- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 255 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 255 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | ISO 75, ASTM D648 |
|
Nilit Nilamid A G7 FR PH1 35% Glass Fiber Reinforced, Flame Retardant PA66 (with Red Phosphorous)
Description: Nilamid A G7 FR PH1 combines flame retardancy with outstanding mechanical performance. This product has a UL 94 V0 listing 1.5 and a complete yellow card. The formulation has been optim..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | ISO 75, ASTM D648 |
|
Nilit Nilamid A3 H G4 General Purpose 20% Glass Reinforced PA66
Description: Nilamid A3 H G4 is a general purpose, 20% glass fiber reinforced NYLON 66. This product combine good overall mechanical performance and impact strength with ease of processing.Key chara..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | ISO 75, ASTM D648 |
|
Nilit Nilamid A3 H6 G5 25% Glass Reinforced PA66
Description: Nilamid A3 H6 G5 is a 25% glass fiber reinforced NYLON 66 with a special stabilization system against hot oil and grease. As a result of this stabilization, the material has a brown nat..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
255
°C <br>@Thickness 6.40 mm
|
491
°F <br>@Thickness 0.252 in
|
Unannealed; ASTM D648 |
|
LG Chemical LUMID GP2130B(W) PA66+GF13%, General Purpose
Feature: Injection Molding, PA66+GF13%, General PurposeApplication: Valve CoversCAS No. 32131-17-2, 65997-17-3 and 9010-79-9Information provided by LG Chemical
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | |
|
LATI Latamid 66 H2E21 G/13 PA 66, 13% Glass Fiber Reinforced
Polyamide 66 (PA66) based compound. Heat stabilized. Toughened. Glass fibers. High impact resistance. Good impact resistance even at low temperature.Availability: Africa & Middle East; Asia Pacific;..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | |
|
LATI Latamid 66 H2 G/25-V0CT1 PA 66, 25% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant
Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free. Availability: Africa & Middle East; Asia Pacific; Europe; Lat..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | Unannealed; ASTM D648 |
|
Techmer ES HiFill® PA6/6 0135 BL069 13% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 13% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures: Lubricated and Heat StabilizedAppearanc..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | Unannealed; ASTM D648 |
|
Techmer ES HiFill® PA6/6 G/CF30 L BK 30% GlassCarbon Filler
Availability: North AmericaForms: PelletsFiller/Reinforcement: GlassCarbon Fiber Reinforcement, 30% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Heat Stabilized and LubricatedApp..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | Unannealed; ASTM D648 |
|
Techmer ES HiFill® PA6/6 GF27 SL2 27% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 27% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Lubricated and Heat StabilizedInformati..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | ASTM D648 |
|
SPS Guang Zhou PONYLâ„¢ EP4003G20 Non-halogen flame retardance/GF20%-PA66
Characteristic: Good flame retardance, high mechanical properties, superior heat resistance, good dimensional stabilityApplications: E/E partsInformation Provided by SPS (Guang Zhou) Ltd.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP STAT-KON RX05489 PA 66
LNP* STAT-KON* RX05489 is a compound based on Nylon 66 resin containing 10% Carbon Fiber, 20% Glass Fiber, 15% PTFE/Silicone. Added features of this material include: Electrically Conductive, Wear..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | Unannealed; ASTM D648 |
|
Techmer ES Luriblend® PA6/6 GF13 SL2 13% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 13% Filler by WeightAdditive: Heat Stabilizer and Silicone LubricantFeatures: Lubricated and Heat StabilizedInformation pr..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
255
°C <br>@Thickness 3.20 mm
|
491
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP RF0049SP PA 66
LNP* THERMOCOMP* RF0049SP is a compound based on Nylon 66 containing 20% Glass Fiber. Added features of this grade include: Flame Retardant, Heat Stabilized.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
255
°C <br>@Thickness 3.20 mm
|
491
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics LNP Thermocomp RF004S PA 66
LNP* Thermocomp* RF004S is a Nylon 6/6 containing Glass Fiber. Characteristics are Heat Stabilized.This data was supplied by SABIC-IP for the Americas region.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP Thermocomp RF006PS PA 66
LNP* Thermocomp* RF-1006 EP HS is based on Nylon 6/6 containing Glass Fiber. Characteristics of this grade include Exceptional Processing and Heat Stabilizer.This data was supplied by SABIC-IP for ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP THERMOCOMP RF006S PA 66
LNP* THERMOCOMP* RF006S is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include: Heat Stabilized.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
255
°C <br>@Thickness 3.20 mm
|
491
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP RX06421S PA 66
LNP* Thermocomp* RX06421S is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Easy Molding.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP STAT-KON RE0069S PA 66
LNP* STAT-KON* RE0069S is a compound based on Nylon 66 resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant, Heat Stabilized.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | Unannealed; ASTM D648 |
|
Techmer ES HiFill® PA6/6 GF33 HS L GY 33% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures: Lubricated and Heat StabilizedAppearanc..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | DIN 53461 |
|
Polyram RamSter PE300J6 PET, 30% Glass Fiber and Glass Bead Reinforced
30% Glass-fiber and glass beads reinforced, high stiffness PET for injection molding applications.Information provided by Polyram Ram On Ind.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | ISO 75-1/-2 |
|
DSM Akulon® S223-HPG5 Impact Modified Nylon 66-25% Glass Reinforced (European Grade) (Dry)
The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Be |
|
Eurostar Staramide ACF4 PA66, 20% Carbon Fiber Reinforced, Heat stabilized, Injection Molding
Staramide ACF3 is a 20% Carbon Fiber Reinforced Polyamide 66, Injection Molding ResinInformation provided by Eurostar.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Bf |
|
Eurostar Starflam AFR470X2 PA66, 35% Glass Filled, Injection Molded
AFR470X2 is a Red Phosphorous, Flame Retardant, Glass Fiber Reinforced, Polyamide 66 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive suppli..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | ISO 75-1/2 |
|
Eurotec® Tecomid® NA40 GR25 NL XA 42 PA 6.6 25% glass fiber reinforced, UL94 V0, red phosphorus
Excellent stiffness/toughness balanceHigh mechanical strengthVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance and low frictionVery good..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | ISO 75 |
|
Eurotec® Tecopet® PT70 GR30 NL100 XD70 PET, 30% glass fiber reinforced, flame retardant - halogen (RoHS compliant), long-term heat stabilized, natural
Information provided by Eurotec®
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | ASTM D648 |
|
ABW Polymers PC/PET Alloy
Typical property data below. Material may be tailored to meet specific requirements. This data should be used only as a guide and no assurance can be granted by the company that all molded articles..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | ISO 75 |
|
BASF Ultramid® N-276 BK ND 3007 40% Glass/Mineral Filled PA66
Description: Ultramid N-276 BK ND3007 is a 40% mineral/glass reinforced, heat stabilized injection molding PA6/6.Information provided by BASF
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | |
|
Radici Radilon® A RV400 (dry) Nylon 66
Radilon® A is a range of polyamide 66 (PA66) products obtained through the polymerization of hexamethylendiamine and adipic acid, and used for injection, extrusion and blow-molding.Information prov..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | |
|
LATI Latamid 66 H2 G/25-V0KB4 PA 66, 25% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant
Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers. UL94 V-0 classified, with red phosphorous. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaIn..
|
|||