other applications. PC offers accuracy, durability and stability, creating ..
Deflection Temperature at 0.46 MPa (66 psi)	138 °C @Thickness 3.20 mm	280 °F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics LNP LUBRICOMP DFL369XF PC (Asia Pacific) LNP* Lubricomp* DFL369XF is a compound based on Polycarbonate resin containing Glass Fiber, PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Retardant.