- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 239 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 239 °F Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | 120°C/h; ISO 75/1 |
|
Polykemi AB POLYblend C65F PC/ABS-blend
Information provided by Polykemi AB
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
115
°C <br>@Thickness 3.20 mm
|
239
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Cycoloy® CX5430 PC+ABS
Cycoloy* resin CX5430 is a general purpose PC/ABS blend developed for thin wall applications requiring weld line strength, high flow and impact together with a good balance of other properties.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | 120°C/h; ISO 75/1 |
|
Polykemi AB POLYfill PPC T1030 Polypropylene Copolymer, Mineral Reinforced
Information provided by Polykemi AB
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | 120°C/h; ISO 75/1 |
|
Polykemi AB POLYfill PPC T4030 E20 Polypropylene Copolymer, Mineral Reinforced, Elastomer Modified
Information provided by Polykemi AB
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
115
°C <br>@Thickness 3.20 mm
|
239
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Cycoloy® MC1300 PC+ABS
Cycoloy MC1300 resin is an injection moldable PC/ABS blend with excellent flow and impact performance. It is designed for plating applications mostly used in the automotive industry.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
|
LyondellBasell Pro-fax SV954 Polypropylene Impact Copolymer
Key Features: nucleation shortens cycles for higher productivity, resists dirt and dust pick-up, good cold impact resistance, good stiffness and impact balance, high flow for ease of mold filling an..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
|
Flint Hills P4C5K-123A Homopolymer Polypropylene
Homopolymer, and FDA compliant.Features: Clarified, antistat, and controlled rheologyApplications: Injection molding: clear containers.Former Huntsman polypropylene products are now produced by Flin..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
115
°C <br>@Thickness 3.20 mm
|
239
°F <br>@Thickness 0.126 in
|
Unannealed; ASTM D648 |
|
LG Chemical LUPOL EI5002 PP
Description: Injection Molding, PP, General PurposeApplication: Automotive Interior PartsCAS: 9003-07-0, 9010-79-1 and 9002-88-4Information provided by LG Chemical
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
|
Kolon NOPLA® KE931 PEN-PET Copolyester
NOPLA® is an advanced PEN-PET copolyester which can be used for bottle, sheet & injection molding applicationsUV protection & prolonged outdoor durability, enhanced gas barrier, outstanding impac..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
115
°C <br>@Thickness 6.40 mm
|
239
°F <br>@Thickness 0.252 in
|
Unannealed; ASTM D648 |
|
LG Chemical LUPOL TE5108H PP+Rubber+MF, High Impact
Description: Injection Molding, PP+Rubber+MF, High Impact, Good WeatherabilityApplication: Automotive Exterior (Bumper Fascia, Rear Bumper Step)Information provided by LG Chemical
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
115
°C <br>@Thickness 6.40 mm
|
239
°F <br>@Thickness 0.252 in
|
Unannealed; ASTM D648 |
|
LG Chemical LUPOL TE5109 PP+Rubber+MF, High Impact
Description: Injection Molding, PP+Rubber+MF, High Impact, Good WeatherabilityApplication: Automotive Exterior (Bumper Fascia, Rear Bumper Step)Information provided by LG Chemical
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 - 125 °C | 239 - 257 °F | ASTM D1525, HDT Method B |
|
Loxim 830 02T HB Polypropylene Compound, 30% Talc Filled, Flame Retardant
Information provided by Loxim Industries
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | |
|
LATI Latistat 52/7-02 PP Homopolymer
Dissipative product based on Polypropylene homopolymer (PPh). Unfilled. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria T..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
115
°C <br>@Thickness 3.20 mm
|
239
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP ML004 PP
LNP* LUBRICOMP* ML004 is a product based on Polypropylene containing 20% PTFE. Added features of this grade include: Wear Resistant.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
115
°C <br>@Thickness 6.40 mm
|
239
°F <br>@Thickness 0.252 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Xenoy® 1731 PBT+PC (Asia Pacific)
Impact/chemical resistant. UV-Stabilized. Excellent physical property retention in automotive exteriors and OVAD.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
|
SABIC Innovative Plastics Noryl PKN4766 PPE+HIPS (Europe-Africa-Middle East)
NORYL PKN4766 is a translucent PPO+PS extrusion grade for dilution with polystyrene resin. It is suitable for (microwavable) food packaging and is compliant with US and European food contact regulat..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
|
A. Schulman POLYFORT™ FXP 2779U UV Stabilized Copolymer Polypropylene
DescriptionPolyfort® FXP 2779U is a 20% talc-filled, UV stabilized copolymer polypropylene.Information provided by A. Schulman.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | GB1634 |
|
Zhejiang Juner JEPP2007 PP For Automotive Parts
Applications: Inner Decorate PartsInformation provided by Zhejiang Juner New Materials Co, Ltd.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
|
A. Schulman POLYFORT™ FPP 1182 Talc Fortified Impact Resistant Polypropylene
DescriptionPolyfort® FPP 1182 is a 20% talc fortified impact resistant polypropylene.Information provided by A. Schulman.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
|
A. Schulman POLYFORT™ FXP 2779U UV Stabilized Copolymer Polypropylene
DescriptionPolyfort® FXP 2779U is a 20% talc-filled, UV stabilized copolymer polypropylene.Information provided by A. Schulman.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75-1/-2 |
|
Covestro Makroblend® S 7916/2 Polycarbonate + PBT, Impact Grade
ISO 7792-1-PBT/PC,MHPR,-020(PBT+PC)-blendsimpact modifiedInjection molding gradeexcellent chemical resistancehigh toughness at low temperaturesideal for painted applicationsunreinforcedPreprocessing..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75-1/-2 |
|
EMS-Grivory Grivory® 2D 25 W 20 X black PA612-I
Product Description: Grilamid 2D 25 W 20 X black 9992 is a semi-flexible high viscosity, plasticized, high impact, heat and UV resistant extrusion grade based on polyamide 612 (PA612). Unique proper..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75-1/-2 |
|
EMS-Grivory Grivory® L 20 G PA12
Product Description: Grilamid L 20 LG is a normal viscosity, heat stabilized polyamide 12 non-reinforced injection molding grade. This product has very good flow characteristics Low moisture absorpt..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75-1/-2 |
|
EMS-Grivory Grivory® L 25 nat 6112 PA12
Product Description: Grilamid L 25 natural 6112 is a high viscous, Polyamide 12 extrusion grade. Grilamid L 25 natural 6112 fulfils the requirements of DIN 73378, Type PA 12-H. Application examples:..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
|
Aclo Accutech Polypropylene Copolymer CP0436W40L1 Wollastonite Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
|
Aclo Accutech Polypropylene Homopolymer HP0339C30L Calcium Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
|
Aclo Accutech Polypropylene Homopolymer HP0339T10L Talc Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75-1/-2 |
|
DSM Arnitel® EL630 Polyether Ester Elastomer (European and Asian Grade)
Product description: Arnitel® combines the advantages of engineering thermoplastics, being easy to process with excellent mechanical properties, at the same time with the flexibility of rubbers.Arn..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
115
°C <br>@Thickness 3.20 mm
|
239
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Cycoloy® CX1440 PC+ABS (Asia Pacific)
CYCOLOY CX1440 is a general purpose PC+ABS blend specially developped for thin wall applications requiring weld line strength and high flow with a good balance of properties
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
|
Aclo Accutech TPO TPO030T9V Paintable Grade