- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 235 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 235 °F Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ASTM D648 |
|
RheTech Products T10UP100-01 10% Talc Reinforced Polypropylene Copolymer, General Purpose Black, UL94 HB Rated
Applications: Wire troughElectrical componentsConsumer goodsInjection molding conditions reported in table.Information provided by RheTech Products.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ASTM D648 |
|
Polymer Resources PC/ABS-GP1-[color]-UV General Purpose PC/ABS Alloy, UV-stabilized
PC/ABS Alloy, General Purpose, UV-stabilized Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provide..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ASTM D648 |
|
Polymer Resources PPX-GP3 Modified-PPO, General Purpose
Modified-Polyphenylene Oxide, General Purpose, 235F HDTFeatures: • Hydrolytically Stable • Low to No Water AbsorptionProcess: Injection MoldingNotes: All physical, mechanical and thermal testing..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ASTM D648 |
|
Polymer Resources PPX-GP3-IM Modified-PPO, Impact Modified
Modified-Polyphenylene Oxide, Impact Modified, 235F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informati..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ASTM D648 |
|
Polymer Resources PPX-GP3-WR Modified-PPO, Wear Resistant
Modified-Polyphenylene Oxide, Wear Resistant, 235F HDTFeatures: • Hydrolytically Stable • Low to No Water Absorption • Good Wear ResistanceProcess: Injection MoldingNotes: All physical, mechan..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ASTM D648 |
|
Polymer Resources PC/ABS-GP1-[color]-LG General Purpose PC/ABS Alloy, Low Gloss Grade
PC/ABS Alloy, General Purpose, Low Gloss GradeProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provid..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ASTM D648 |
|
Kolon NOPLA® KE911 PEN-PET Copolyester
NOPLA® is an advanced PEN-PET copolyester which can be used for bottle, sheet & injection molding applicationsUV protection & prolonged outdoor durability, enhanced gas barrier, outstanding impac..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ASTM D648 |
|
Ineos N05U-00 Polypropylene Impact Copolymer
This is an extrusion-grade nucleated impact copolymer polypropylene resin designed for fiber optic buffer tube applications in the protection of glass fibers. It also has an excellent impact/stiffn..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
113
°C @Thickness 6.40 mm |
235
°F @Thickness 0.252 in |
Unannealed; ASTM D648 |
|
LG Chemical XR407D ABS
Feature: Electric & Electronic HousingApplication: Electric & Electronic HousingCAS No. 25120-20-1, 9003-56-9, 25747-74-7, and 31621-07-5Information provided by LG Chemical
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
113
°C @Thickness 6.40 mm |
235
°F @Thickness 0.252 in |
Unannealed; ASTM D648 |
|
LG Chemical XR407E ABS, Heat Resistance
Feature: Injection Molding, Heat ResistanceApplication: Electric & Electronic Housing (MWO Frame, DVD inner part etc)CAS No. 25120-20-1, 9003-56-9, 25747-74-7, and 31621-07-5Information provided by..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | Unannealed; ASTM D648 |
|
Techmer ES Electrablend® ABS CF10 10% Carbon Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 10% Filler by WeightInformation provided by TP Composites, Inc.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | Unannealed; ASTM D648 |
|
Techmer ES Electrablend® ABS CF15 BK 15% Carbon Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 15% Filler by WeightAppearance: BlackInformation provided by TP Composites, Inc.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | Unannealed; ASTM D648 |
|
Techmer ES Electrablend® ABS CF30 BK 30% Carbon Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 30% Filler by WeightAppearance: BlackInformation provided by TP Composites, Inc.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | Unannealed; ASTM D648 |
|
Techmer ES HiFill® ABS GF60 BK 60% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 60% Filler by WeightAppearance: BlackInformation provided by TP Composites, Inc.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP Stat-kon ZE0039 MODIFIED POYPHENYLENE
LNP* Stat-kon* ZE0039 is a compound based on MODIFIED POYPHENYLENE resin containing Carbon Fiber.This data was supplied by SABIC-IP for the Americas region.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | Unannealed; ASTM D648 |
|
Techmer ES HiFill® PP GB20 20% Glass Beads Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Bead, 20% Filler by WeightInformation provided by TP Composites, Inc.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | Unannealed; ASTM D648 |
|
Techmer ES Luriblend® TPX-PPO/HIPS-02072 BK
Availability: North AmericaForms: PelletsAdditive: PTFE LubricantFeatures: Lubricated, Good Wear Resistance, Low Friction and HomopolymerUL File Number: E157318Information provided by TP Composites,..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ISO 75 |
|
Styrolution Luran® S KR2866C ASA / PC
Luran S KR2866C is a blend of ASA and PC with a reduced content of PC. It is characterized by a medium impact toughness and heat resistance.Good heat resistanceMedium impact strengthInformation prov..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ISO 75 |
|
Styrolution Novodur® HH-112 ABS
Novodur HH-112 is a high heat injection molding grade. It provides good heat resistance combined with enhanced stiffness.Information provided by Styrolution
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ISO 75 |
|
Styrolution Terluran® HH-112 ABS
Terluran HH-112 is an injection molding grade of ABS with very high heat resistance.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | Unannealed; ISO 75-2/Bf |
|
Styron INSPIREâ„¢ DTF8000 ES Compounded Polypropylene
Overview: INSPIREâ„¢ TF 8000 ES is a superior scratch and mar resistant low gloss talc filled interior grad TPO exhibiting excellent low temperature ductility, high modulus and heat performance.M..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
113
°C @Thickness 3.20 mm |
235
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics NORYL PPX PPX7110 PPE+PP (Asia Pacific)
PPE+PP blend. High Impact, Good Heat Resistance
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
113
°C @Thickness 6.40 mm |
235
°F @Thickness 0.252 in |
ASTM D648 |
|
Samsung Cheil Industries Infino® HI-1001BN PC/ABS, Unreinforced
PC/ABS that is used for the housing of mobile phone, wheel cap, rice cooker, electric iron etc., refrigerator door handle, panel etc.Information provided by Samsung Cheil Industries.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ASTM D648 |
|
Plastics Group Polifil® C-40 40% Calcium Carbonate-Reinforced Polypropylene
Polifil® C series compounds are homopolymer polypropylene resins reinforced with fine particle size calcium carbonate. They combine high impact with stiffness, heat aging, good colorability, resist..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ASTM D648 |
|
A. Schulman POLYFORT™ FPP 1182E Talc Filled, Extrusion Grade Copolymer Polypropylene
DescriptionPolyfort® FPP 1182E is a 20% talc-filled, extrusion grade copolymer polypropylene. It had a good balance of flexural modulus, low temperature impact, and appearance properties. Informat..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ASTM D648 |
|
A. Schulman POLYFORT™ FPP 1182E Talc Filled, Extrusion Grade Copolymer Polypropylene
DescriptionPolyfort® FPP 1182E is a 20% talc-filled, extrusion grade copolymer polypropylene. It had a good balance of flexural modulus, low temperature impact, and appearance properties. Informat..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ISO 75-2/B |
|
ExxonMobil Exxtral™ CMV 205 Performance Polyolefin
Product Description: A specialty thermoplastic polyolefin resin characterized by high stiffness and designed for automotive interior applications in which good surface finish and good UV resistance ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ASTM D648 |
|
Aaron Industries AAROPRENE® CFPP 2040 Calcium Carbonate Filled Polypropylene
AAROPRENE® CFPP 2000 Series Reinforced CompoundsMelt flow index may be specified. Color may be specified.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | 120°C/h; ISO 75/1 |
|
Polykemi AB POLYfill PP HJ752 UV2 Polypropylene/Elastomer, Mineral Reinforced
Information provided by Polykemi AB
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ASTM D648 |
|
E-Polymers Tekaloy® S630X , High Impact, Weather Resistance, Chemical Resistance PC/PBT Alloy
High impact, weather resistance, chemical resistanceInformation provided by E-Polymers Co. Ltd.
|
|||