- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 210 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 210 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75 |
|
Nilit FRIANYL B63 H-GV15 Nylon 6 for injection molding, 15% glass fiber reinforced
Nylon 6 for injection molding, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ASTM D648 |
|
LG Chemical Lupox® PBT-GP-2150 15% GFR PBT
Information provided by US distributor Polymer Technology and Services, LLC (PTS).
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 - 215 °C | 410 - 419 °F | ASTM D1525, HDT Method B |
|
Loxim 230 01HB Polybutylene Terephthalate
Information provided by Loxim Industries
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75-1, -2 |
|
Lanxess Durethan® BKV 130 GIT DUS008 900116 Nylon 6, Impact Modified
PA 6, 30% glass fibers, injection molding, impact modified, GIT/WITInformation provided by LANXESS.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75-1/-2 |
|
Lanxess Durethan® BKV 140 H2.0 900051 Copolyamide, 40% Glass Fiber
CoPA, injection molding grade, 40% glass fibers, elastomer-modified, electroplateable, higher notched impact strength and also higher energy absorption under biaxial impact load than BKV 40, even in..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
210
°C @Thickness 6.40 mm |
410
°F @Thickness 0.252 in |
Unannealed; ASTM D648 |
|
LG Chemical Lupox® GP2156FM PBT+GF15%
Description: Injection Molding, PBT+GF15%, Flame Retardant Application: IT/OA, E&E (CRT Socket)CAS No. 68928-70-1, 65997-17-3, 24968-12-5 and 1309-64-4Information provided by LG Chemical
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ASTM D648 |
|
LG Chemical Lupox® SG-4405 Surface Gloss PBT, 40% Glass Fiber/Mineral Reinforced, Dimensional Stability
LUPOX semi-crystalline thermoplastic PBT resins exhibit properties including high strength, rigidity and good resistance to fatigue and creep at elevated temperatures. Furthermore, LUPOX resins sho..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | |
|
LATI Kelon® B FR H CETG/250-V0 PA 6, Glass/Mineral Reinforced, Flame Retardant, Heat Stabilized
Polyamide 6 (PA6) based compound. Heat stabilized. Glass fibers / Mineral filler. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free.Availability: Africa & Middle East; Asia Pacifi..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | V-notch; ISO R 75 |
|
Schwartz Technical Plastics LAMIGAMID® 310 Cast Polyamide 6, Conditioned
Application: sheaves, wheels, rollers, mandrell segments, coupling parts, vibrator parts etc.Information provided by Schwartz Technical Plastics GmbH
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | V-notch; ISO R 75 |
|
Schwartz Technical Plastics LAMIGAMID® 324 Cast Polyamide 6, MoS2, Heat Stabilized, Dry
Application: heavy-duty wheels, running speed up to 3m/sInformation provided by Schwartz Technical Plastics GmbH
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
210
°C @Thickness 6.40 mm |
410
°F @Thickness 0.252 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM 1000R PEI (Asia Pacific)
Standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0, V2 and 5VA listing.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
210
°C @Thickness 6.40 mm |
410
°F @Thickness 0.252 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Ultem 2200N PEI (Asia Pacific)
20% Glass fiber filled Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacific region.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
|
SABIC Innovative Plastics ULTEM UF5011S PEI
Enhanced flow, Specialty filtered Polyetherimide (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics and ketones. ECO Conforming.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75 |
|
Ter Hell Plastic Terez® PA 6 7500 GF 30 Polyamide 6, 30% Glass Fiber Reinforced
Description: Medium viscosity Polyamide 6, 30% glass fiber reinforced, good flowability, good impact resistance and bright natural color.Application: For molding parts with good stiffness and good..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | >= 210 °C | >= 410 °F | DIN 53461 |
|
Polyram PlusTek RB300G6 Nylon 6, 30% Glass Fiber
30% glass-fiber reinforced polyamide 6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75 |
|
A. Schulman SCHULAMID® 66 MK40HI 40% Mineral Reinforced, Impact Modified 66
Information provided by A. Schulman.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 179 |
|
CP-Polymer-Technik Wellamid® 6600 MR 209 HWCP 20% Mineral Nylon 66, Heat Stabilized, Dry
Information provided by CP-Polymer-Technik GmbH & Co. KG
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | 1/4''; ASTM D648 |
|
Ensinger TECAPEI® 10% Glass Reinforced, made from Ultem® 2100 PEI
TECAPEI™ is an amorphous thermoplastic polyetherimide (PEI) made from Sabic Innovative Plastics' Ultem® 1000 and 2000 series resins. The unreinforced 1000 series materials are translucent amber in..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | DAM; ISO 75-1/-2 |
|
DuPont Performance Polymers Minlon® 11C40 BKB086 Nylon 66
(Unverified Data**)
40% Mineral Reinforced Polyamide 66 Minlon 11C40 BKB086 is a 40% mineral reinforced heat stabilized black polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Be |
|
Eurostar Starflam AFR200Y PA66, Flame Retardant, Injection Molding
Staramide AFR200Y is an Unfilled, Halogen Free and Red Phosphorous Free, Flame Retardant Polyamide 66, Injection Molding ResinInformation provided by Eurostar.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ASTM D648 |
|
E-Polymers TEKAMID® TB120GM20 , 20% GF/MF Reinforced PA6, DAM
20% GF/MF reinforced, Good surface, Low warpageInformation provided by E-Polymers Co. Ltd.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ASTM D648 |
|
Adell BR-13 Nylon 6, 15% Glass Reinforced
Data provided by Adell Plastics, Inc.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ASTM D648 |
|
Gromax CCP PBT 5630-104C 30% Glass Fiber Filled
Product Description: A glass fiber 30% reinforced injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature Excellent ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ASTM D648 |
|
Gromax CCP PBT 5630-200C 30% Glass Fiber Filled
Product Description: A glass fiber 30% reinforced injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature Excellent ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | |
|
LATI Kelon® A FR H2 CET/35-V2 PA 66, 35% Mineral Reinforced, Flame Retardant, Heat Stabilized
Polyamide 66 (PA66) based compound. Heat stabilized. Mineral filler. UL94 V-2 classified, with brominated flame retardants, PBB/PBDE free.Availability: Africa & Middle East; Asia Pacific; Europe; La..
|
|||