- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 214 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 214 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 418 °F | ASTM D648 |
|
Polymer Resources PEI-G40 Polyetherimide, 40% Glass Reinforced
Polyetherimide, 40% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Poly..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ISO 75 |
|
GEHR Plastics PPSU Polyphenylenesulfone
Polyphenylenesulfone is an amorphous material, with improved impact and hydrolysis resistance compared to PSU. The usual operating temperature is approximately 180°C. The extremely high notched i..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ISO 75-1, -2 |
|
Lanxess Durethan® A 30 S H3.0 000000 Nylon 66, Injection Molding
PA 66, non-reinforced, injection moldingInformation provided by LANXESS.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
214
°C <br>@Thickness 3.20 mm
|
417
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP IFP36 PA6.12
LNP* LUBRICOMP* IFP36 is a Nylon 6/12 base resin containing 30% Glass Fiber, 15% PTFE/Silicone. Added features of t his grade include: Wear Resistant.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
214
°C <br>@Thickness 6.40 mm
|
417
°F <br>@Thickness 0.252 in
|
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Ultem DH1004F PEI (Asia Pacific)
High Temperature, Transparent, Polyetherimide Blend with Improved Ductility and Enhanced Hydrostability. US FDA and EU Food Contact compliant.This data was supplied by SABIC-IP for the Asia Pacific ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
214
°C <br>@Thickness 6.40 mm
|
417
°F <br>@Thickness 0.252 in
|
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Ultem DH1004F PEI (Europe-Africa-Middle East)
High Temperature, Transparent, Polyetherimide Blend with Improved Ductility and Enhanced Hydrostability. US FDA and EU Food Contact compliant.This data was supplied by SABIC-IP for the Europe-Africa..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
214
°C <br>@Thickness 6.40 mm
|
417
°F <br>@Thickness 0.252 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM HU1004 PEI
High Temperature, Transparent, Polyetherimide Blend with Improved Ductility and Enhanced Hydrostability. For medical devices and pharmaceutical applications. Healthcare management of change, biocomp..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
214
°C <br>@Thickness 6.40 mm
|
417
°F <br>@Thickness 0.252 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM HU1004 PEI (Asia Pacific)
High Temperature, Transparent, Polyetherimide Blend with Improved Ductility and Enhanced Hydrostability. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI) and FDA and EUFC f..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
214
°C <br>@Thickness 6.40 mm
|
417
°F <br>@Thickness 0.252 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM HU1004 PEI (Europe-Africa-Middle East)
High Temperature, Transparent, Polyetherimide Blend with Improved Ductility and Enhanced Hydrostability. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI) and FDA and EUFC f..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | Unannealed; ASTM D648 |
|
Solvay Specialty Polymers Radel® R-5100 Polyphenylsulfone (PPSU), Filled
Radel® R-5100 is an opaque, general purpose polyphenylsulfone (PPSU) for injection molding, that offers exceptional hydrolytic stability, and toughness superior to other commercially-available, h..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP STAT-KON EEF42 PEI
LNP STAT-KON* EEF42 is a compound based on Polyetherimide resin containing 10% Carbon Fiber, 20% Glass Fiber. Added features of this material include: Electrically Conductive.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP STAT-KON PFD04S PA 6 (Europe-Africa-Middle East)
LNP* Statkon* PFD04S is a compound based on PA 6 resin containing Glass Fiber, Carbon Powder. Added features include: Electrically Conductive, Heat Stabilized.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 418 °F | Unannealed; ASTM D648 |
|
Techmer ES HiFill® PEI BK
Availability: North AmericaForms: PelletsAppearance: BlackInformation provided by TP Composites, Inc.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 418 °F | Unannealed; ASTM D648 |
|
Techmer ES HiFill® PEI HF BK
Availability: North AmericaForms: PelletsFeatures: High FlowAppearance: BlackInformation provided by TP Composites, Inc.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP THERMOCOMP IF00C PA6.12
LNP* THERMOCOMP* IF00C is a compound based on Nylon 6/12 resin containing 60% Glass Fiber.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP THERMOCOMP JF003XXZ PES
LNP* THERMOCOMP* JF003XXZ is a compound based on Polyethersulfone resin containing 15% Glass Fiber.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ASTM D648 |
|
Samyang Tramid® 215 Polyamide, High Impact
Strong with excellent thermal resistance. Abrasion resistance, chemical resistance and oil resistance are excellent.215 is a high impact grade.Applications:Automotive knob types, door handles and m..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
214
°C <br>@Thickness 3.20 mm
|
417
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOTUF IX02582 PA6.12
LNP* Thermotuf* IX02582 is a compound based on Nylon 6/12 resin containing Proprietary Filler(s). Added features of this material include: High Impact.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
214
°C <br>@Thickness 6.40 mm
|
417
°F <br>@Thickness 0.252 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics ULTEM 9090 PEI
Polyetherimide Blend with improved Ductility and Detergent resistance. Meets FAR 25.853 and OSU 55/55 heat release and provides low toxicity, smoke and flame evolution.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
214
°C <br>@Thickness 3.20 mm
|
417
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP 9X10401H ABS
LNP* THERMOCOMP* 9X10401H is a compound based on Polyphenylsulfone containing proprietary filler(s). Added feature of this grade is: X-Ray Opaque.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
214
°C <br>@Thickness 6.40 mm
|
417
°F <br>@Thickness 0.252 in
|
ASTM D648 |
|
Samsung Cheil Industries Infino® VB-5150GL PBT, 15% Glass Filled FR
Information provided by Samsung Cheil Industries.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ASTM D648 |
|
Westlake Plastics Polyethersulfone
High resistance to heat and combustibility, low smoke emission, and transparency are the combination of properties possessed by stock shapes extruded from PES. These, coupled with light weight, good..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ASTM D648 |
|
Westlake Plastics Radel® R 5500 Polyphenylsulfone
Stock shapes extruded from Radel R resins offer a superior combination of high performance properties that include excellent thermal stability, outstanding toughness, and good environmental stress c..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ASTM D648 |
|
Westlake Plastics Radel® R Polyphenylsulfone
Stock shapes extruded from Radel R resins offer a superior combination of high performance properties that include excellent thermal stability, outstanding toughness and good environmental stress cr..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ISO 75-1/-2 |
|
BASF Ultramid® B35G3 BK 00564 15% Glass Filled PA6 (Dry)
Description: 15% glass fiber reinforced injection molding grade e.g. for internal gas pressure applications such as flashing direction switch gears, automobile mirror housings and wheels of mountain..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ISO 75 |
|
BASF Ultramid® B3GM35 BKQ642 23220 15/25% Glass/Mineral Filled PA6 (Dry)
Ultramid B3GM35 BKQ642 23220 is a 40% combined glass-fiber and mineral reinforced, pigmented black injection molding PA6 grade.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ASTM D648 |
|
A. Schulman ComAlloy Comtuf® 615 Nylon 6, Glass Reinforced, Impact Modified
Data provided by the manufacturer, ComAlloy International Company.45% Glass Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been int..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ISO 75 |
|
BASF Ultradur B 4040 G4 LS High Speed BK15029 20% Glass Filled PBT/PET |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP VERTON PX00700 PA 6
LNP VERTON* PX00700 is a compound based on Nylon 6 resin containing proprietary fillers. Added feature of this grade is: Structural.
|
|||