- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 93.0 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 93.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | 4 mm thick;10.0 mm wide molded rod; ISO 75/Method Bf |
|
Premix Thermoplastics PRE-ELEC® PPE 1461
(discontinued **)
PRE-ELEC PPE 1461 is a conductive thermoplastic compound based on modified polyphenylene ether (PPE). Conductivity is achieved by using special conductive carbon black. In addition to a low electric..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 - 93.9 °C | 199 - 201 °F | Average value: 93.2 °C Grade Count:4 |
|
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Sheet
This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Sheet". Each property range of values reported is minimum and max..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | unannealed; ASTM D648 |
|
Phillips 66 COPYLENE® CH020 Polypropylene, Homopolymer, BOPP
COPYLENE™ CH020 is a polypropylene homopolymer resin designed for BOPP (biaxially oriented polypropylene) film extrusion applications. Applications: Bags & Pouches; Raffia/Tapes/Strapping; Peelable..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | ASTM D648 |
|
LyondellBasell Pro-fax 6301 Polypropylene Homopolymer, Flake Resin
Primary Processing Method: Masterbatch/ConcentratesKey Features: general purpose polypropylene homopolymer flake resin, minimal stabilization, FDA acceptableApplications: compounding, concentrates, ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
93.0
°C @Thickness 6.40 mm |
199
°F @Thickness 0.252 in |
Unannealed; ASTM D648 |
|
LG Chemical ALPHALAC SG910 HIPS
High gloss and high impact equivalent to ABS, Excellent mechanical properties compare with general HIPS, Meet requirements for cost and quality, Applications include housing of electric appliancesCA..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | |
|
Ineos ABS Lustran® 488
Key Features:UnfilledSuitable processing methods:Injection molding
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
93.0
°C @Thickness 6.40 mm |
199
°F @Thickness 0.252 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Prevex BJAX PPE+PS
Foamable resin. All properties at 10% density reduction; 0.250" thick specimens; improved productivity.This data was supplied by SABIC-IP for the Americas region.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
93.0
°C @Thickness 3.20 mm |
199
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Xylex X7300OQ PC+POLYESTER (Europe-Africa-Middle East)
PC+ POLYESTER unreinforced alloy developed for optical or lense market. High flow with good impact and excellent optical quality.This data was supplied by SABIC-IP for the Europe-Africa-Middle East..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP STAT-LOY AX06484 ABS
LNP* STAT-LOY* AX06484 is a compound based on ABS resin containing Talc. Added feature of this grade is: Antistatic, Extrudeable.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | ISO 75 |
|
Styrolution Terlux® 2812 TR MABS
Terlux 2812 TR is a transparent grade of MABS for injection molding with high flowability.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
93.0
°C @Thickness 6.40 mm |
199
°F @Thickness 0.252 in |
ASTM D648 |
|
Samsung Cheil Industries Starex® LX-0981 ABS, Unreinforced Metallic-Look
Luminous Grade - gives aesthetics of a painted surface without painting. Reduces time, cost, and environmental hazards (such as soilvents).Information provided by Samsung Cheil Industries.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
93.0
°C @Thickness 6.40 mm |
199
°F @Thickness 0.252 in |
ASTM D648 |
|
Samsung Cheil Industries Starex® SD-0170 F ABS, Unreinforced
Information provided by Samsung Cheil Industries.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
93.0
°C @Thickness 6.40 mm |
199
°F @Thickness 0.252 in |
ASTM D648 |
|
Samsung Cheil Industries Starex® VE-0852 ABS, Unreinforced FR
Information provided by Samsung Cheil Industries.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | Unannealed; ASTM Data |
|
Styron Magnumâ„¢ 8325 ABS, Sheet Coextrusion Grade
MAGNUM® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | Unannealed; ASTM Data |
|
Styron Magnumâ„¢ 9030 ABS, High Gloss
MAGNUM® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | Unannealed; ASTM Data |
|
Styron Magnumâ„¢ HPC 952 ABS, High Gloss
MAGNUM® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
93.0
°C @Thickness 3.20 mm |
199
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics NORYL N850 PPE+PS (Asia Pacific)
ECO-FLO(tm). ECO conforming, nonhalogenated flame retardant PPE+PS. High flow. Electrical and Business Equipment applications.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | ISO 75-2 |
|
Borealis BJ380MO Polypropylene Copolymer
BJ380MO is a very high melt flow heterophasic copolymer with high/medium impact strength and stiffness. This grade is designed for high-speed injection molding and contains nucleating and antistatic..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | ISO 75-2 |
|
Borealis HG430MO Polypropylene
HG430MO is a polypropylene homopolymer intended for injection molding. This polymer product is characterized by a superior impact resistance. This grade has ductile failure in falling weight impact ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | ASTM D648 |
|
Goodfellow TPX® MX002O Polymethylpentene
This grade is highly recommended for injection molding, film and mandrel extrusion; also for fiber extrusion and blow molding.TPX® is semi-crystalline, transparent, very light and - for a polyolefi..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | Annealed; ASTM Data |
|
Dow Prevail® 3150 ABS + Polyurethane
PREVAIL® 3150 thermoplastic resin offers designers and manufacturers a combination of flexibility and low temperature toughness not previously available in an engineering thermoplastic and is used ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | ASTM D648 |
|
Braskem H 107 Coating Polypropylene
Description: H 107 is a ultra-high melt flow rate additivated homopolymer used for general purposes. Designed for extrusion coating. This product exhibits excellent processability, good melt stabili..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | ASTM D-648 |
|
Bapolan® 6403 Polystyrene, Extrusion Grade
Bapolan PS6403 is a high impact polystyrene resin designed for extrusion-thermoforming applications. It complies with US FDA21 CFR177.1640 and 94HB UL rating.Applications: General purpose, housewar..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | ASTM D648 |
|
A. Schulman ComAlloy Comtuf® 101 Polypropylene, Mineral Reinforced, Impact Modified
Data provided by the manufacturer, ComAlloy International Company.25% Mineral Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been i..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | ASTM D648 |
|
Braskem CP 442 XP Injection Molding Polypropylene
Description: CP 442XP is a medium melt flow rate heterophasic copolymer suitable for injection molding applications. The product combines good stiffness with excellent impact resistance even at sub-..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | ASTM D648 |
|
Buckeye Polymers BP RPP 1012 C Polypropylene, 10% Mineral Filled
Calcium carbonate-filled PP grades have a high impact toughness, moderate increased stiffness, and excel in high gloss applications. This material can be customized through the addition of UV packag..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | ASTM D648 |
|
Adell RZ-18 Copolymer Polypropylene, 40% Calcium Carbonate Filled
Data provided by Adell Plastics, Inc.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | ASTM D648 |
|
A. Schulman POLYFORT™ FPP 3711 High Impact Polypropylene
DescriptionPolyfort® FPP 3711 is a 26% calcium carbonate filled high impact polypropylene.Information provided by A. Schulman.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | ASTM D648 |
|
Ineos H05H-01 Polypropylene Homopolymer
Grade H05H-01 is a homopolymer polypropylene for injection molding applications. It is an excellent long-term heat aging grade and offers superior extraction resistance in hot aqueous solutions. T..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
|
SABIC Innovative Plastics LNP Stat-kon MDM40 PP
LNP* Stat-Kon* MDM40 is a compound based on Polypropylene resin containing Mica and Carbon. Characteristics are Statically Conductive.This data was supplied by SABIC-IP for the Americas region.
|
|||