Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 98.9 °C Product List

Thermal Properties

Tips: 30 items are displayed at most.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	98.9 °C	210 °F	ASTM D648
RheTech Products FRP102-01 Polypropylene, Flame Retardant, Black Applications: Electrical component housingsInjection molding conditions reported in table.Information provided by RheTech Products.
Deflection Temperature at 0.46 MPa (66 psi)	98.9 °C @Thickness 6.35 mm	210 °F @Thickness 0.250 in	Unannealed; ASTM D648
PolyOne Stat-Tech™ AS-08CF/000 Acrylonitrile Butadiene Styrene (ABS) Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compound..
Deflection Temperature at 0.46 MPa (66 psi)	98.9 °C	210 °F	ASTM D648
RheTech Products RCC120-01 20% Calcium Carbonate Reinforced Polypropylene, Black, Recycled Content Applications: Electrical componentsConsumer goodsInjection molding conditions reported in table.Information provided by RheTech Products.
Deflection Temperature at 0.46 MPa (66 psi)	98.9 °C	210 °F	ASTM D648
Polymer Resources PC/TP-GP2-[color]-UV PC/Polyester Alloy, UV-stabilized High Impact, Excellent Chemical Resistance, UV-stabilizedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informa..
Deflection Temperature at 0.46 MPa (66 psi)	98.9 °C	210 °F	ASTM D648
Polymer Resources PPX-FR2 Modified-PPO, V-1 Flame Retardant Modified-Polyphenylene Oxide, V-1 Flame Retardant, 210F HDTFeatures: • Bromine Free • Chlorine FreeProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-..
Deflection Temperature at 0.46 MPa (66 psi)	98.9 °C	210 °F	ASTM D648
Polymer Resources PPX-FR2-[color]EN Modified PPO, UL 94 V-1 with HDT of 210 F, Extrusion Grade Process: ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Deflection Temperature at 0.46 MPa (66 psi)	98.9 °C	210 °F	ASTM D648
Polymer Resources PPX-FR2-[color]-EN Modified-PPO, V-1 Flame Retardant, Extrusion Grade Modified-Polyphenylene Oxide, V-1 Flame Retardant, 210F HDT, Extrusion GradeFeatures: • Bromine Free • Chlorine FreeProcess: ExtrusionNotes: All physical, mechanical and thermal testing conducte..
Deflection Temperature at 0.46 MPa (66 psi)	98.9 °C	210 °F	ASTM D648
Polymer Resources PPX-GP4-IM Modified-PPO, Impact Modified Modified-Polyphenylene Oxide, Impact Modified, 210F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informati..
Deflection Temperature at 0.46 MPa (66 psi)	98.9 °C	210 °F	ASTM D648
Rochling Engineered Plastics Polystone® P Polypropylene Extruded Sheet Information provided by Röchling Engineered Plastics.
Deflection Temperature at 0.46 MPa (66 psi)	98.9 °C	210 °F	ASTM D648
Polymer Resources PPX-GP4 Modified PPO, General Purpose with HDT of 210 F  (Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Deflection Temperature at 0.46 MPa (66 psi)	98.9 °C	210 °F	Unannealed; ASTM Data
Dow Isoplast® 151 Polyurethane (PUR-RT), Impact Modified  (discontinued **) ISOPLAST® 151 resin is an impact modified amorphous polymer with the chemical resistance of crystalline resins. Its outstanding properties include excellent chemical resistance, high heat, low mois..
Deflection Temperature at 0.46 MPa (66 psi)	98.9 - 182 °C	210 - 360 °F	Average value: 147 °C Grade Count:63
Overview of materials for Polycarbonate, 30% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 30% Glass Filled". Specific grades with glass content between 25% and 34% are included. E..
Deflection Temperature at 0.46 MPa (66 psi)	98.9 Â°C	210 Â°F	ASTM D648
Ineos H36G-00 Polypropylene Homopolymer This is a high flow rate homopolymer. This material is designed for fiber spinning and spun bonded processes. It meets the requirements of the U.S. Food and Drug Administration as specified in 21 ..
Deflection Temperature at 0.46 MPa (66 psi)	98.9 Â°C	210 Â°F	ASTM D648
FiberfilÂ® PP-15/T/10/20 Polypropylene Homopolymer, 22% Talc Filled Information provided by FIBERFIL Engineered Plastics
Deflection Temperature at 0.46 MPa (66 psi)	98.9 Â°C	210 Â°F	Unannealed; ISO 75B-1, -2
LyondellBasell Hifaxâ„¢ DR279 Thermoplastic Polyolefin Elastomer Description: Hifaxâ„¢ DR279 high melt flow, 1,200 MPa flexural modulus, paintable thermoplastic elastomeric olefin (TEO) resin has a unique balance of stiffness, impact resistance, processability..
Deflection Temperature at 0.46 MPa (66 psi)	98.9 Â°C	210 Â°F	Unannealed; ASTM D648
Techmer ES HiFill FRÂ® ABS GF15 FR-2 15% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 15% Filler by WeightFeatures: Flame RetardantInformation provided by TP Composites, Inc.
Deflection Temperature at 0.46 MPa (66 psi)	98.9 Â°C	210 Â°F	Unannealed; ASTM D648
Techmer ES HiFillÂ® HDPE TM30 30% Talc Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Talc Filler, 30% Filler by WeightInformation provided by TP Composites, Inc.
Deflection Temperature at 0.46 MPa (66 psi)	98.9 Â°C	210 Â°F	ASTM D648
Spartech EP6240 Filled and Reinforced Copolymer Filled copolymers offer a higher level of impact performance than homopolymer materials, and higher stiffness than unfilled copolymers. Copolymer based materials retain much of their impact strength..
Deflection Temperature at 0.46 MPa (66 psi)	98.9 Â°C	210 Â°F	Unannealed; ASTM D648
Techmer ES HiFillÂ® PP 0112 B Polypropylene Availability: North AmericaForms: PelletsFiller/Reinforcement: Unspecified Filler/ReinforInformation provided by TP Composites, Inc.
Deflection Temperature at 0.46 MPa (66 psi)	98.9 Â°C	210 Â°F	Unannealed; ASTM D648
Techmer ES LuriblendÂ® ABS TX15 Availability: North AmericaForms: PelletsAdditive: PTFE Lubricant(15%)Features: Lubricated and Good Wear ResistanceInformation provided by TP Composites, Inc.
Deflection Temperature at 0.46 MPa (66 psi)	98.9 °C	210 °F	ASTM D648
CPC - Vycom PROTEC® Homopolymer Polypropylene Protec HP is a high corrosion resistant polypropylene material which exhibits excellent tensile strength and stiffness at elevated temperatures. Homopolymer polypropylene possesses excellent resista..
Deflection Temperature at 0.46 MPa (66 psi)	98.9 °C	210 °F	ASTM D648
Clariant Renol ABS3470 ABS, High Heat, Low Gloss Data provided by Clariant Masterbatches
Deflection Temperature at 0.46 MPa (66 psi)	98.9 °C	210 °F	ASTM D648
Aclo Accutech ABS ABS832G20L Glass Reinforced
Deflection Temperature at 0.46 MPa (66 psi)	98.9 °C	210 °F	ASTM D648
Asahi Kasei Thermofil P-9900-1760 Unreinforced, Heat Stabilized, Impact Modified Information provided by Asahi Thermofil
Deflection Temperature at 0.46 MPa (66 psi)	98.9 °C	210 °F	ASTM D648
Aaron Industries AAROPRENE® CFPP 2020 Calcium Carbonate Filled Polypropylene AAROPRENE® CFPP 2000 Series Reinforced CompoundsMelt flow index may be specified. Color may be specified.
Deflection Temperature at 0.46 MPa (66 psi)	98.9 - 155 °C	210 - 311 °F	Average value: 148 °C Grade Count:26
Overview of materials for Polycarbonate, 40% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 40% Glass Filled". Specific grades with glass content between 35% and 44% are included. E..