- HOME
- POLYMER SEARCH
- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 286 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 286 °F Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | Unannealed; ASTM D648 |
|
Multibase Nylex™ 2185 HFX Natural Polyamide + PP
Forms: PelletsProcessing Methods:Injection moldingFeatures:Tensile Strength, HighInformation provided by Multibase
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | ASTM D648 |
|
Nylene® PX1719 Nylon 6
Dry as molded. Extrusion grade. Nylene PX1719HS is a heat stabilized, high impact, nylon 6 extrusion grade resin with a low flexural modulus. PX1719HS is ideally suited for extrusion of tubing and..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | ISO 75/Method Bf |
|
Premix Thermoplastics PRE-ELEC® PBT 1455
PRE-ELEC PBT 1455 is a conductive thermoplastic compound based on PBT. Conductivity is achieved by using special conductive carbon black. PRE-ELEC PBT 1455 has excellent mechanical properties as wel..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
141
°C @Thickness 3.20 mm |
286
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® BFL2010 PC (Asia Pacific)
Non-brominated, non-chlorinated flame retardant, glass reinforced PC with improved flow. Available in opaque colors.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
141
°C @Thickness 3.20 mm |
286
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® HPS7R PC
Low flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, steam, e-beam, and gamma sterilizable. ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP Lubricomp DCL329XZ PC
LNP LUBRICOMP* DCL329XZ is a compound based on Polycarbonate resin containing Carbon Fiber, Flame Retardant, PTFE. Added features of this material include: Electrically Conductive.This data was sup..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
|
SABIC Innovative Plastics Lexan® 950A PC (Europe-Africa-Middle East)
LEXAN 950A is a high viscosity flame retardant grade, especially suitable for electrical applications.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
|
SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF0335 PC (Europe-Africa-Middle East)
LNP* Lubricomp* LEXAN_LF0335 compound is a 35% glass fiber, milled glass reinforced PC injection moulding resin with improved wear resistance and reduced friction.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP LUBRICOMP ZFG26 PPE+PS
LNP* LUBRICOMP* ZFG26 is a compound based on PPE+PS resin containing 30% Glass Fiber, 10% Graphite. Added features of this material include: Wear Resistant.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP LUBRICOMP ZFG26 PPE+PS (Asia Pacific)
LNP* Lubricomp* ZFG26 is a compound based on PPE+PS Blend resin containing Glass Fiber, Graphite Powder. Added features of this material include: Internally Lubricated.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP STAT-KON DEL13EXC PC
LNP STAT-KON* DEL13EXC is a compound based on Polycarbonate resin containing 15% Carbon Fiber, 5% PTFE. Added features of this material include: Easy Molding, Electrically Conductive, Wear Resistan..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
141
°C @Thickness 3.20 mm |
286
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP STAT-KON DEL339XF PC
LNP* STAT-KON* DEL339XF is a compound based on Polycarbonate resin containing 15% Carbon Fiber, 15% PTFE. Added features include: Electrically Conductive, Flame Retardant, Wear Resistant.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP STAT-KON DEP23FXC PC
LNP STAT-KON* DEP23FXC is a compound based on Polycarbonate resin containing 15% Carbon Fiber, 10% PTFE/Silicone. Added features include: Electrically Conductive. Wear Resistant, Superior Molding.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
141
°C @Thickness 3.20 mm |
286
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP STAT-KON DEP23FXC PC
LNP STAT-KON* DEP23FXC is a compound based on Polycarbonate resin containing 15% Carbon Fiber, 10% PTFE/Silicone. Added features include: Electrically Conductive. Wear Resistant, Superior Molding.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
141
°C @Thickness 3.20 mm |
286
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP DF002ERH PC
LNP THERMOCOMP* DF002ERH is a compound based on Polycarbonate resin containing 10% Glass Fiber. Added features of this material include: Easy Molding, Healthcare, Mold Release.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | ISO 75 |
|
Teijin Panlite® L-1225Z100 Transparent and Weather Resistant grade Polycarbonate Resin
Conforms to SAE regulations. It is an injection molding grade that has slightly high fluidity, weather resistance and mold release property and is bluish-tinted to exhibit clear colorApplications:Co..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | ISO 75 |
|
Teijin Panlite® LN-2250Y Flame Resistant, Translucent Polycarbonate Resin
Flame retardant and mold release grade with normal fluidity, while maintaining intrinsic transparency of polycarbonate resin. It is suitable for injection molding applications.Applications:Electric,..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | Annealed; ISO 75-2/B; ASTM D648 |
|
Styron CALIBREâ„¢ 303V-10 Polycarbonate Resin
Overview: CALIBREâ„¢ 300V-10 Polycarbonate resins offer exceptional impact resistance, heat distortion resistance, optical clarity and meets UL94 V-2 rating. CALIBRE 300V series products are avai..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | 0.157 in, annealed; ASTM D648 |
|
Styron EMERGEâ„¢ 4530-10 Polycarbonate
EMERGEâ„¢ PC 4530-10 advanced resin is a general purpose polycarbonate resin offering ignition resistance, heat resistance and excellent toughness. Applications: Consumer Electronics and Inform..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
141
°C @Thickness 3.20 mm |
286
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP STAT-KON DDF029 PC
LNP STAT-KON* DDF029 is a compound based on Polycarbonate resin containing Carbon, Glass Fiber. Added features of this material include: Electrically Conductive. Flame Retardant.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP Stat-kon DE0049 PC (Europe-Africa-Middle East)
LNP* Stat-kon* DC-1004 FR is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant.This..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP THERMOCOMP DF002ER PC
LNP THERMOCOMP* DF002ER is a compound based on Polycarbonate resin containing 10% Glass Fiber. Added features of this material include: Easy Molding. Mold Release
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | annealed; ISO 75-B |
|
Styron CALIBREâ„¢ 280-15 Polycarbonate
CALIBREâ„¢ PC Utility Grade 280-15 is a high flow opaque polycarbonate with an internal mold release system. Applications: Internal parts Electrical Electronics Lightning Information provided b..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics Noryl MX5569 PPE+PS
PPE+PS blend. High Heat. Good balance of flow and impact. Offers good aging performance under heat. Typical applications include Automotive Interiors and Lighting.This data was supplied by SABIC-..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | ISO 75-1,-2 |
|
Covestro Makrolon® 3100 Polycarbonate
Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Hig..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | ISO 75-1/-2 |
|
Covestro Makrolon® 3106 Polycarbonate
ISO 7391-PC,M,(,,)-09-9Global gradeMVR (300 °C/1.2 kg) 6.0 cm3/10 minFood contact qualityHigh viscosityGood hydrolysis resistanceInjection molding - Melt temperature 280 - 320 °CExtrusionAvailable..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | ASTM D648 |
|
Adell EQ-18 Homopolymer Polypropylene, 40% Mica Filled
Data provided by Adell Plastics, Inc.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
141
°C @Thickness 3.20 mm |
286
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP DBL349E PC (Asia Pacific)
LNP* Lubricomp* DBL349E is a compound based on Polycarbonate resin containing Glass Bead, PTFE, Flame Retardant. Added features of this material include:LNP* Lubricomp* DBL349E is a compound based ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP Lubricomp DCL329XZ PC (Asia Pacific)
LNP LUBRICOMP* DCL329XZ is a compound based on Polycarbonate resin containing Carbon Fiber, Flame Retardant, PTFE. Added features of this material include: Electrically Conductive.This data was sup..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP THERMOCOMP DX06409 PC (Asia Pacific)
LNP* Thermocomp* DX06409 is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release.
|
|||