- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 105 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 105 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | 120°C/h; ISO 75/1 |
|
Polykemi AB POLYblend 65CI PC/ABS-Blend
Information provided by Polykemi AB
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | 120°C/h; ISO 75/1 |
|
Polykemi AB POLYblend C65HF PC/ABS-blend
Information provided by Polykemi AB
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics Cycoloy® CY9640 PC+ABS
PC+ ABS, High Impact and High Flow, ductility at low temperature, excellent properties retention after Hydrolytic and Heat Aging
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics Cycoloy® CY9640 PC+ABS (Asia Pacific)
PC+ ABS, High Impact and High Flow, ductility at low temperature, excellent properties retention after Hydrolytic and Heat Aging
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics Cycoloy® XCY630 PC+ABS (Asia Pacific)
PC+ ABS Automotive applications, High Impact and High Flow, ductility at low temperature, excellent properties retention after Hydrolytic and Heat Aging
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | ASTM D648 |
|
Shell Carilon® DB6F0A10 Polyketone, Flame-Retarded (V-0) Injection Molding Grade
(discontinued **)
Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON Polymer DB6F0A10 is a flame-retarded injection molding grade with mechanical properties which classify it a..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
105
°C @Thickness 6.40 mm |
221
°F @Thickness 0.252 in |
ASTM D648 |
|
Kingfa PBT-T15 15% Mineral Filled PBT
Features:Excellent size stabilityLow tendency to wrapLow abrasionGood surfaceApplications:Injection moldingApplication partsE & E partsInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
105
°C @Thickness 6.40 mm |
221
°F @Thickness 0.252 in |
Unannealed; ASTM D648 |
|
LG Chemical LUCEL FW700S Modified POM, Friction Resistance, Abrasion Resistance
Feature: Injection Molding, Modified POM, Friction Resistance, Abrasion ResistanceApplication: Gears, Printer Roller Pumps, Gear Worm WheelsCAS No. 66455-31-0Information provided by LG Chemical
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | ASTM D648 |
|
LG Chemical LUMAX HF-5306F High Flow PBT, 30% Polymer Alloy, Weather Resistant, Flame Retardant
LUMAX resins are a family of thermoplastic blends of polybutyleneterephthalate(PBT) and styrenic resins that combine the most desirable properties of both resins and fillers. They offer high heat r..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | ISO 75 |
|
GEHR Plastics POM-ESD Acetal, Antistatic
Polyoxymethylene can be used in temperatures up to 100°C. The high surface strength is only surpassed by a few materials. POM shows good sliding properties and high resistance to wear and tear be..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | ISO 75/A |
|
Grupo Repol Dinalon® B1S25 M404 PA6 40% Mineral Charge
Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | ISO 75-1/-2 |
|
Lanxess Durethan® T 40 ZS 000000 Partially aromatic polyamide
Partially aromatic polyamide, injection molding and extrusion grade, easy release, transparent in all wall thicknesses, isotropic shrinkage, mechanical and electrical properties largely unaffected b..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | |
|
LATI Laticonther 52/11 CP1/600 F3 PP Homopolymer
High thermal conductivity product based on Polypropylene homopolymer (PPh). Special filler. Potentially suitable for food/medical contact application.Availability: Africa & Middle East; Asia Pacific..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | Unannealed; ASTM D648 |
|
Solvay Specialty Polymers Ryton® QC220P Polyphenylene Sulfide (PPS)
Ryton® PPS Fiber Grade Resins are high molecular weight polyphenylene sulfide polymers suitable for monofilament and/or multifilament fiber extrusion. They exhibit excellent thermal stability and..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
105
°C @Thickness 6.40 mm |
221
°F @Thickness 0.252 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Xenoy® 1731J PBT+PC (Asia Pacific)
PBT+PC, Impact/chemical resistant. UV-Stabilized. Excellent physical property retention in automotive exteriors and OVAD.This data was supplied by SABIC-IP for the Asia Pacific region.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
SABIC Innovative Plastics NORYL PX1185 PPE+HIPS (Europe-Africa-Middle East)
NORYL PX1185 is a special NORYL grade developed for extrusion of automotive trims. NORYL PX1185 offers high heat resistance and good impact performance.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
105
°C @Thickness 3.20 mm |
221
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP MF002AS PP
LNP THERMOCOMP* MF002AS is a compound based on Polypropylene resin containing 10% Glass Fiber. Added features of this material include: Heat Stabilized.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | unannealed; ISO 75-A |
|
Styron Pulse® 920 MG PC/ABS
An inherently matt medium heat, medium impact PC/ABS resin, PULSEâ„¢ 920 MG is designed for interior automotive applications where a matt aesthetic is required.Information provided by DowThis pro..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
105
°C @Thickness 3.20 mm |
221
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics NORYL PX0844 PPE+PS
PPE+PS blend. Unfilled. UL94 HB rated. Low water absorption. Hydrolytic stability. Dimensional stability.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | ISO 75-1, 2 |
|
Polyplastics Duranex® 601SA Polybutylene Terephthalate (PBT), Low density, Low wear, Mineral filled
DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 |
|
Diamond Polymers ABS 4001H3F
Description: Heat Resistant Grade, High HeatInformation provided by Diamond Polymers, Inc.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 - 115 °C | 221 - 239 °F | ASTM D648 |
|
Arkema Group KYNAR® 740 Polyvinylidene Fluoride Homopolymer - Injection Molding and Extrusion
Characteristics: Natural resin - translucent, off-white hemispheres. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeabili..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 - 115 °C | 221 - 239 °F | ASTM D648 |
|
Arkema Group KYNAR® 740-02 Polyvinylidene Fluoride Homopolymer - Injection Molding and Extrusion
Characteristics: Natural resin - translucent, off-white hemispheres. Flame and smoke suppressant. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mecha..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 - 115 °C | 221 - 239 °F | ASTM D648 |
|
Arkema Group KYNAR® 760 Polyvinylidene Fluoride Homopolymer - Extrusion
Characteristics: Natural resin - translucent, off-white hemispheres. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low permeabili..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | Unannealed; ISO 75-2/C |
|
Pasargad Polymer Peyvand Pasalen 3P-H3240B Polypropylene, 40% Mineral Filled Reinforced
Form: PelletsProcessing Method: Injection MoldingUses: Automotive Application Furniture Appliance Components Automotive Exterior PartsAutomotive Interior PartsInformation provided by Pasargad Poly..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | 0.25 inch; ASTM D648 |
|
PlastxWorld CEVIAN® A1700 PA/ABS Alloy, DAM
Property data is for dry as molded (DAM) samples.Information provided by PlastxWorld Inc.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | ASTM D648 |
|
Samyang Triloy® 450N Polymer Alloy, Blow Molding
Excellent impact, formability and weather resistance.450N is a blow molding grade.Applications: ConnectorsInformation provided by Samyang.
|
|||