Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 95.0 °C Product List

Thermal Properties

Tips: 30 items are displayed at most.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C <br>@Thickness 3.18 mm	203 °F <br>@Thickness 0.125 in	Unannealed; ASTM D648
PolyOne Trilliant™ HC X THC 1100 Natural Copolyester Trilliant™ HC high performance blends offer outstanding strength, durability and chemical resistance through the combination of Eastman Tritan™ copolyester with other various polymeric resins. Tri..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F	ASTM D648
SABIC PP 5703P Polypropylene Homopolymer for Injection Molding Product Description: PP 5702P is specially developed for producing rigid injection molded articles for general purpose applications. It gives consistent processability and high gloss in the produc..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C <br>@Thickness 3.20 mm	203 °F <br>@Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics Cycolac® MG38N ABS (Asia Pacific) Very high impact ABS. Toughness/rigidity. Good fatigue resistance. NSF Standard 61 certified in limited colors (restrictions may apply)>
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C <br>@Thickness 3.20 mm	203 °F <br>@Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics Cycoloy® MC5215 PC+ABS
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F	ASTM D648
Reliance Industries Repol R110MK Polypropylene REPOL Polypropylene R110MK is manufactured using Unipol PP process which combines the production efficiency of gas phase fluidized bed reactor technology with the high activity stereospecific cataly..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F	ASTM D648
PolyMirae Moplen RP370G Blow Molding Grade Polypropylene Moplen RP370G is the polypropylene copolymer manufactured by PMC under the license of BASELL using the Spheripol process. Moplen RP370G is a copolymer particularly suitable for blow molding applicat..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F
Polimeri Europa SINKRAL PD H330/S ABS, Heat Stabilized  (discontinued **) Symbol according to ISO 1043-1: ABS Grade designation according to ISO 2580-ABS 1,MG,095-15-16-25 Injection moulding grade with high flow and gloss, specially developed to meet the requirements of..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F	ASTM D648
Reliance Industries Repol B120MA Polypropylene REPOL Polypropylene B120MA is manufactured using Unipol PP process which combines the production efficiency of gas phase fluidized bed reactor technology with the high activity stereospecific cataly..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 - 138 °C	203 - 280 °F	Average value: 124 °C Grade Count:7
Overview of materials for Polypropylene, Stainless Fiber, EMI This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Stainless Fiber, EMI". Each property range of values reported is minimum and maximum valu..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F
Eastman Tenite 383A-08 Cellulose Acetate Propionate  (discontinued **) 8% Plasticized. ISO data as provided by the manufacturer, Eastman Chemical.
Deflection Temperature at 0.46 MPa (66 psi)	95.0 Â°C	203 Â°F	ASTM D648
FiberfilÂ® M-2450 Polypropylene Copolymer Information provided by FIBERFIL Engineered Plastics
Deflection Temperature at 0.46 MPa (66 psi)	95.0 Â°C <br>@Thickness 6.40 mm	203 Â°F <br>@Thickness 0.252 in	Unannealed; ASTM D648
LG Chemical LI970HF Co-Extrusion ASA Description: Good Weatherability, Scratch Resistance, High FlowApplication: Window Profile, Siding, Rain GutterCAS: 26299-47-8Information provided by LG Chemical
Deflection Temperature at 0.46 MPa (66 psi)	95.0 Â°C <br>@Thickness 6.40 mm	203 Â°F <br>@Thickness 0.252 in	Unannealed; ASTM D648
LG Chemical LUPOY GN1000F PC, Halogen Free, Flame Retardant, Transparency Description: Injection Molding, PC, Halogen Free Flame Retardant, TransparencyApplication: IT/OA, Electric & Electronic Housing and ComponentsCAS: 103598-77-2 and 181028-79-5Information provided by ..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 Â°C <br>@Thickness 6.40 mm	203 Â°F <br>@Thickness 0.252 in	ASTM D648
Samsung Cheil Industries StarexÂ® GC-0770 H ABS/PET, Unreinforced Recycled Eco-friendly Post-Consumer recycled PET.Information provided by Samsung Cheil Industries.
Deflection Temperature at 0.46 MPa (66 psi)	95.0 Â°C <br>@Thickness 6.40 mm	203 Â°F <br>@Thickness 0.252 in	ASTM D648
Samsung Cheil Industries StarexÂ® LX-0971 S ABS, Unreinforced Metallic-Look Luminous Grade - gives aesthetics of a painted surface without painting. Reduces time, cost, and environmental hazards (such as soilvents).Information provided by Samsung Cheil Industries.
Deflection Temperature at 0.46 MPa (66 psi)	95.0 Â°C <br>@Thickness 6.40 mm	203 Â°F <br>@Thickness 0.252 in	ASTM D648
Samsung Cheil Industries StarexÂ® LX-0971 S ABS, Unreinforced Metallic-Look Luminous Grade - gives aesthetics of a painted surface without painting. Reduces time, cost, and environmental hazards (such as soilvents).Information provided by Samsung Cheil Industries.
Deflection Temperature at 0.46 MPa (66 psi)	95.0 Â°C <br>@Thickness 3.20 mm	203 Â°F <br>@Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics LNP STAT-LOY NX13401 PC+ABS LNP* STAT-LOY* NX13401 is a compound based on PC+ABS blend. Added features of this material include: Antistat, Flame Retardant, Excellent Release.
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F	ISO 75-2
Borealis Daplen™ EE188HP Polypropylene TPO Compound Daplen™ EE188HP is a 15% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has an excellent balance between impact strength and stiffness and g..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F	ISO 75-2
Borealis Daplen™ KB4436 Polypropylene TPO Compound Daplen™ KB4436 is a 30% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has an excellent balance between impact strength and stiffness and gi..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F	ASTM D648
A. Schulman PP 3487-01 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 3487-01 is a special homopolymer polypropylene formulated with a long term heat aging resistance. This material has excellent resistance to chemicals and solvents. High..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F	DIN 53461
Polyram PlusTek PA517 Nylon 6.6, Flame Retardant Flame retardant halogen free polyamide 6.6 formulated to meet V-0, for injection molding applicationsInformation provided by Polyram Ram On Ind.
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F	ASTM D648
A. Schulman POLYFORT™ FPP 1245 CaCO3 Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1245 is a 20% CAC03 filled copolymer polypropylene product. Information provided by A. Schulman.
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F	HDT B flatwise
Corbion Purac Blend C High Heat, Impact Modified Homopolymer PLA Heat resistance higher than typical PLA is achieved by addition of a nucleating agent and PDLA homopolymer. Increased impact is produced by addition of impact modifier to the base grade; a small am..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F	ISO 75-1/-2
Covestro Bayblend® FR 3008 Polycarbonate + ABS, Flame Retardant Grade Injection molding gradeHDT/A = 85 °CVicat/B 120 temperature = 103 °CUL-listing 94 V-0 (1.5 mm)improved chemical and hydrolysis resistance antimony-, chlorine- and bromine-free flame retardant..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F	ISO 75-1/-2
Covestro Bayblend® FR 3020 Polycarbonate + ABS, Mineral Filled 5 % mineral filledfor thin-wall applicationsinjection moldingVicat/B 120 = 103 °CHDT/A = 85 °Cvery good UL listing in small wall thickness (V-0 at 0.75 mm)PreprocessingMax. Water content
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F	ISO 75-1,-2
Covestro Bayblend® FR3001 PC/ABS Blend Main characteristics:• High toughness even at low temperatures• High dimensional accuracy and stability• Good paintability• Good flowabilityGrade characteristics:• Flame-retardant• Injec..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 - 100 °C	203 - 212 °F
C.O.I.M. EXTER S® S 107 Orthophthalic Resin Description: The Exter S product line contains a large number of unsaturated polyester resin products with an array of properties and applications.Specific Notes for ESTER S® S 107: Resin for trans..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F	ASTM D648
Carmel Olefins CAPILENE® G 86 E Polypropylene Homopolymer CAPILENE® G 86 E is a polypropylene homopolymer intended for extrusion and thermoforming applications. This grade is formulated with a low water carry-over additive packaging and it exhibits good m..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F	ASTM D648
Carmel Olefins CAPILENE® M 45 F Polypropylene Homopolymer CAPILENE® M 45 F is a polypropylene homopolymer developed for the production of cast films. It is formulated with slip and anti-blocking agents. They show high gloss, high transparency and good sti..
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F
LATI Latimass 47/7-04 D008 PP Copolymer Specific density compound based on Polypropylene copolymer (PPc). Special filler.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati In..