- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 198 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 198 °F Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) |
92.0
°C @Thickness 3.20 mm |
198
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Cycoloy® CM6220 PC (Asia Pacific)
CYCOLOY CM6220 resin is a mineral filled grade featuring of high modulus (6GPa), good flow and ductility, low warpage. It is of non-Br & non-Cl flame retardant systems intended to meet thin wall fla..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 - 95.0 °C | 198 - 203 °F | after thermal post treatment procedure B; ASTM D648-06 |
|
Proto3000 Objet Digital Materials™ RGD5160-DM ABS-like Prototyping Polymer
Objet ABS-like Digital Material made of Object RGD515 & Objet RGD535Digital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
92.0
°C @Thickness 3.20 mm |
198
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® BM5225X PC (Asia Pacific)
BM5225X resin is a mineral filled grade featuring of high modulus, good flow and ductility, low warpage. It is of non-Br & non-Cl flame retardant systems intended to meet thin wall flame resistance ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
92.0
°C @Thickness 3.20 mm |
198
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP FARADEX MS003 PP
LNP* FARADEX* MS003 is a compound based on Polypropylene resin containing 15% Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 - 113 °C | 198 - 235 °F | Average value: 102 °C Grade Count:16 |
|
Overview of materials for Polystyrene, Glass Filled
This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene, Glass Filled". Each property range of values reported is minimum and maximum values of appr..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | |
|
Polimeri Europa SINKRAL PD M323 ABS
(discontinued **)
Symbol according to ISO 1043-1: ABS Grade designation according to ISO 2580-ABS 1,MG,095-25-16-25 General purpose injection moulding grade that exhibits outstanding flow and thermal stability duri..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | Annealed, 80°C, 4 hours; ISO 75 |
|
LG Chemical AF-320T ABS, Flame Retardant, High Impact, High Flow, Slim Wall
Information Provided by LG Chem
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.2 °C | 198 °F | Unannealed; ASTM D648 |
|
Global PP-3240-H Polypropylene Random Copolymer
Description-medium stiffness, low melting temperatures, very good for seal Applications-sheets, bottlesInformation provided by Global Polymers Corporation.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | |
|
Ineos ABS Lustran® 348
Key Features:UnfilledSuitable processing methods:Injection molding
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
92.0
°C @Thickness 6.40 mm |
198
°F @Thickness 0.252 in |
Unannealed; ASTM D648 |
|
LG Chemical LUPOY GN5001RFM PC/ABS, Halogen Free Flame Retardant
Description: Injection Molding, PC/ABS, Halogen Free Flame Retardant, General PurposeApplication: E&E (Housing)CAS: 103598-77-2, 9003-56-9 and 181028-79-5Information provided by LG Chemical
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
92.0
°C @Thickness 6.40 mm |
198
°F @Thickness 0.252 in |
Unannealed; ASTM D648 |
|
LG Chemical PI642G ABS, General Purpose, High Modulus
Feature: Extrusion Molding, General Purpose, High ModulusApplication: Pipe fittingCAS No. 9003-56-9Information provided by LG Chemical
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | ASTM D648 |
|
LG Chemical SEETEC R3410 Polypropylene Random Copolymer
Features: Seetec R3410 is a polypropylene-ethylene random copolymer designed for the production of expandable PP and films. It has the good clarity due to the appropriate content of ethylene and off..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
92.0
°C @Thickness 6.40 mm |
198
°F @Thickness 0.252 in |
Unannealed; ASTM D648 |
|
LG Chemical LUPOY ER5001RF PC/ABS
Description: Injection Molding, PC/ABS, Halogen Free Flame Retardant, EPEATApplication: IT&OA (All in One PC & Notebook PC housing)CAS: 103598-77-2, 9003-56-9 and 181028-79-5Information provided by ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | Annealed; ASTM D648 |
|
Spartech Royalite R632M Carbon Black Filled ABS/PVC Resin
Data provided by the manufacturer. This static-conductive material is UL®-listed and meets minimum static-decay requirements outlined in MIL-B-1705B and NFPA Code 56A specifications.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
92.0
°C @Thickness 3.20 mm |
198
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics XYLEX X8303 PC+POLYESTER (Europe-Africa-Middle East)
PC+ POLYESTER, Transparent, Low processing Temperature, High flow with excellent impact, UV stabilized. For In Mold Decoration /Labeling.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
92.0
°C @Thickness 3.20 mm |
198
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Xylex X8303CL PC+POLYESTER
PC+ POLYESTER, Transparent, Low processing Temperature, High flow with excellent impact, UV stabilized, OQ quality. For In Mold Decoration /Labeling.This data was supplied by SABIC-IP for the Americ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
92.0
°C @Thickness 3.20 mm |
198
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics XYLEX X8303CL PC+POLYESTER (Europe-Africa-Middle East)
PC+ POLYESTER, Transparent, Low processing Temperature, High flow with excellent impact, UV stabilized, OQ quality. For In Mold Decoration /Labeling.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.2 °C | 198 °F | Unannealed; ASTM D648 |
|
Techmer ES Plastiblend® ABS 8003 A1
Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer and Impact ModifierFeatures: Heat Stabilized and Impact ModifiedProcessing Method: Injection MoldingInformation provided by TP Comp..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
92.2
°C @Thickness 3.17 mm |
198
°F @Thickness 0.125 in |
Unannealed; ASTM D648 |
|
Chase Plastics CP Pryme® A300 BK General Purpose (Utility) ABS Molding Resin
Information provided by Chase Plastics.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | 120°C per hour; ISO 75-2 |
|
Total PPC 4663 Polypropylene, Heterophasic Copolymer
ATOFINA Polypropylene PPC 4663 is heterophasic copolymer. PPC 4663 is characterized by a combination of ease of processing and good manufacturing article properties in applications ranging from hou..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | Annealed; ASTM Data |
|
Dow Prevail® 3100 ABS + Polyurethane
PREVAIL® 3100 thermoplastic resin offers designers and manufacturers a combination of flexibility and low temperature toughness not previously available in an engineering thermoplastic and is used ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | Unannealed; ASTM Data |
|
Dow Tyril® 1011 SAN
TYRIL® 1011 SAN copolymer is a light stabilized general purpose injection molding resin available in crystone color only. It exhibits excellent weathering characteristics, high strength, good chemi..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | |
|
BASF Polystyrol® 456 F Impact Grade Polystyrene (Europe)
Heat distortion resistant, good flowing grade for parts subjected to heat.Data was collected by ISO methods and provided by BASF.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.2 °C | 198 °F | ASTM D648 |
|
Americas Styrenics STYRON® 421 High Impact Polystyrene
Product CharacteristicsStiffness/FlowHeat resistanceContact clarityFood Contact CompliantUL Classification 94HBTypical ApplicationsAppliancesRefrigerationPackaging/disposablesConsumer electronicsInf..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | ASTM D648 |
|
Bapolene® 4022 Polypropylene, Biaxially Oriented Film Grade
Bapolene PP4022 is a PP homopolymer designed for oriented film applications. It offers good clarity and optical properties. This resin meets FDA standards for food contact applications.Application..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | 120°C per hour; ISO 752 |
|
Total PPC 3120 MU5 Polypropylene, Heterophasic Copolymer, Automotive
Polypropylene PPC 3120 MU5 is a heterophasic copolymer with a Melt Flow index of 15 g/10 min. Polypropylene PPC 3120 MU5 is a high impact copolymer formulated to give good UV resistance.Polypropyle..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | unannealed; ASTM D648 |
|
Phillips 66 COPYLENE® CM360N Polypropylene, Impact Copolymer, Injection Molding
COPYLENE® CM360N is a high melt flow, no-break impact polypropylene copolymer resin designed for injection molding applications requiring a good balance of stiffness, impact, resistance and process..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | |
|
Ineos ABS Centrex® 825 ASA+AES Blend
(discontinued **)
Key Features:UnfilledHigh impact or high impact modifiedLight stabilized or stable to lightU.V. stabilized or stable to weatherSuitable processing methods:Profile extrusionSheet extrusionThermoformi..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 92.0 °C | 198 °F | ASTM D648 |
|
Braskem H 401 Cast Film Extrusion Polypropylene
Description: H 401 is a medium melt flow rate homopolymer polypropylene, additived with slip and antiblocking agents. Designed specially for cast film. This product features good impact strength, ex..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
92.0
°C @Thickness 6.35 mm |
198
°F @Thickness 0.250 in |
ASTM D648 |
|
IRPC Polimaxx Porene KU900 Acrylonitrile Butadiene Styrene
Applications:extrusion sheetrefrigerator door liners and inner box linerspicnic coolerssnow boatsluggage cases
|
|||